Hydroxyl-epoxy phosphate （HEP） as a reactive corrosion inhibitor was innovatively synthe- sized by the reaction of bisphenol A epoxy resin with phosphoric acid. HEP was mixed with hydroxyl acrylate resin, and crossl...Hydroxyl-epoxy phosphate （HEP） as a reactive corrosion inhibitor was innovatively synthe- sized by the reaction of bisphenol A epoxy resin with phosphoric acid. HEP was mixed with hydroxyl acrylate resin, and crosslinked with waterborne isocyanate curing agent, which was used to form waterborne HEP/acrylic polyurethane composite （HEP-APU） coatings on Q235 steel surfaces. Electrochemical impedance spectroscopy and polarization curves were applied to analyze the corrosion behavior of the HEP-APU coatings in 3.5wt% NaCl solutions. The results indicated that the HEP-APU coatings show a superior passivation property and efficient corrosion protection of Q235 steel. The waterborne acrylic polyurethane coating containing 0.5wt% HEP exhibited the best corrosion performance among all the coating specimens. The improved flash-rust resistance can be attributed to the introduction of the phosphate group which could form phosphate film on the steel substrate.展开更多
文摘Hydroxyl-epoxy phosphate （HEP） as a reactive corrosion inhibitor was innovatively synthe- sized by the reaction of bisphenol A epoxy resin with phosphoric acid. HEP was mixed with hydroxyl acrylate resin, and crosslinked with waterborne isocyanate curing agent, which was used to form waterborne HEP/acrylic polyurethane composite （HEP-APU） coatings on Q235 steel surfaces. Electrochemical impedance spectroscopy and polarization curves were applied to analyze the corrosion behavior of the HEP-APU coatings in 3.5wt% NaCl solutions. The results indicated that the HEP-APU coatings show a superior passivation property and efficient corrosion protection of Q235 steel. The waterborne acrylic polyurethane coating containing 0.5wt% HEP exhibited the best corrosion performance among all the coating specimens. The improved flash-rust resistance can be attributed to the introduction of the phosphate group which could form phosphate film on the steel substrate.