The SiCf/SiC composites containing PyC interphase were prepared by chemical vapor infiltration process. The influences of thermal oxidation on the complex permittivity and microwave absorption properties of Si Cf/Si C...The SiCf/SiC composites containing PyC interphase were prepared by chemical vapor infiltration process. The influences of thermal oxidation on the complex permittivity and microwave absorption properties of Si Cf/Si C composites were investigated in the frequency range of 8.2-12.4 GHz. Both the real and imaginary parts of the complex permittivity decreased after thermal oxidation. The composites after 100 h thermal oxidation showed that reflection loss exceeded-10 d B in the frequency of 9.7-11.9 GHz and the minimum value was-11.4 d B at 11.0 GHz. The flexural strength of composites decreased but fracture behavior was improved obviously after thermal oxidation. These results indicate that the SiCf/SiC composites containing PyC interphase after thermal oxidation possess good microwave absorbing property and fracture behavior.展开更多
BN interphase was successfully synthesized on SiC fiber fabrics by dip-coating process using boric acid and urea as precursors under N2 atmosphere. The morphology of BN interphase was observed by SEM, and the structur...BN interphase was successfully synthesized on SiC fiber fabrics by dip-coating process using boric acid and urea as precursors under N2 atmosphere. The morphology of BN interphase was observed by SEM, and the structure was characterized by XRD and FT-IR spectra. The SiCf/SiC composites with dip-coated BN interphase were fabricated by chemical vapor infiltration （CVI） process, and the effects ofBN interphase on the mechanical properties of composites were investigated. The results show that the SiC fibers are fully covered by BN interphase with smooth surface and turbostratic structure （t-BN）, and the thickness is about 0.4 μm. The flexural strengths of SiCf/SiC composites with and without BN interphase are about 180 and 95 MPa, respectively. Compared with the as-received SiCf/SiC composites, the composites with BN interphase exhibit an obvious toughened fracture behavior. From the microstructural analysis, it can be confirmed that the BN interphase plays a key part in protecting the fibers from chemical attack during matrix infiltration and weakening interfacial bonding, which can improve the mechanical properties of SiCf/SiC composites remarkably.展开更多
SiC with fiber-reinforced composites, which are presently considered as the primary structural materials in some fusion reactor conceptual designs, are more attractive and competitive for structural materials in a fus...SiC with fiber-reinforced composites, which are presently considered as the primary structural materials in some fusion reactor conceptual designs, are more attractive and competitive for structural materials in a fusion energy system because of its excellent chemical and mechanical properties such as high fracture toughness, induced-low activation, afterheat under 14MeV neutron irradiation environment at elevated temperature, and good compatibility with coolant and breeder materials. Thus it is important to investigate the research progress of advanced SiC composite, including transmuted helium gas, radiation swelling, radiation effects on mechanical properties, irradiation-enhanced creep, fatigue, physical properties associated with fusion design and their critical issues. This report summarized these results and addressed the major critical issues under irradiation conditions.展开更多
基金Project(51072165)supported by the National Natural Science Foundation of ChinaProject(201305)supported by the Fund of State Key Laboratory of Solidification Processing,ChinaProjects(2013JK0921,2013JK0922)supported by Shaanxi Provincial Education Department of China
文摘The SiCf/SiC composites containing PyC interphase were prepared by chemical vapor infiltration process. The influences of thermal oxidation on the complex permittivity and microwave absorption properties of Si Cf/Si C composites were investigated in the frequency range of 8.2-12.4 GHz. Both the real and imaginary parts of the complex permittivity decreased after thermal oxidation. The composites after 100 h thermal oxidation showed that reflection loss exceeded-10 d B in the frequency of 9.7-11.9 GHz and the minimum value was-11.4 d B at 11.0 GHz. The flexural strength of composites decreased but fracture behavior was improved obviously after thermal oxidation. These results indicate that the SiCf/SiC composites containing PyC interphase after thermal oxidation possess good microwave absorbing property and fracture behavior.
基金Project(51072165)supported by the National Natural Science Foundation of ChinaProject(KP201307)supported by the Fund of the State Key Laboratory of Solidification Processing in NWPU
文摘BN interphase was successfully synthesized on SiC fiber fabrics by dip-coating process using boric acid and urea as precursors under N2 atmosphere. The morphology of BN interphase was observed by SEM, and the structure was characterized by XRD and FT-IR spectra. The SiCf/SiC composites with dip-coated BN interphase were fabricated by chemical vapor infiltration （CVI） process, and the effects ofBN interphase on the mechanical properties of composites were investigated. The results show that the SiC fibers are fully covered by BN interphase with smooth surface and turbostratic structure （t-BN）, and the thickness is about 0.4 μm. The flexural strengths of SiCf/SiC composites with and without BN interphase are about 180 and 95 MPa, respectively. Compared with the as-received SiCf/SiC composites, the composites with BN interphase exhibit an obvious toughened fracture behavior. From the microstructural analysis, it can be confirmed that the BN interphase plays a key part in protecting the fibers from chemical attack during matrix infiltration and weakening interfacial bonding, which can improve the mechanical properties of SiCf/SiC composites remarkably.
基金The project supported by the 21st COE research program of Kyoto University on the establishment of sustainable energy system
文摘SiC with fiber-reinforced composites, which are presently considered as the primary structural materials in some fusion reactor conceptual designs, are more attractive and competitive for structural materials in a fusion energy system because of its excellent chemical and mechanical properties such as high fracture toughness, induced-low activation, afterheat under 14MeV neutron irradiation environment at elevated temperature, and good compatibility with coolant and breeder materials. Thus it is important to investigate the research progress of advanced SiC composite, including transmuted helium gas, radiation swelling, radiation effects on mechanical properties, irradiation-enhanced creep, fatigue, physical properties associated with fusion design and their critical issues. This report summarized these results and addressed the major critical issues under irradiation conditions.
基金Project(6142907200301) supported by the National Defense Pre-Research Foundation of ChinaProject supported by the Key Laboratory for Lightweight High Strength Structural Materials,Central South University,China。