Interplay of laser power and pore characteristics in selective laser melting of ZK60 magnesium alloys:A study based on in-situ monitoring and image analysis

This study offers significant insights into the multi-physics phenomena of the SLM process and the subsequent porosity characteristics of ZK60 Magnesium(Mg)alloys.High-speed in-situ monitoring was employed to visualise process signals in real-time,elucidating the dynamics of melt pools and vapour plumes under varying laser power conditions specifically between 40 W and 60 W.Detailed morphological analysis was performed using Scanning-Electron Microscopy(SEM),demonstrating a critical correlation between laser power and pore formation.Lower laser power led to increased pore coverage,whereas a denser structure was observed at higher laser power.This laser power influence on porosity was further confirmed via Optical Microscopy(OM)conducted on both top and cross-sectional surfaces of the samples.An increase in laser power resulted in a decrease in pore coverage and pore size,potentially leading to a denser printed part of Mg alloy.X-ray Computed Tomography(XCT)augmented these findings by providing a 3D volumetric representation of the sample internal structure,revealing an inverse relationship between laser power and overall pore volume.Lower laser power appeared to favour the formation of interconnected pores,while a reduction in interconnected pores and an increase in isolated pores were observed at higher power.The interplay between melt pool size,vapour plume effects,and laser power was found to significantly influence the resulting porosity,indicating a need for effective management of these factors to optimise the SLM process of Mg alloys.

High-strength and thermally stable TiB_(2)-modified Al-Mn-Mg-Er-Zr alloy fabricated via selective laser melting

To increase the processability and plasticity of the selective laser melting(SLM)fabricated Al-Mn-Mg-Er-Zr alloys,a novel TiB_(2)-modified Al-Mn-Mg-Er-Zr alloy with a mixture of Al-Mn-Mg-Er-Zr and nano-TiB_(2) powders was fabricated by SLM.The pro-cessability,microstructure,and mechanical properties of the alloy were systematically investigated by density measurement,microstruc-ture characterization,and mechanical properties testing.The alloys fabricated at 250 W displayed higher relative densities due to a uni-formly smooth top surface and appropriate laser energy input.The maximum relative density value of the alloy reached(99.7±0.1)%,demonstrating good processability.The alloy exhibited a duplex grain microstructure consisting of columnar regions primarily and equiaxed regions with TiB_(2),Al6Mn,and Al3Er phases distributed along the grain boundaries.After directly aging treatment at a high tem-perature of 400℃,the strength of the SLM-fabricated TiB_(2)/Al-Mn-Mg-Er-Zr alloy increased due to the precipitation of the secondary Al6Mn phases.The maximum yield strength and ultimate tensile strength of the aging alloy were measured to be(374±1)and(512±13)MPa,respectively.The SLM-fabricated TiB_(2)/Al-Mn-Mg-Er-Zr alloy demonstrates exceptional strength and thermal stability due to the synergistic effects of the inhibition of grain growth,the incorporation of TiB_(2) nanoparticles,and the precipitation of secondary Al6Mn nanoparticles.

Effects of processing parameters on fabrication defects,microstructure and mechanical properties of additive manufactured Mg–Nd–Zn–Zr alloy by selective laser melting process

Mg–3Nd–0.2Zn–0.4Zr(NZ30K,wt.%)alloy is a new kind of high-performance metallic biomaterial.The combination of the NZ30K Magnesium(Mg)alloy and selective laser melting(SLM)process seems to be an ideal solution to produce porous Mg degradable implants.However,the microstructure evolution and mechanical properties of the SLMed NZ30K Mg alloy were not yet studied systematically.Therefore,the fabrication defects,microstructure,and mechanical properties of the SLMed NZ30K alloy under different processing parameters were investigated.The results show that there are two types of fabrication defects in the SLMed NZ30K alloy,gas pores and unfused defects.With the increase of the laser energy density,the porosity sharply decreases to the minimum first and then slightly increases.The minimum porosity is 0.49±0.18%.While the microstructure varies from the large grains with lamellar structure inside under low laser energy density,to the large grains with lamellar structure inside&the equiaxed grains&the columnar grains under middle laser energy density,and further to the fine equiaxed grains&the columnar grains under high laser energy density.The lamellar structure in the large grain is a newly observed microstructure for the NZ30K Mg alloy.Higher laser energy density leads to finer grains,which enhance all the yield strength(YS),ultimate tensile strength(UTS)and elongation,and the best comprehensive mechanical properties obtained are YS of 266±2.1 MPa,UTS of 296±5.2 MPa,with an elongation of 4.9±0.68%.The SLMed NZ30K Mg alloy with a bimodal-grained structure consisting of fine equiaxed grains and coarser columnar grains has better elongation and a yield drop phenomenon.

Selective Laser Melting of Novel SiC and TiC Strengthen 7075 Aluminum Powders for Anti-Cracks Application

The aerospace and military sectors have widely used AA7075, a type of 7075 aluminum alloy, due to its exceptional mechanical performance. Selective laser melting (SLM) is a highly effective method for producing intricate metallic components, particularly in the case of aluminum alloys like Al-Si-Mg. Nevertheless, the production of high-strength AA7075 by SLM is challenging because of its susceptibility to heat cracking and elemental vaporization. In this study, AA7075 powders were mechanically mixed with SiC and TiC particles. Subsequently, this new type of AA7075 powder was effectively utilized in green laser printing to create solid components with fine-grain strengthening microstructures consisting of equiaxial grains. These as-printed parts exhibit a tensile strength of up to 350 MPa and a ductility exceeding 2.1%. Hardness also increases with the increasing content of mixed powder, highlighting the essential role of SiC and TiC in SLM for improved hardness and tensile strength performance. .

Strength and plasticity improvement induced by strong grain refinement after Zr alloying in selective laser-melted AlSiMg1.4 alloy

In order to enhance the mechanical properties of the selective laser-melted(SLM) high-Mg content AlSiMg1.4 alloy,the Zr element was introduced.The influence of Zr alloying on the processability,microstructure,and mechanical properties of the alloy was systematically investigated through performing microstructure analysis and tensile testing.It was demonstrated that the SLM-fabricated AlSiMg1.4-Zr alloy exhibited high process stability with a relative density of over 99.5% at various process parameters.Besides,the strong grain refinement induced by the primary Al3Zr particle during the melt solidification process simultaneously enhanced both the strength and plasticity of the alloy.The values for the yield strength,ultimate tensile strength,and elongation of the SLM-fabricated AlSiMg1.4-Zr were(343±3) MPa,(485±4) MPa,and(10.2±0.2)%,respectively,demonstrating good strengthplasticity synergy in comparison to the AlSiMg1.4 and other Al-Si-based alloys fabricated by SLM.

Crack elimination and strength enhancement mechanisms of selective laser melted Si-modified Al−Mn−Mg−Er−Zr alloy

In order to increase the processability and process window of the selective laser melting(SLM)-fabricated Al−Mn−Mg−Er−Zr alloy,a novel Si-modified Al−Mn−Mg−Er−Zr alloy was designed.The effect of Si alloying on the surface quality,processability,microstructure,and mechanical properties of the SLM-fabricated alloy was studied.The results showed that introducing Si into the Al−Mn−Mg−Er−Zr alloy prevented balling and keyhole formation,refined the grain size,and reduced the solidification temperature,which eliminated cracks and increased the processability and process window of the alloy.The maximum relative density of the SLM-fabricated Si/Al−Mn−Mg−Er−Zr alloy reached 99.6%.The yield strength and ultimate tensile strength of the alloy were(371±7)MPa and(518±6)MPa,respectively.These values were higher than those of the SLM-fabricated Al−Mn−Mg−Er−Zr and other Sc-free Al−Mg-based alloys.

Effects of heat input on layer heterogeneity of selective laser melting Ti-6Al-4V components

Due to the layer-by-layer manufacturing characteristics,metallurgical process of selective laser melting(SLM)is inherently dif-ferent in the building direction because of varying conditions,thereby resulting inter-layer heterogeneity.To mitigate such anisotropy,it is of great significance to understand the effects of processing parameters on the property evolution and thus metallurgy of fabrication process.This research proposes one-factor-at-a-time experiment to investigate the influences of laser power and scanning speed on the surface qual-ity,microstructures and mechanical properties of selective laser melted Ti-6Al-4V parts.Surface quality is assessed by roughness around the printings while mechanical properties are evaluated through microhardness and tensile strengths.Phases in microstructure are quantified by XRD to correlate with mechanical properties.Fracture morphology is analyzed to understand the effect of defects and microstructure on mechanical performance.The optimized parameter corresponding to best surface quality and mechanical properties has been found respect-ively in laser power of 190 W and scanning speed of 800 mm/s.After optimization,surface roughness has decreased by 44.47%for upper surface.Yielding strength,tensile strength and elongation rate have improved by 13.17%,43.34%and 64.51%,respectively,with similar hardness and Young’s modulus.In addition,heterogeneity of mechanical properties has great improvement by a range of 31.63%-92.68%.

Microstructure,Properties and Crack Suppression Mechanism of High-speed Steel Fabricated by Selective Laser Melting at Different Process Parameters

To enrich material types applied to additive manufacturing and enlarge application scope of additive manufacturing in conformal cooling tools,M2 high-speed steel specimens were fabricated by selective laser melting(SLM).Effects of SLM parameters on the microstructure and mechanical properties of M2 high-speed steel were investigated.The results showed that substrate temperature and energy density had significant influence on the densification process of materials and defects control.Models to evaluate the effect of substrate temperature and energy density on hardness were studied.The optimized process parameters,laser power,scan speed,scan distance,and substrate temperature,for fabricated M2 are 220 W,960 mm/s,0.06 mm,and 200℃,respectively.Based on this,the hardness and tensile strength reached 60 HRC and 1000 MPa,respectively.Interlaminar crack formation and suppression mechanism and the relationship between temperature gradient and thermal stress were illustrated.The inhibition effect of substrate temperature on the cracks generated by residual stresses was also explained.AM showed great application potential in the field of special conformal cooling cutting tool preparation.

Surface Integrity of Inconel 738LC Parts Manufactured by Selective Laser Melting Followed by High-speed Milling

This study is concerned with the surface integrity of Inconel 738LC parts manufactured by selective laser melting(SLM)followed by high-speed milling(HSM).In the investigation process of surface integrity,the study employs ultradepth three-dimensional microscopy,laser scanning confocal microscopy,scanning electron microscopy,electron backscatter diffractometry,and energy dispersive spectroscopy to characterize the evolution of material microstructure,work hardening,residual stress coupling,and anisotropic effect of the building direction on surface integrity of the samples.The results show that SLM/HSM hybrid manufacturing can be an effective method to obtain better surface quality with a thinner machining metamorphic layer.High-speed machining is adopted to reduce cutting force and suppress machining heat,which is an effective way to produce better surface mechanical properties during the SLM/HSM hybrid manufacturing process.In general,high-speed milling of the SLM-built Inconel 738LC samples offers better surface integrity,compared to simplex additive manufacturing or casting.

Topology optimization of microstructure and selective laser meltingfabrication for metallic biomaterial scaffolds

The precise design and fabrication of biomaterial scaffolds is necessary to provide a systematic study for bone tissue engineering. Biomaterial scaffolds should have sufficient stiffness and large porosity. These two goals generally contradict since larger porosity results in lower mechanical properties. To seek the microstructure of maximum stiffness with the constraint of volume fraction by topology optimization method, algorithms and programs were built to obtain 2D and 3D optimized microstructure and then they were transferred to CAD models of STL format. Ti scaffolds with 30% volume fraction were fabricated using a selective laser melting （SLM） technology. The architecture and pore shape in the metallic biomaterial scaffolds were relatively precise reproduced and the minimum mean pore size was 231μm. The accurate fabrication of intricate microstructure has verified that the SLM process is suitable for fabrication of metallic biomaterial scaffolds.

Selective laser melted AZ91D magnesium alloy with superior balance of strength and ductility

In the context of global carbon neutrality, the application of lightweight magnesium alloys is becoming increasingly attractive. In this study, selective laser melting(SLM) was employed to achieve nearly full dense and crack-free AZ91D components with fine equiaxed grain structure. The formation mechanism of typical pore defects(gas pore, lack-of-fusion pore and keyhole pore) and melting modes(keyhole mode and conduction mode) were systematically studied by varying the laser power and scanning speed. The morphology and volume fraction of the pores under different processing conditions were characterized. A criterion based on the depth-to-width ratio of the melt pool was established to identify different melting modes. The strength and ductility(tensile strength up to 340 MPa and uniform elongation of 8.9%)of the as deposited AZ91D are far superior to those of the casting components and are comparable to those of its wrought counterparts.The superior balance of strength and ductility of SLMed AZ91D, as well as the negligible anisotropic properties are mainly ascribed to the extremely fine equiaxed grain structure(with average grain size of ~1.2 μm), as well as the discontinuous distribution of β-Al_(12)Mg_(17) phases. It thus provides an alternative way to fabricate high-strength magnesium alloys with complex geometry.

Defect Formation Mechanisms in Selective Laser Melting:A Review

Defect formation is a common problem in selective laser melting （SLM）. This paper provides a review of defect formation mechanisms in SLM. It sum- marizes the recent research outcomes on defect findings and classification, analyzes formation mechanisms of the common defects, such as porosities, incomplete fusion holes, and cracks. The paper discusses the effect of the process parameters on defect formation and the impact of defect formation on the mechanical properties of a fabri- cated part. Based on the discussion, the paper proposes strategies for defect suppression and control in SLM.

A review of particulate-reinforced aluminum matrix composites fabricated by selective laser melting

Selective laser melting(SLM)is an emerging layer-wise additive manufacturing technique that can generate complex components with high performance.Particulate-reinforced aluminum matrix composites(PAMCs)are important materials for various applications due to the combined properties of Al matrix and reinforcements.Considering the advantages of SLM technology and PAMCs,the novel SLM PAMCs have been developed and researched in recent years.Therefore,the current research progress about the SLM PAMCs is reviewed.Firstly,special attention is paid to the solidification behavior of SLM PAMCs.Secondly,the important issues about the design and fabrication of high-performance SLM PAMCs,including the selection of reinforcement,the influence of parameters on the processing and microstructure,the defect evolution and phase control,are highlighted and discussed comprehensively.Thirdly,the performance and strengthening mechanism of SLM PAMCs are systematically figured out.Finally,future directions are pointed out on the advancement of high-performance SLM PAMCs.

Wear behavior of Ti6Al4V biomedical alloys processed by selective laser melting, hot pressing and conventional casting

The aim of this work was to study the influence of the processing route on the microstructural constituents,hardness andtribological(wear and friction)behavior of Ti6Al4V biomedical alloy.In this sense,three different processing routes were studied:conventional casting,hot pressing and selective laser melting.A comprehensive metallurgical,mechanical and tribologicalcharacterization was performed by X-ray diffraction analysis,Vickers hardness tests and reciprocating ball-on-plate wear tests ofTi6Al4V/Al2O3sliding pairs.The results showed a great influence of the processing route on the microstructural constituents andconsequent differences on hardness and wear performance.The highest hardness and wear resistance were obtained for Ti6Al4Valloy produced by selective laser melting,due to a markedly different cooling rate that leads to significantly different microstructurewhen compared to hot pressing and casting.This study assesses and confirms that selective laser melting is potential to producecustomized Ti6Al4V implants with improved wear performance.

Effect of Nb additions on microstructure and properties of γ-TiAl based alloys fabricated by selective laser melting

The γ-TiAl based Ti.Al.Mn.Nb alloys with different Nb additions were fabricated by selective laser melting (SLM) on the TC4 substrate. The effects of Nb content on microstructure and properties of the alloys were investigated. The results reveal that the alloys consist of γ-TiAl phase with tetragonal lattice structure and α2-Ti3Al phase with hcp lattice structure, and show a sequential structure change from near full dendrite to near lamellar structure with the increase of Nb addition. Owing to the higher Nb content in γ-TiAl phase and the formation of near lamellar structure, the alloy with 7.0 at.% Nb addition has the best combination of properties among the studied alloys, namely, not only a high hardness of HV 2000, a high strength of 1390 MPa and a plastic deformation of about 24.5%, but also good tribological properties and high-temperature oxidation resistance.

Microstructure and mechanical properties of Ti6Al4V alloy prepared by selective laser melting combined with precision forging

To improve the mechanical properties of Ti6Al4V alloy prepared by selective laser melting(SLM)process,the precision forging was conducted at950°C and different strains and strain rates.The microstructure evolution of as-built samples and forged samples in both horizontal and vertical sections was visualized and analyzed by optical microscope and X-ray diffraction.The microstructure was improved by the precision forging and subsequent water quenching.The porosity in each section was accounted.It can be seen that high strain rate and large deformation result in low porosity,consequently contributing to a better fatigue performance.The micro-hardness was lowered after precision forging and water quenching,while the difference of microhardness between the horizontal and vertical sections became smaller,which illustrated that this process can improve the anisotropy of structural components fabricated by SLM.

Microstructure and mechanical properties of high strength Mg−15Gd−1Zn−0.4Zr alloy additive-manufactured by selective laser melting process

In order to verify the feasibility of producing Mg−rare earth(RE)alloy by selective laser melting(SLM)process,the microstructure and mechanical properties of Mg−15Gd−1Zn−0.4Zr(wt.%)(GZ151K)alloy were investigated.The results show that fine grains(~2μm),fine secondary phases and weak texture,were observed in the as-fabricated(SLMed)GZ151K Mg alloy.At room temperature,the SLMed GZ151K alloy has a yield strength(YS)of 345 MPa,ultimate tensile strength(UTS)of 368 MPa and elongation of 3.0%.After subsequent aging(200℃,64 h,T5 treatment),the YS,UTS and elongation of the SLMed-T5 alloy are 410 MPa,428 MPa and 3.4%,respectively,which are higher than those of the conventional cast-T6 alloy,especially with the YS increased by 122 MPa.The main strengthening mechanisms of the SLMed GZ151K alloy are fine grains,fine secondary phases and residual stress,while after T5 treatment,the YS of the alloy is further enhanced by precipitates.

Research progress on selective laser melting processing for nickel-based superalloy

Selective laser melting(SLM),an additive manufacturing process mostly applied in the metal material field,can fabricate complex-shaped metal objects with high precision.Nickel-based superalloy exhibits excellent mechanical properties at elevated temperatures and plays an important role in the aviation industry.This paper emphasizes the research of SLM processed Inconel 718,Inconel 625,CM247LC,and Hastelloy X,which are typical alloys with different strengthening mechanisms and operating temperatures.The strengthening mechanism and phase change evolution of different nickel-based superalloys under laser irradiation are discussed.The influence of laser parameters and the heat-treatment process on mechanical properties of SLM nickel-based superalloys are systematically introduced.Moreover,the attractive in-dustrial applications of SLM nickel-based superalloy and printed components are presented.Finally,the prospects for nickel-based superalloy materials for SLM technology are presented.

Tensile behavior of Ti-6Al-4V alloy fabricated by selective laser melting: effects of microstructures and as-built surface quality

Selective laser melting （SLM） is a powerful additive manufacturing （AM） technology, of which the most prominent advantage is the ability to produce components with a complex geometry. The service performances of the SLM-processed components depend on the microstructure and surface quality. In this work, the microstructures, mechanical properties, and fracture behaviors of SLM-processed Ti-6AI-4V alloy under machined and as-built surfaces after annealing treatments and hot isostatic pressing （HIP） were investigated. The microstructures were analyzed by optical microscope （OM）, scanning electron microscope （SEM） and transmission electron microscopy （TEM）. The mechanical properties were measured by tensile testing at room temperature. The results indicate that the as-deposited microstructures are characterized by columnar grains and fine brittle martensite and the as- deposited properties present high strength, low ductility and obvious anisotropy. After annealing at 800-900~C for 2-4 h and HIP at 920~C/100MPa for 2 h, the brittle martensite could be transformed into ductile lamellar （a＋~） microstructure and the static tensile properties of SLM-processed Ti-6AI-4V alloys in the machined condition could be comparable to that of wrought materials. Even after HIP treatment, the as-built surfaces could decrease the ductility and reduction of area of SLM-processed fi-6AI-4V alloys to 9.2% and 20%, respectively. The crack initiation could occur at the columnar grain boundaries or at the as-built surfaces. The lamellar （a＋13） microstructures and columnar grains could hinder or distort the crack propagation path during tensile tests.

Effects of selective laser melting parameters on surface quality and densification behaviours of pure nickel

The effects of laser power and scanning speed on the forming characteristic of scanning tracks,densification behaviours and surface roughness of pure nickel fabricated with selective laser melting(SLM)were studied.The results indicate that the scanning tracks showed continuous,regular and flat surface with increasing laser power and decreasing scanning speed in a specific range,which could avoid the defects(like holes and balling structures)forming in SLM processing.The optimal process window was identified as the scanning speed of 900 mm/s and the laser power of 255−275 W by comparing the surface qualities and densification behaviours.With the suitable processing parameters,the relative density could achieve 99.16%,the tensile strength was(359.49±2.74)MPa,and the roughnesses of the top and side surfaces were(12.88±2.23)and(14.98±0.69)μm,respectively.