The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic perf...The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic performance of Ni-Al2O3 catalyst for hydrogenation of 1,4-butynediol to produce 1,4-butenediol were investigated.The catalysts were characterized by PSD,EDX,XRD,H2-TPR,BET,TEM,and NH3-TPD methods.Results showed that the MCt2.5 catalyst treated at a ball milling time of 2.5 h could form a smallest particle size of 191.0 nm.The evaluation experiments revealed that the activity of the prepared catalyst increased at first and then reached a constant value with the extension of ballmilling time.The BYD conversion,BED selectivity and yield on the MCt2.5 catalyst reached 35.63%,33.48%and 32.46%,respectively,which were higher than those obtained by other samples.The excellent performance of MCt2.5 sample is mainly related to the following three reasons from characterization results.Firstly,it has a smallest particle size of 191.0 nm;and then,the surface acidity(in terms of strong acids)of the catalyst was weaker than other catalysts;and eventually,the loading amount(23.84%)of the active component Ni exceeded the theoretical value(20%).展开更多
基金This work has been supported by the Xinjiang Uygur Autonomous Region Key R&D Program(2017B02012)the Xinjiang University Natural Science Foundation Project(BS160221).
文摘The Ni-Al2O3 catalyst was prepared by the mechanochemical method in combination with a planetary ballmilling machine.Effect of milling time on the crystal structure,the reduction characteristics and the catalytic performance of Ni-Al2O3 catalyst for hydrogenation of 1,4-butynediol to produce 1,4-butenediol were investigated.The catalysts were characterized by PSD,EDX,XRD,H2-TPR,BET,TEM,and NH3-TPD methods.Results showed that the MCt2.5 catalyst treated at a ball milling time of 2.5 h could form a smallest particle size of 191.0 nm.The evaluation experiments revealed that the activity of the prepared catalyst increased at first and then reached a constant value with the extension of ballmilling time.The BYD conversion,BED selectivity and yield on the MCt2.5 catalyst reached 35.63%,33.48%and 32.46%,respectively,which were higher than those obtained by other samples.The excellent performance of MCt2.5 sample is mainly related to the following three reasons from characterization results.Firstly,it has a smallest particle size of 191.0 nm;and then,the surface acidity(in terms of strong acids)of the catalyst was weaker than other catalysts;and eventually,the loading amount(23.84%)of the active component Ni exceeded the theoretical value(20%).