The dielectric performance of alkali activated slag （AAS） cement paste was investigated in the frequency range of 1 to 1000 MHz. The experimental results showed the unstable dielectric properties of harden paste wer...The dielectric performance of alkali activated slag （AAS） cement paste was investigated in the frequency range of 1 to 1000 MHz. The experimental results showed the unstable dielectric properties of harden paste were mostly influenced by the fraction of free water in paste or absorbed water from ambient, but not including hydration water and microstructure. The free water was completely eliminated by heat treatment at 105 ℃ about 4 hours, and then its dielectric loss was depressed; but with the exposure time in air increasing, the free water adsorption in ambient air made the dielectric property of harden cement paste to be bad. The temperature and relative humidity of environment was the key factors of free water adsorption; hence, if the influence of free water on dielectric constant was measured or eliminated, the cement-based materials may be applied in humidity sensitive materials or dielectric materials domains.展开更多
By means of 'Mortar Bar Method',the ratio of cement to aggregate was kept as a constant 1∶2.25,the water cement ratio of the mixture was 0.40,and six prism specimens were prepared for each batch of mixing pr...By means of 'Mortar Bar Method',the ratio of cement to aggregate was kept as a constant 1∶2.25,the water cement ratio of the mixture was 0.40,and six prism specimens were prepared for each batch of mixing proportions with dimensions of 10×10×60mm 3 at 38±2℃ and RH≥95%, the influences of content and particle size of active aggregate, sort and content of alkali component and type of slag on the expansion ratios of alkali activated slag cement(ASC) mortars due to alkali aggregate reaction(AAR) were studied. According to atomic absorption spectrometry,the amount of free alkali was measured in ASC mortars at 90d.The results show above factors affect AAR remarkably,but no dangerous AAR will occur in ASC system when the amount of active aggregate is below 15% and the mass fraction of alkali is not more than 5% (Na 2O).Alkali participated in reaction as an independent component, and some hydrates containing alkali cations were produced, free alkalis in ASC system can be reduced enormously.Moreover,slag is an effective inhibitor, the possibility of generating dangerous AAR in ASC system is much lower at same conditions than that in ordinary Portland cement system.展开更多
文摘The dielectric performance of alkali activated slag （AAS） cement paste was investigated in the frequency range of 1 to 1000 MHz. The experimental results showed the unstable dielectric properties of harden paste were mostly influenced by the fraction of free water in paste or absorbed water from ambient, but not including hydration water and microstructure. The free water was completely eliminated by heat treatment at 105 ℃ about 4 hours, and then its dielectric loss was depressed; but with the exposure time in air increasing, the free water adsorption in ambient air made the dielectric property of harden cement paste to be bad. The temperature and relative humidity of environment was the key factors of free water adsorption; hence, if the influence of free water on dielectric constant was measured or eliminated, the cement-based materials may be applied in humidity sensitive materials or dielectric materials domains.
文摘By means of 'Mortar Bar Method',the ratio of cement to aggregate was kept as a constant 1∶2.25,the water cement ratio of the mixture was 0.40,and six prism specimens were prepared for each batch of mixing proportions with dimensions of 10×10×60mm 3 at 38±2℃ and RH≥95%, the influences of content and particle size of active aggregate, sort and content of alkali component and type of slag on the expansion ratios of alkali activated slag cement(ASC) mortars due to alkali aggregate reaction(AAR) were studied. According to atomic absorption spectrometry,the amount of free alkali was measured in ASC mortars at 90d.The results show above factors affect AAR remarkably,but no dangerous AAR will occur in ASC system when the amount of active aggregate is below 15% and the mass fraction of alkali is not more than 5% (Na 2O).Alkali participated in reaction as an independent component, and some hydrates containing alkali cations were produced, free alkalis in ASC system can be reduced enormously.Moreover,slag is an effective inhibitor, the possibility of generating dangerous AAR in ASC system is much lower at same conditions than that in ordinary Portland cement system.