A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer...A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.展开更多
The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching effic...The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching efficiency of zinc were examined. The leaching kinetics of low-grade zinc oxide ore in NH3-NH4Cl-H2O system follows the kinetic law of shrinking-core model. The results show that diffusion through the inert particle pores is the leaching kinetics rate controlling step. The calculated apparent activation energy of the process is about 7.057 kJ/mol. The leaching efficiency of zinc is 92.1% under the conditions of ore particle size of 69 μm, holding at 80 ℃ for 60 min, sum ammonia concentration of 7.5 mol/L, the molar ratio of ammonium to ammonia being 2-1, and the ratio (g/mL) of solid to liquid being 1-10.展开更多
The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperat...The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperature on anodic reaction rate were studied through the curve measurement of potentiostatic polarization. The results reveal that the electrochemically controlled anodic reaction obeys Tafel equation and the anodic reaction order for ammonium chloride is 1.056, with the apparent activation energy of 40.17 kJ/mol. The general equation of anodic reaction kinetics was obtained.展开更多
The crystal detachment behaviors from a chilling solid surface with vibration were investigated using a transparent NH4Cl-70%H2O alloy.The nucleation experiments of NH4Cl-70%H2O alloy were performed on a chilling surf...The crystal detachment behaviors from a chilling solid surface with vibration were investigated using a transparent NH4Cl-70%H2O alloy.The nucleation experiments of NH4Cl-70%H2O alloy were performed on a chilling surface generator with various vibration frequency from 20 to 1 000 Hz and vibration acceleration from 10 to 100 m/s2.The results indicate that the crystal detach rate increases and the grains are refined with increasing vibration acceleration under a certain vibration frequency.It is interesting to note that,when the frequency is 50 Hz,acceleration is 100 m/s2,the crystal detach rate increases sharply and the grain refinement effect is strengthened.A special grain refinement phenomenon can be observed,when the vibration acceleration and frequency are up to a critical value.A power-based definition was introduced in order to describe the relationship between the vibration parameters and imposed power on the system.It is found that a power criterion exists for the grain refinement in the current system.展开更多
基金Projects (51101096, 51002093) supported by the National Natural Science Foundation of ChinaProject (1052nm05000) supported by Special Foundation of the Shanghai Science and Technology Commission for Nano-Materials ResearchProject (J51042) supported by Leading Academic Discipline Project of the Shanghai Education Commission, China
文摘A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.
基金Project(2007CB613604) supported by the Major State Basic Research Development Program of ChinaProject(50674104) supported by the National Natural Science Foundation of ChinaProject(GJJ08279) supported by the Department of Education of Jiangxi Province
文摘The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching efficiency of zinc were examined. The leaching kinetics of low-grade zinc oxide ore in NH3-NH4Cl-H2O system follows the kinetic law of shrinking-core model. The results show that diffusion through the inert particle pores is the leaching kinetics rate controlling step. The calculated apparent activation energy of the process is about 7.057 kJ/mol. The leaching efficiency of zinc is 92.1% under the conditions of ore particle size of 69 μm, holding at 80 ℃ for 60 min, sum ammonia concentration of 7.5 mol/L, the molar ratio of ammonium to ammonia being 2-1, and the ratio (g/mL) of solid to liquid being 1-10.
文摘The anodic reaction kinetics of zinc electrowinning was investigated on the titanium base RuO2 anode in the system of Zn（Ⅱ）-NH3-NH4Cl-H2O. The effects of stirring speed, ammonium chloride concentration and temperature on anodic reaction rate were studied through the curve measurement of potentiostatic polarization. The results reveal that the electrochemically controlled anodic reaction obeys Tafel equation and the anodic reaction order for ammonium chloride is 1.056, with the apparent activation energy of 40.17 kJ/mol. The general equation of anodic reaction kinetics was obtained.
基金Projects(50571029,50771083) supported by the National Natural Science Foundation of ChinaProjects(02-TZ-2008,36-TP-2009) supported by State Key Laboratory of Solidification Processing in NWPU,China
文摘The crystal detachment behaviors from a chilling solid surface with vibration were investigated using a transparent NH4Cl-70%H2O alloy.The nucleation experiments of NH4Cl-70%H2O alloy were performed on a chilling surface generator with various vibration frequency from 20 to 1 000 Hz and vibration acceleration from 10 to 100 m/s2.The results indicate that the crystal detach rate increases and the grains are refined with increasing vibration acceleration under a certain vibration frequency.It is interesting to note that,when the frequency is 50 Hz,acceleration is 100 m/s2,the crystal detach rate increases sharply and the grain refinement effect is strengthened.A special grain refinement phenomenon can be observed,when the vibration acceleration and frequency are up to a critical value.A power-based definition was introduced in order to describe the relationship between the vibration parameters and imposed power on the system.It is found that a power criterion exists for the grain refinement in the current system.