Ti/TiN/Zr/ZrN multilayer coatings were deposited on Cr_17Ni_2 steel substrates with different surface roughnesses by vacuum cathodic arc deposition method. Microstructure, micro-hardness, adhesion strength and cross-s...Ti/TiN/Zr/ZrN multilayer coatings were deposited on Cr_17Ni_2 steel substrates with different surface roughnesses by vacuum cathodic arc deposition method. Microstructure, micro-hardness, adhesion strength and cross-sectional morphology of the obtained multilayer coatings were investigated. The results show that the Vickers hardness of Ti/TiN/Zr/ZrN multilayer coating, with a film thickness of 11.37 μm, is 29.36 GPa. The erosion and salt spray resistance performance of Cr_17Ni_2 steel substrates can be evidently improved by Ti/TiN/Zr/ZrN multilayer coating. The surface roughness of Cr_17Ni_2 steel substrates plays an important role in determining the mechanical and erosion performances of Ti/TiN/Zr/ZrN multilayer coatings. Overall, a low value of the surface roughness of substrates corresponds to an improved performance of erosion and salt spray resistance of multilayer coatings. The optimized performance of Ti/TiN/Zr/ZrN multilayer coatings can be achieved provided that the surface roughness of Cr_17Ni_2 steel substrates is lower than 0.4μm.展开更多
β-Sialon/ZrN/ZrON composites were successfully fabricated by an in-situ carbothermal reduction？nitridation process with fly ash, zircon and active carbon as raw materials. The effects of raw materials composition an...β-Sialon/ZrN/ZrON composites were successfully fabricated by an in-situ carbothermal reduction？nitridation process with fly ash, zircon and active carbon as raw materials. The effects of raw materials composition and holding time on synthesis process were investigated, and the formation process of the composites was also discussed. The phase composition and microstructure of the composites were characterized by means of XRD and SEM. It was found that increasing carbon content in a sample and holding time could promote the formation of β-Sialon, ZrN and ZrON. The proper processing parameters to synthesize β-Sialon/ZrN/ZrON composites were mass ratio of zircon to fly ash to active carbon of 49：100：100, synthesis temperature of 1550 °C and holding time of 15 h. The average grain size ofβ-Sialon and ZrN（ZrON） synthesized at 1550 °C for 15 h reached about 2 and 1μm, respectively. The fabrication process ofβ-Sialon/ZrN/ZrON composites included the formation ofβ-Sialon and ZrO2 as well as the conversion of ZrO2 to ZrN and ZrON.展开更多
基金Project(2011B050400007)supported by the International Cooperation Program of Guangdong Province,China
文摘Ti/TiN/Zr/ZrN multilayer coatings were deposited on Cr_17Ni_2 steel substrates with different surface roughnesses by vacuum cathodic arc deposition method. Microstructure, micro-hardness, adhesion strength and cross-sectional morphology of the obtained multilayer coatings were investigated. The results show that the Vickers hardness of Ti/TiN/Zr/ZrN multilayer coating, with a film thickness of 11.37 μm, is 29.36 GPa. The erosion and salt spray resistance performance of Cr_17Ni_2 steel substrates can be evidently improved by Ti/TiN/Zr/ZrN multilayer coating. The surface roughness of Cr_17Ni_2 steel substrates plays an important role in determining the mechanical and erosion performances of Ti/TiN/Zr/ZrN multilayer coatings. Overall, a low value of the surface roughness of substrates corresponds to an improved performance of erosion and salt spray resistance of multilayer coatings. The optimized performance of Ti/TiN/Zr/ZrN multilayer coatings can be achieved provided that the surface roughness of Cr_17Ni_2 steel substrates is lower than 0.4μm.
基金Project(2013AA030902)supported by the National High-tech Research and Development Program of ChinaProjects(51074038,51274057)supported by the National Natural Science Foundation of China+2 种基金Projects(N120402006,N100302002)supported by the Fundamental Research Funds for the Central Universities,ChinaProject(L2012079)supported by the Educational Commission of Liaoning Province of ChinaProject(110215)supported by the Training Program on National College Students Innovation Experiment
文摘β-Sialon/ZrN/ZrON composites were successfully fabricated by an in-situ carbothermal reduction？nitridation process with fly ash, zircon and active carbon as raw materials. The effects of raw materials composition and holding time on synthesis process were investigated, and the formation process of the composites was also discussed. The phase composition and microstructure of the composites were characterized by means of XRD and SEM. It was found that increasing carbon content in a sample and holding time could promote the formation of β-Sialon, ZrN and ZrON. The proper processing parameters to synthesize β-Sialon/ZrN/ZrON composites were mass ratio of zircon to fly ash to active carbon of 49：100：100, synthesis temperature of 1550 °C and holding time of 15 h. The average grain size ofβ-Sialon and ZrN（ZrON） synthesized at 1550 °C for 15 h reached about 2 and 1μm, respectively. The fabrication process ofβ-Sialon/ZrN/ZrON composites included the formation ofβ-Sialon and ZrO2 as well as the conversion of ZrO2 to ZrN and ZrON.