A Sr3Yb2（BO3）4 single crystal was obtained by the Czochralski method. The structure of Sr3Yb2 （BO3）4 crystal was determined by single-crystal X-ray diffraction. The compound crystallizes in orthorhombic, space gro...A Sr3Yb2（BO3）4 single crystal was obtained by the Czochralski method. The structure of Sr3Yb2 （BO3）4 crystal was determined by single-crystal X-ray diffraction. The compound crystallizes in orthorhombic, space group Pnma with a=7.3750（8）, b=15.9265（14）, c=8.6776（9）, V=1019.25（18）3 , Mr=844.18, Z=4, Dc=5.501 g/cm3 , λ（MoKa）=0.71073, μ= 33.835 mm-1 , F（000）=1480, the final R=0.0339 and wR=0.0907 for 1090 observed reflections with I〉2σ（I）. The structure features a three-dimensional framework composed of isolated BO3 planar triangles bridged by YbO8 and SrO8 polyhedra. The Sr2＋ and Yb3＋ occupy statistically three independent sites with a Cm and two C1 local symmetries.展开更多
In this paper, the Sr3Y2 （BO3）4 ：Eu^3＋ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red...In this paper, the Sr3Y2 （BO3）4 ：Eu^3＋ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613 nm corresponding to the electric dipole 5^Do-7^F2 transition of Eu^3＋ under 365 nm excitation, this is because Eu^3＋ substituted for Y^3＋ occupied the non-centrosymmetric position in the crystal structure of Sr3Y2（BO3）4. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet （254 nm, 365 nm and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the red emission of Sr3Y2（BO3）4 ：Eu^3＋ was measured, the result shows that the emission intensities increase with increasing Eu^3＋ concentration, then decrease. The Commission Internationale del＇Eclairage chromaticity （x, y） of Sr3Y2（BO3）4 ：Eu^3＋ phosphor is （0.640, 0.355） at 15 mol% Eu^3＋.展开更多
基金Shanghai Commission of Sciences and Technology(08520513100)Shanghai Municipal Education Commission(J51504,09ZZ196)SIT Research Project on Optical Functional Crystals(TDP2009-03)
基金Supported by the National Natural Science Foundation of China (51002152)the Natural Science Foundation of Fujian Province (2010J05125)
文摘A Sr3Yb2（BO3）4 single crystal was obtained by the Czochralski method. The structure of Sr3Yb2 （BO3）4 crystal was determined by single-crystal X-ray diffraction. The compound crystallizes in orthorhombic, space group Pnma with a=7.3750（8）, b=15.9265（14）, c=8.6776（9）, V=1019.25（18）3 , Mr=844.18, Z=4, Dc=5.501 g/cm3 , λ（MoKa）=0.71073, μ= 33.835 mm-1 , F（000）=1480, the final R=0.0339 and wR=0.0907 for 1090 observed reflections with I〉2σ（I）. The structure features a three-dimensional framework composed of isolated BO3 planar triangles bridged by YbO8 and SrO8 polyhedra. The Sr2＋ and Yb3＋ occupy statistically three independent sites with a Cm and two C1 local symmetries.
基金supported by Hebei Provincial Technology Development Foundation of China (Grant No 51215103b)Science Foundation of Hebei University, China (Grant No 2006Q06)
文摘In this paper, the Sr3Y2 （BO3）4 ：Eu^3＋ phosphor was synthesized by high temperature solid-state reaction method and the luminescence characteristics were investigated. The emission spectrum exhibits one strong red emission at 613 nm corresponding to the electric dipole 5^Do-7^F2 transition of Eu^3＋ under 365 nm excitation, this is because Eu^3＋ substituted for Y^3＋ occupied the non-centrosymmetric position in the crystal structure of Sr3Y2（BO3）4. The excitation spectrum indicates that the phosphor can be effectively excited by ultraviolet （254 nm, 365 nm and 400 nm） and blue （470 nm） light. The effect of Eu^3＋ concentration on the red emission of Sr3Y2（BO3）4 ：Eu^3＋ was measured, the result shows that the emission intensities increase with increasing Eu^3＋ concentration, then decrease. The Commission Internationale del＇Eclairage chromaticity （x, y） of Sr3Y2（BO3）4 ：Eu^3＋ phosphor is （0.640, 0.355） at 15 mol% Eu^3＋.