In this study,the effects of reaction parameters on the deep-reduction and carbonization process of WO_(2)-Co to WC-Co were studied.The results indicate that the oxygen loss rate of WO_(2) is positively correlated wit...In this study,the effects of reaction parameters on the deep-reduction and carbonization process of WO_(2)-Co to WC-Co were studied.The results indicate that the oxygen loss rate of WO_(2) is positively correlated with temperature and methane partial pressure.The partial pressure of methane has no significant effect on the formation rate of WC.The carbon content and particle size of the product increase with the increase of CH_(4) partial pressure.By synergistically regulating the reaction temperature to 950℃,the CH_(4) partial pressure to 1.25%,and the reaction time to 60 min,ultrafine WC-Co powder without h phase can be obtained.The particle size of the composite powder is 128 nm,with total carbon content of 6.16%,free carbon content of 0.4%,and residual oxygen content of 0.05%,respectively.The growth rate relationship of tungsten carbide is as follows:δ(t)=1.21×10^(-13)exp(-12809.72/T)√t.展开更多
基金financial support from the National Natural Science Foundation of China(22078326,21878305).
文摘In this study,the effects of reaction parameters on the deep-reduction and carbonization process of WO_(2)-Co to WC-Co were studied.The results indicate that the oxygen loss rate of WO_(2) is positively correlated with temperature and methane partial pressure.The partial pressure of methane has no significant effect on the formation rate of WC.The carbon content and particle size of the product increase with the increase of CH_(4) partial pressure.By synergistically regulating the reaction temperature to 950℃,the CH_(4) partial pressure to 1.25%,and the reaction time to 60 min,ultrafine WC-Co powder without h phase can be obtained.The particle size of the composite powder is 128 nm,with total carbon content of 6.16%,free carbon content of 0.4%,and residual oxygen content of 0.05%,respectively.The growth rate relationship of tungsten carbide is as follows:δ(t)=1.21×10^(-13)exp(-12809.72/T)√t.