The microstructual evolution and stability of a second generation single crystal (SC) nickel-based superalloy DD5 with minor grain boundary (GB) strengthening elements (C, B and Hf) were studied as a function of as-ca...The microstructual evolution and stability of a second generation single crystal (SC) nickel-based superalloy DD5 with minor grain boundary (GB) strengthening elements (C, B and Hf) were studied as a function of as-cast, heat treatment and thermal exposure. The microstructure and composition of the alloy were investigated by optical microscopy, scanning electron microanalysis (SEM), electron probe microanalysis (EPMA), energy dispersive spectrometry (EDS) and extraction analysis. In the as-cast condition,the microstructure observations and composition analysis showed that γ phase was the primary solidification phase and there were three microsegregations in the metal matrix. The morphology of these microsegregations depended on element segregations. After heat treatment, the dendrite cores contained fine and cuboidal-shaped γ′ particles with an average edge length of about 0.5 μm, whileinterdendritic regions contained irregularly-shaped γ′ particles and MC/M23C6 carbides. The mass fraction of γ′ phases was 61.685%.After exposure at 980 °C for 1000 h, no TCP phase was observed in both dendritic and interdendritic regions, indicating a good microstructual stability of the DD5 alloy at 980 °C.展开更多
Interfacial dislocations found in single crystal superalloys after long term thermal aging have an important effect on mechanical properties. Long term thermal aging tests for DD5 single crystal superalloy were carrie...Interfacial dislocations found in single crystal superalloys after long term thermal aging have an important effect on mechanical properties. Long term thermal aging tests for DD5 single crystal superalloy were carried out at 1,100 ℃ for 20, 100, 200, 500 and 1000 h, and then cooled by air. The effect of long term thermal aging on the dislocation networks at the γ/γ' interfaces was investigated by FE-SEM. Results showed that during the long term thermal aging at 1,100 ℃, misfit dislocations formed firstly and then reorientation in the(001) interfacial planes occurred. Different types of square or rectangular dislocation network form by dislocation reaction. Square dislocation networks consisting of four groups of dislocations can transform into octagonal dislocation networks, and then form another square dislocation network by dislocation reaction. Rectangular dislocation networks can also transform into hexagonal dislocation networks. The interfacial dislocation networks promote the γ' phase rafting process. The dislocation networks spacings become smaller and smaller, leading to the effective lattice misfit increasing from-0.10% to-0.32%.展开更多
文摘The microstructual evolution and stability of a second generation single crystal (SC) nickel-based superalloy DD5 with minor grain boundary (GB) strengthening elements (C, B and Hf) were studied as a function of as-cast, heat treatment and thermal exposure. The microstructure and composition of the alloy were investigated by optical microscopy, scanning electron microanalysis (SEM), electron probe microanalysis (EPMA), energy dispersive spectrometry (EDS) and extraction analysis. In the as-cast condition,the microstructure observations and composition analysis showed that γ phase was the primary solidification phase and there were three microsegregations in the metal matrix. The morphology of these microsegregations depended on element segregations. After heat treatment, the dendrite cores contained fine and cuboidal-shaped γ′ particles with an average edge length of about 0.5 μm, whileinterdendritic regions contained irregularly-shaped γ′ particles and MC/M23C6 carbides. The mass fraction of γ′ phases was 61.685%.After exposure at 980 °C for 1000 h, no TCP phase was observed in both dendritic and interdendritic regions, indicating a good microstructual stability of the DD5 alloy at 980 °C.
基金supported by the National Natural Science Foundation of China(Grant No.:50901046)
文摘Interfacial dislocations found in single crystal superalloys after long term thermal aging have an important effect on mechanical properties. Long term thermal aging tests for DD5 single crystal superalloy were carried out at 1,100 ℃ for 20, 100, 200, 500 and 1000 h, and then cooled by air. The effect of long term thermal aging on the dislocation networks at the γ/γ' interfaces was investigated by FE-SEM. Results showed that during the long term thermal aging at 1,100 ℃, misfit dislocations formed firstly and then reorientation in the(001) interfacial planes occurred. Different types of square or rectangular dislocation network form by dislocation reaction. Square dislocation networks consisting of four groups of dislocations can transform into octagonal dislocation networks, and then form another square dislocation network by dislocation reaction. Rectangular dislocation networks can also transform into hexagonal dislocation networks. The interfacial dislocation networks promote the γ' phase rafting process. The dislocation networks spacings become smaller and smaller, leading to the effective lattice misfit increasing from-0.10% to-0.32%.