GdVO_(4):Yb^(3+),Ho^(3+)和GdPO_(4):Yb^(3+),Ho^(3+)荧光粉的上转换发光特性研究

为了探究Yb^(3+),Ho^(3+)分别共掺杂在GdVO_(4)和GdPO_(4)两种基质材料的发光差异性,采用高温固相法制备GdVO_(4):Yb^(3+),Ho^(3+)和GdPO_(4):Yb^(3+),Ho^(3+)上转换发光材料。并采用X射线衍射仪(X-ray diffraction,XRD)、拉曼光谱(Raman spectroscopy,Raman)、扫描电子显微镜(scanning electron microscopy,SEM)和荧光光谱对材料的结构、组成、形貌和上转换发光性能进行测试分析。结果表明,合成样品均是纯相,GdVO_(4):Yb^(3+),Ho^(3+)样品形状为不规则块状;GdPO_(4):Yb^(3+),Ho^(3+)样品为米粒状。在980 nm激发下,两种样品都存在绿光和红光发射。与掺杂相同浓度的GdVO_(4):Yb^(3+),Ho^(3+)相比,GdPO_(4):Yb^(3+),Ho^(3+)样品的红绿比较大,色度坐标更接近红光,在生物成像领域具有更大的应用潜力。

亲水性CIT-NaYF_(4)∶Yb^(3+),Ho^(3+)纳米粒子的制备及其发光性能研究

采用溶剂热法制备了油溶性稀土掺杂上转换纳米粒子NaYF_(4)∶Yb^(3+),Ho^(3+),并利用TEM、XRD、IR、荧光光谱法等考察了反应温度、反应时间、掺杂比等反应条件对纳米粒子形貌、结构、发光性能的影响。结果表明,在反应温度为300℃、反应时间为50 min、稀土离子掺杂比为NaYF_(4)∶20%Yb^(3+),2%Ho^(3+)条件下,制备出的油溶性NaYF_(4)∶Yb^(3+),Ho^(3+)纳米粒子呈标准六方晶型,尺寸均一、单分散性好,平均粒径为31.55 nm。通过表面配体交换法成功将柠檬酸修饰在其表面,转为亲水性CIT-NaYF_(4)∶Yb^(3+),Ho^(3+)纳米粒子。

棒状结构NaGdF_(4):Yb^(3+),Er^(3+)上转换发光性能的研究

以乙二胺四乙酸二钠(EDTD-2Na)为螯合剂,采用水热法合成了棒状结构的NaGdF_(4):Yb^(3+),Er^(3+)纳米粉末。分别借助X射线衍射(XRD)、荧光光谱仪(PL)和扫描显微镜(SEM)对其晶体结构、发光强度和表面形貌进行分析和表征。探究了稀土前驱体、水热温度和水热时间的实验条件对NaGdF_(4):Yb^(3+),Er^(3+)纳米粉末上转换发光强度的影响;研究了氟源和钠源对NaGdF_(4):Yb^(3+),Er^(3+)晶体形貌和上转换发光强度的改善;同时,采用煅烧处理的方法,进一步探究样品的形貌和发光强度收到的影响。实验结果表明NH4F与NaOH作为氟源和钠源及200℃煅烧1 h得到的棒状结构NaGdF_(4):Yb^(3+),Er^(3+)的发光强度最好,色坐标(CIE)绿色发光强度从84%提升到94.88%。

Lu^(3+)掺杂Na_(5)Y_(9)F_(32)∶Ho^(3+)/Yb^(3+)/Ce^(3+)单晶体的增强红色上转换发光与光学温度传感性能

采用密封的坩埚下降法技术生长了一系列Lu^(3+)(摩尔分数0、0.6%、1.2%、1.8%)掺杂Na_(5)Y_(9)F_(32)∶Ho^(3+)/Yb^(3+)/Ce^(3+)单晶体。在980 nm LD激发下,观察到单晶体的绿光543 nm(^(5)S_(2)/^(5)F_(4)→^(5)I_(8))、红光656 nm(^(5)F_(5)→^(5)I_(8))以及近红外750 nm(^(5)S_(2)/^(5)F4→^(5)I_(7))上转换发光。从上转换发光强度随激发光强度的变化情况,确定了543 nm、656 nm与750 nm的发光为双光子跃迁过程。研究了Lu^(3+)离子掺杂浓度对其发光强度与荧光寿命的影响情况,随着Lu^(3+)掺杂浓度从0增加到1.8%,单晶体中的656 nm红光逐步增强,543 nm绿光与750 nm近红外光随之减弱,红绿光强度比从0.01增加到了1.55,而543 nm荧光寿命从1.29 ms降低至0.99 ms。Lu^(3+)离子的掺入取代Y^(3+)晶格位,改变了单晶体的局域场环境,导致上转换发光强度的变化。基于随温度变化的上转换红光656 nm(^(5)F5→^(5)I8)与绿光543 nm(^(5)S_(2)/^(5)F4→^(5)I8)的发光强度变化,研究了1.8%Lu^(3+)掺杂Na_(5)Y_(9)F_(32)∶Ho^(3+)/Yb^(3+)/Ce^(3+)单晶体在298~448 K范围内的绝对灵敏度和相对灵敏度最大值分别为0.242%·K^(-1)和0.217%·K^(-1)。

不同激发波长下NaLaF_(4):Er^(3+)/Yb^(3+)的上转换光谱调控研究

为探究不同激发波长(980 nm、1 550 nm)对NaLaF_(4):Er^(3+)/Yb^(3+)上转换发光材料光谱调控的规律和机理,采用水热-固相两步反应法合成一系列不同Er^(3+)/Yb^(3+)掺杂浓度的NaLaF_(4)荧光粉。利用X射线衍射仪(XRD)、荧光分光光度计对材料进行测试,分析其发光性能与机理。结果表明,样品在980 nm激发下呈绿色发光,上转换发光强度随Er^(3+)/Yb^(3+)掺杂浓度增加而呈现先增后减的规律,该发光过程为双光子过程;而在1 550 nm激发下呈红色发光,上转换发光强度随Er^(3+)掺杂浓度增加而呈增强趋势,但随Yb^(3+)浓度增加而降低,发光过程为三光子过程。因此,通过调节激发光波长,在同组分NaLaF_(4):Er^(3+)/Yb^(3+)荧光粉中实现颜色可控的绿、红色发光,对设计新型光谱调控手段和探索新的发光材料具有一定的理论指导意义。

溶剂热法制备NaScF_(4):Yb^(3+)/Er^(3+)及其发光性能的研究

利用溶剂热法在油酸(OA),正辛醇(OC)及乙二醇(EG)三溶剂中成功制备出NaScF_(4):Yb^(3+)/Er^(3+)纳米颗粒。调节三种溶剂的不同比例观察对样品晶相、结构、尺寸及发光强度的影响。此外,我们使用了X射线粉末衍射(XRD)、扫描电子显微镜(SEM)、荧光光谱仪对样品进行了表征。通过XRD证明在OA、OC、EG分别为16mL,12mL、4mL时成功合成出了纯相的NaScF_(4):Yb^(3+)/Er^(3+)纳米颗粒。SEM图进一步证明样品形貌均匀,分散性较好,粒径较小,颗粒尺寸为37.62±9.36nm。此外,样品的荧光光谱表明样品在980nm激光激发下能发射出红色荧光。因此,该方法下制备的NaScF_(4):Yb^(3+)/Er^(3+)尺寸较小,形貌较均匀,拥有强的红色发射且该材料有望用于生物成像、信息储存,防伪等领域。

动态缺陷导致Na_(3)Sc_(2)(PO_(4))_(3):Yb^(3+),Er^(3+)材料上转换和下转移发光不同热猝灭行为研究

掺Eu^(2+)的离子导体Na_(3)Sc_(2)(PO_(4))_(3)具有优异的抗热猝灭性能,是一种很有前景的大功率照明用发光材料。然而,其负热猝灭机理仍有待深入研究。本文以Yb^(3+)/Er^(3+)的f-f跃迁上转换和下转移窄带发射而非更易受干扰的Eu^(2+)d-f跃迁发射为研究对象,旨在获得更清晰的机理。结果表明,热致缺陷/离子的动态迁移能促进高温下辐射跃迁和抑制非辐射跃迁,导致上转换发光具有显著的负热猝灭,下转移发光热猝灭较小。其中,布居速率较慢的上转换过程更容易受到时间尺度与之相当的Na^(+)/空位迁移过程的影响。本研究可为理解发光材料热猝灭机制提供另一种视角。

NaGd(MoO_(4))_(2)∶Er^(3+),Yb^(3+)发光粉的合成与上转换发光性质

采用水热法合成了系列NaGd(MoO_(4))_(2)∶Er^(3+),Yb^(3+)上转换发光粉。利用X射线衍射仪、扫描电子显微镜和上转换发光光谱仪等对样品的结构、形貌和发光性能进行表征。结果显示,合成的样品均具有四方晶系NaGd(MoO_(4))_(2)结构;pH对样品的形貌有影响;980nm红外光激发下,NaGd(MoO_(4))_(2)∶Er^(3+),Yb^(3+)上转换发光粉显示来自于Er^(3+)的^(2)H_(11/2)→^(4)I_(15)和^(4)S_(3/2)→^(4)I_(15/2)跃迁产生的绿光发射和4I 9/2→4I 15/2跃迁产生的红光发射。比较各样品的发光强度和绿光/红光相对积分强度比,结果显示上转换发光强度和绿光/红光相对积分强度比与晶粒尺寸、晶粒表面形貌,以及Er^(3+)和Yb^(3+)掺杂浓度有关。讨论了可能的上转换发光过程,并计算了样品的色坐标。

Yb^(3+)/Nd^(3+)掺杂对Sr_(9)Ga(PO_(4))_(7)∶Cr^(3+)发光性能的影响

近红外荧光粉由于其独特的物理特性和广阔的应用前景吸引了人们极大的研究兴趣。本文通过高温固相反应法合成Sr_(9)Ga(PO_(4))_(7)∶0.8Cr^(3+)近红外荧光粉,使用460 nm蓝光激发样品的发射波长位于833 nm,半峰宽为117 nm。随后引入稀土离子合成Sr_(9)Ga(PO_(4))_(7)∶0.8Cr^(3+),Yb^(3+)和Sr_(9)Ga(PO_(4))_(7)∶0.8Cr^(3+),Nd^(3+)近红外荧光粉。相比Sr_(9)Ga(PO_(4))_(7)∶0.8Cr^(3+),460 nm蓝光激发的Sr_(9)Ga(PO_(4))_(7)∶0.8Cr^(3+),Yb^(3+)同时出现Cr^(3+)和Yb^(3+)特征发射峰,经过光谱分析和荧光寿命变化证明Cr^(3+)-Yb^(3+)存在能量传递通道,最高使Cr^(3+)-Yb^(3+)能量传递效率达80.2%,得益于Yb^(3+)卓越的热稳定性促使整体荧光光谱热稳定性提高约3.7倍。设计合成的Sr_(9)Ga(PO_(4))_7∶0.8Cr^(3+),Nd^(3+)样品调制出833,876,1 060 nm的多峰发射,显著拓宽了近红外光谱范围。最终,讨论了荧光粉在温度传感和无损检测领域的应用,证明该系列荧光粉具有广阔的应用前景。

Y_(2)Mo_(4)O_(15):Ho^(3+)/Yb^(3+)上转换材料的合成及其温度传感

上转换发光材料以其窄的发光谱带、发光带的可调性、优异的物理化学稳定性等特点,在生物成像和温度传感方面具有独特的优势.钼酸盐作为一种很典型的上转换发光基质,具有良好的化学稳定性、较高的量子产率以及独特的四方相结构,使其具备了作为高效上转换发光材料的条件.采用溶胶-凝胶法成功地合成了Y_(2)Mo_(4)O_(15):Ho^(3+)/Yb^(3+)纳米颗粒.以Ho^(3+)离子为激活剂,Yb^(3+)离子为敏化剂,探究了Y_(2)Mo_(4)O_(15)基质的上转换发光以及其在温度传感性能.在980 nm近红外的激发下,实现了Y_(2)Mo_(4)O_(15)基质的红色上转换发光,显示出Ho^(3+)的特征发射.Y_(2)Mo_(4)O_(15)基质在温度298~498 K范围内,其光谱发射与温度变化具有规律的响应.基于荧光强度比(FIR)技术,我们对^(5)S_(2)和^(5)F_(5)两个非热耦合能级进行理论计算,获得了在498 K时最大的相对灵敏度为2.72%K^(-1),研究结果表明Y_(2)Mo_(4)O_(15)在非接触温度传感应用方面具有极大的潜力.

Upconversion Luminescence Properties of Ho^(3+),Tm^(3+),Yb^(3+) Co-Doped Nanocrystal NaYF_4 Synthesized by Hydrothermal Method

Nanocrystal of upconversion （UC） phosphor Ho^3＋, Tm^3＋ , and Yb^3＋ co-doped NaYF4 was prepared by the hydrothermal method in the presence of the complexing agent EDTA. Under 980 nm diode laser excitation, the impact of different concentrations of Ho^3＋ ion on the UC luminescence intensity was discussed. The law of luminescence intensity versus pump power shows that the 474 nm blue emission, 538 nm green emission, and 642 nm red emission are all due to the two-photon process, while the 450 nm blue emission is a three-photon process. The UC mechanism and processes were also analyzed. The sample was characterized by transmission electron microscopy （TEM） and X-ray diffraction （XRD）. The result shows that Ho^3＋ ,Tm^3＋ , and Yb^3＋ co-doped NaYF4 prepared by the hydrothermal method exhibits a hexagonal nanocrystal.

Zn^(2+)掺杂增强NaY(MoO_4)_2:Yb^(3+),Ho^(3+)荧光粉的上转换发光性能研究

采用高温固相法制备了一系列的NaY_(0.78-x)(MoO_4)_2∶0.2Yb^(3+),0.02Ho^(3+),xZn^(2+)(x=0,0.05,0.1,0.15,0.2,0.25)荧光粉。通过X射线衍射仪、扫描电镜以及荧光光谱仪分别对样品的结构、形貌和荧光性能进行了表征。结果表明Zn^(2+)的掺杂可以通过替换Y^(3+)格位和占据晶格间隙的方式进入基质晶格。在980nm激光激发下,样品呈现出了强烈的绿光(551nm)和相对微弱的红光发射(668nm),分别归因于Ho^(3+)的~5F_4,~5S_2→~5I_8和~5F_5→~5I_8跃迁。Zn^(2+)的掺杂可以使上转换发光强度显著增强,其原因是Zn^(2+)掺杂产生了O^(2-)空位而且可以裁剪Ho^(2+)周围的局域晶体场对称性。基于泵浦依赖的研究,对能级图和可能的上转换发光机理进行了详细的讨论。

Gd_2(MoO_4)_3:Yb^(3+),Ho^(3+),Ce^(3+)在980nm激发下的上转换发光及其温度传感特性

以Gd_2(MoO_4)_3:Yb^(3+),Ho^(3+),Ce^(3+)上转换发光材料为对象,研究了980nm激发下的上转换发光及比值计算的发光温度传感特性.结果证实,Gd_2(MoO_4)_3:Yb^(3+),Ho^(3+)是一种良好的红色上转换发光材料,同时具有高灵敏的温度传感特性.前期研究显示,Ce^(3+)掺杂可以将Ho^(3+)的绿光调成红光,并改善发光温度传感的灵敏度.但在本研究中Ce^(3+)掺杂不但减弱Gd_2(MoO_4)_3:Yb^(3+),Ho^(3+)红光发射的强度和色纯度,而且降低发光温度传感的灵敏度.其原因在于Gd_2(MoO_4)_3:Yb^(3+),Ho^(3+),Ce^(3+)不寻常的红色发光机制及Ce^(3+)和Ho^(3+)之间的交叉弛豫.

水热法合成纳米晶NaYF4：Er^3＋，Tm^3＋，Yb^3＋的上转换发光特性

以EDTA为络合剂,用水热法合成了Er3+,Tm3+和Yb3+共掺杂的NaYF4纳米晶。XRD和TEM的结果表明:粒径约为30 nm,属于六方晶系。在980 nm半导体激光器激发下,研究了不同Er3+离子掺杂浓度对Tm3+和Er3+离子上转换发光性能的影响,光强与泵浦功率的双对数曲线表明,474,525,539,650 nm的发射均属于双光子过程,408 nm的发射属于三光子过程。讨论了样品的协作敏化和声子辅助共振能量传递的上转换发光机制。

Yb^(3+):YVO_4晶体的生长及光谱性能研究

采用提拉法生长出光学质量优良的Yb3 + :YVO4晶体 ,研究生长过程中工艺参数的控制。测得掺杂浓度为18.1%Yb3 + :YVO4晶体中Yb3 + 离子的有效分凝系数Keff为 0 96。测定了不同Yb3 + 离子掺杂浓度晶体的吸收光谱和荧光光谱 ,并分别计算了不同掺杂浓度下Yb3 + :YVO4晶体的光谱参数。本文总结和解释了掺杂浓度影响其性能的规律 ,讨论了Yb3 + :YVO4晶体作为激光晶体的优点。

980nm激发下Ho^(3+)/Yb^(3+)共掺杂ZrO_2-ZnO粉末的上转换发光特性

通过固相反应法制备了Ho3+/Yb3+共掺杂ZrO2-ZnO粉末样品,重点报道了Ho3+/Yb3+共掺杂ZrO2-ZnO粉末样品在980nm激发下的上转换发光现象。在常温下测试得到的发射光谱显示3个发射峰,中心波长依次为540,671和762nm,分别对应Ho3+的5S2/5F4→5I8,5F5→5I8,5S2/5F4→5I7或5I4→5I8跃迁过程。稀土离子的掺杂浓度明显影响样品的上转换发光特性,当Ho3+浓度确定的情况下,随着Yb3+含量增大,红光强度和绿光强度先减小后增大,近红外光却先增大后减小,而绿光强度与红光强度的比值一直减小。当Yb2O3含量为4.7mol%时,随着Ho3+含量增大,各波段荧光强度均减小,而绿光强度与红光强度的比值基本不变。双对数曲线显示3个波长的上转换发光的发射过程均为双光子过程,对样品的上转换发光机制做了详细的说明。XRD显示样品的均匀性良好。

Er^(3+),Yb^(3+)∶YAl_3(BO_3)_4晶体的光谱性质研究

采用助熔剂法生长了Er3 + ,Yb3 + 共掺的YAl3 (BO3 ) 4 晶体 ,测量了晶体的室温吸收谱。由此吸收谱 ,根据Judd Ofelt理论计算了Er3 + 在Er3 + ,Yb3 + ∶YAl3 (BO3 ) 4 晶体中的强度参数、自发辐射几率、积分发射截面等参数。强度参数为Ω2 =2 .4 4× 10 -2 0 cm2 、Ω4=2 .0 0× 10 -2 0 cm2 、Ω6=6 .10× 10 -2 0 cm2 。研究了晶体的荧光特性 ,并在 976nm激光泵浦下得到了上转换绿色荧光。

Er^(3+)/Yb^(3+):KG(WO_4)_2的熔盐提拉法生长及光谱性能

采用熔盐提拉法生长了尺寸达30mm×25mm×15mm的Er3+/Yb3+:KGd(WO4)2透明晶体,从中切出5mm×5mm×3mm大小的激光器件,在室温下测试了吸收光谱,可以观察到晶体存在366,380,489,522,651,811,980nm等吸收峰,并对之进行了能级归属。同时在980nm激光激发下测试了荧光光谱,可以发现在1024,1535nm处存在较宽的强发射峰,其半高宽分别为60和36nm。研究结果表明,Er3+/Yb3+:KG(WO4)2适合于InGaAsLD(980nm)泵浦,有可能产生1024nm波段及人眼安全的1535nm波段的可调谐激光。

不同波长激发下YLiF_4∶Er^(3+),Tm^(3+),Yb^(3+)的发光

水热法合成了YL iF4∶Er3+,Tm3+,Yb3+,其中Er3+、Yb3+和Tm3+的摩尔分数分别为1%、1.5%和2%。当用355 nm光激发时,其发光为蓝色,峰值位于450 nm,对应于Tm3+的1D2→3F4跃迁。用378 nm激发时,发光为绿色,主要发光峰位于552 nm。980 nm光激发时,发光为白色,发光峰分别位于665(651),552(543),484,450 nm处,并在648 nm处还观察到了一个发光峰,其中最强的发射为红光。YL iF4∶Er3+,Tm3+,Yb3+的蓝光来源于Tm3+的激发态1G4到基态3H6的跃迁,绿光来源于Er3+的4S3/2和2H11/2到基态4I15/2的跃迁,红光既来源于Tm3+的1G4→3F4的跃迁,也来源于Er3+的4F9/2→4I15/2的跃迁。在上转换发光中,还探测到了紫外光359 nm的发射。监测665 nm得到的激发光谱不同于监测552 nm的激发光谱,在665 nm的激发光谱中出现了对应Tm3+的1G4能级的峰。在双对数曲线中,蓝光484 nm、绿光552 nm和红光665 nm的斜率分别为2.25、2.28和2.21,紫外光359 nm的斜率为2.85。因此在980 nm激发下,蓝光484 nm、绿光552 nm和红光665 nm都是双光子过程,紫外光359 nm的发射是三光子过程。

YLiF_4:Er^(3+),Tm^(3+),Yb^(3+)中Tm^(3+)浓度对上转换发光的影响

利用水热法合成了YLiF4:Er3+,Tm3+,Yb3+,其中Er3+和Yb3+的浓度保持固定不变,分别为1 mol%和1.5 mol%,Tm3+浓度变化范围是2 mol%~8 mol%。在这种共掺杂体系中,同时观察到了Er3+,Tm3+和Yb3+的吸收,且Tm3+的吸收随着其浓度的增强而增强。在980 nm光的激发下,当Tm3+浓度很小时,这种材料的上转换发光为白光。其中蓝光主要来源于Tm3+的激发态1G4到基态3H6的跃迁,绿光来源于Er3+的4S3/2和2H11/2到基态4I15/2的跃迁,红光既来源于Tm3+的1G4→3F4的跃迁,也来源于Er3+的4F9/2→4I15/2的跃迁。并且这种上转换发光强度随着Tm3+浓度的增强而降低,但对应不同能级跃迁的发光强度降低的幅度不同,这是因为Er3+和Tm3+之间的相互作用。