Effect of Sintering Temperature on the Microstructure and Mechanical Properties of Nanocrystalline Cemented Carbide

WC-Co nanocrystalline nitrogen-containing cemented carbides were prepared by vacuum sintering and low pressure sintering.The sintering processes of Cr_(2)(C,N)doped nano WC-Co powders were studied by using thermogravimetric analysis(TGA)and differential scanning calorimetry(DSC).The effect of sintering temperature on the microstructure and mechanical properties of nanocrystalline cemented carbide was studied by scanning electron microscope(SEM),high resolution transmission electron microscope(HRTEM)and mechanical property test.The results showed that the nano WC grains began to grow in the solid phase sintering stage.A high-performance nano-nitrogen-containing cemented carbide with uniform microstructure and good interfacial bonding can be obtained by increasing the sintering temperature to 1380℃.It has a transverse rupture strength(TRS)of 5057 MPa and a hardness of 1956 HV30.

Micro air vehicle-motivated computational biomechanics in bio-flights:aerodynamics,flight dynamics and maneuvering stability

Aiming at developing an effective tool to unveil key mechanisms in bio-flight as well as to provide guidelines for bio-inspired micro air vehicles（MAVs） design,we propose a comprehensive computational framework,which integrates aerodynamics,flight dynamics,vehicle stability and maneuverability.This framework consists of（1） a Navier-Stokes unsteady aerodynamic model;（2） a linear finite element model for structural dynamics;（3） a fluidstructure interaction（FSI） model for coupled flexible wing aerodynamics aeroelasticity;（4） a free-flying rigid body dynamic（RBD） model utilizing the Newtonian-Euler equations of 6DoF motion;and（5） flight simulator accounting for realistic wing-body morphology,flapping-wing and body kinematics,and a coupling model accounting for the nonlinear 6DoF flight dynamics and stability of insect flapping flight.Results are presented based on hovering aerodynamics with rigid and flexible wings of hawkmoth and fruitfly.The present approach can support systematic analyses of bio- and bio-inspired flight.

Micro/nano Indentation and Single Grit Diamond Grinding Mechanism on Ultra Pure Fused Silica

The existing research about ductile grinding of fused silica glass was mainly focused on how to carry out ductile regime material removal for generating very ＂smoothed＂ surface and investigate the machining-induced damage in the grinding in order to reduce or eliminate the subsurface damage.The brittle/ductile transition behavior of optical glass materials and the wear of diamond wheel are the most important factors for ductile grinding of optical glass.In this paper,the critical brittle/ductile depth,the influence factors on brittle/ductile transition behavior,the wear of diamond grits in diamond grinding of ultra pure fused silica（UPFS） are investigated by means of micro/nano indentation technique,as well as single grit diamond grinding on an ultra-stiff machine tool,Tetraform ＂C＂.The single grit grinding processes are in-process monitored using acoustic emission（AE） and force dynamometer simultaneously.The wear of diamond grits,morphology and subsurface integrity of the machined groves are examined with atomic force microscope（AFM） and scanning electron microscope（SEM）.The critical brittle/ductile depth of more than 0.5 μm is achieved.When compared to the using roof-like grits,by using pyramidal diamonds leads to higher critical depths of scratch with identical grinding parameters.However,the influence of grit shapes on the critical depth is not significant as supposed.The grinding force increased linearly with depth of cut in the ductile removal regime,but in brittle removal regime,there are large fluctuations instead of forces increase.The SEM photographs of the cross-section profile show that the median cracks dominate the crack patterns beneath the single grooves.Furthermore,The SEM photographs show multi worn patterns of diamond grits,indicating an inhomogeneous wear mechanism of diamond grits in grinding of fused silica with diamond grinding wheels.The proposed research provides the basal technical theory for improving the ultra-precision grinding of UPFS.

Effects of nano TiN addition on the microstructure and mechanical properties of TiC based steel bonded carbides

TiC based steel bonded carbides with the addition of nano TiN were prepared by vacuum sintering techniques.The microstructure was investigated using scanning electron microscopy（SEM） and transmission electron microscopy（TEM）,and the mechanical properties,such as bending strength,impact toughness,hardness,and density,were measured.The results indicate that the grain size becomes small and there is uniformity in the steel bonded carbide with nano addition;several smaller carbide particles are also found to be inlaid in the rim of the larger carbide grains and prevent the coalescence of TiC grains.The smaller and larger carbide grains joint firmly,and then the reduction of the average size of the grains leads to the increase in the mechanical properties of the steel bonded carbides with nano addition.But the mechanical properties do not increase monotonously with an increase in nano addition.When the nano TiN addition accounts for 6-8 wt.% of the amount of steel bonded carbides,the mechanical properties reach the maximum values and then decrease with further increase in nano TiN addition.

Ignition processes and characteristics of charring conductive polymers with a cavity geometry in precombustion chamber for applications in micro/nano satellite hybrid rocket motors

The arc ignition system based on charring polymers has advantages of simple structure,low ignition power consumption and multiple ignitions,which bringing it broadly application prospect in hybrid propulsion system of micro/nano satellite.However,charring polymers alone need a relatively high input voltage to achieve pyrolysis and ignition,which increases the burden and cost of the power system of micro/nano satellite in practical application.Adding conductive substance into charring polymers can effectively decrease the conducting voltage which can realize low voltage and low power consumption repeated ignition of arc ignition system.In this paper,a charring conductive polymer ignition grain with a cavity geometry in precombustion chamber,which is composed of PLA and multiwall carbon nanotubes(MWCNT)was proposed.The detailed ignition processes were analyzed and two different ignition mechanisms in the cavity of charring conductive polymers were revealed.The ignition characteristics of charring conductive polymers were also investigated at different input voltages,ignition grain structures,ignition locations and injection schemes in a visual ignition combustor.The results demonstrated that the ignition delay and external energy required for ignition were inversely correlated with the voltages applied to ignition grain.Moreover,the incremental depth of cavity shortened the ignition delay and external energy required for ignition while accelerated the propagation of flame.As the depth of cavity increased from 2 to 6 mm(at 50 V),the time of flame propagating out of ignition grain changed from 235.6 to 108 ms,and values of mean ignition delay time and mean external energy required for ignition decreased from 462.8 to 320 ms and 16.2 to 10.75 J,respectively.The rear side of the cavity was the ideal ignition position which had a shorter ignition delay and a faster flame propagation speed in comparison to other ignition positions.Compared to direct injection scheme,swirling injection provided a more favorable flow field environment in the cavity,which was beneficial to ignition and initial flame propagation,but the ignition position needed to be away from the outlet of swirling injector.At last,the repeated ignition characteristic of charring conductive polymers was also investigated.The ignition delay time and external energy required for ignition decreased with repeated ignition times but the variation was decreasing gradually.

Macroscopic and microscopic mechanical behavior and seepage characteristics of coal under hydro-mechanical coupling

Understanding the physical,mechanical behavior,and seepage characteristics of coal under hydro-mechanical coupling holds significant importance for ensuring the stability of surrounding rock formations and preventing gas outbursts.Scanning electron microscopy,uniaxial tests,and triaxial tests were conducted to comprehensively analyze the macroscopic and microscopic physical and mechanical characteristics of coal under different soaking times.Moreover,by restoring the stress path and water injection conditions of the protective layer indoors,we explored the coal mining dynamic behavior and the evolution of permeability.The results show that water causes the micro-surface of coal to peel off and cracks to expand and develop.With the increase of soaking time,the uniaxial and triaxial strengths were gradually decreased with nonlinear trend,and decreased by 63.31%and 30.95%after soaking for 240 h,respectively.Under different water injection pressure conditions,coal permeability undergoes three stages during the mining loading process and ultimately increases to higher values.The peak stress of coal,the deviatoric stress and strain at the permeability surge point all decrease with increasing water injection pressure.The results of this research can help improve the understanding of the coal mechanical properties and seepage evolution law under hydro-mechanical coupling.

On-Chip Micro Temperature Controllers Based on Freestanding Thermoelectric Nano Films for Low-Power Electronics

Multidimensional integration and multifunctional com-ponent assembly have been greatly explored in recent years to extend Moore’s Law of modern microelectronics.However,this inevitably exac-erbates the inhomogeneity of temperature distribution in microsystems,making precise temperature control for electronic components extremely challenging.Herein,we report an on-chip micro temperature controller including a pair of thermoelectric legs with a total area of 50×50μm^(2),which are fabricated from dense and flat freestanding Bi2Te3-based ther-moelectric nano films deposited on a newly developed nano graphene oxide membrane substrate.Its tunable equivalent thermal resistance is controlled by electrical currents to achieve energy-efficient temperature control for low-power electronics.A large cooling temperature difference of 44.5 K at 380 K is achieved with a power consumption of only 445μW,resulting in an ultrahigh temperature control capability over 100 K mW^(-1).Moreover,an ultra-fast cooling rate exceeding 2000 K s^(-1) and excellent reliability of up to 1 million cycles are observed.Our proposed on-chip temperature controller is expected to enable further miniaturization and multifunctional integration on a single chip for microelectronics.

Active Micro-Nano-Collaborative Bioelectronic Device for Advanced Electrophysiological Recording

The development of precise and sensitive electrophysiological recording platforms holds the utmost importance for research in the fields of cardiology and neuroscience.In recent years,active micro/nano-bioelectronic devices have undergone significant advancements,thereby facilitating the study of electrophysiology.The distinctive configuration and exceptional functionality of these active micro-nano-collaborative bioelectronic devices offer the potential for the recording of high-fidelity action potential signals on a large scale.In this paper,we review three-dimensional active nano-transistors and planar active micro-transistors in terms of their applications in electroexcitable cells,focusing on the evaluation of the effects of active micro/nano-bioelectronic devices on electrophysiological signals.Looking forward to the possibilities,challenges,and wide prospects of active micro-nano-devices,we expect to advance their progress to satisfy the demands of theoretical investigations and medical implementations within the domains of cardiology and neuroscience research.

Effect of nano-silver on microstructure, mechanical and tribological properties of cast 6061 aluminum alloy

Al6061matrix with different amounts of nano-silver(1%and2%)was produced by stir-casting method.Producedsamples were characterized by hardness,tensile,compression and wear tests.The hardness of the specimens at room temperature wasmeasured by Brinnell hardness testing machine.The magnitude of hardness increased evidently with the function of the mass fractionof the nano-Ag particle.The polished specimens were examined with an optical microscope.The fracture surfaces of tensile andcompressive specimens were further examined by scanning electron microscopy.Wear mechanisms were discussed based on thescanning electron microscopy observations of worn surface and wear debris morphology.There is an increase in compressivestrength,ultimate tensile strength,elongation and wear resistance of the Al?Ag composites compared with base alloy.The executionof stir-casting technique is relatively homogenous and fine microstructure which improves the addition of reinforcement material inthe molten metal.The results show that Al6061?nano-silver which is the best combination of hardness can replace the conventionalmaterial for better performance and longer life.

Research on a Diamond Tip Wear Mechanism in Atomic Force Microscope-based Micro/nano-machining

The object is to investigate the wear of an atomic force microscope (AFM) diamond tip when conducting micro/nano machining on single crystal silicon surface. The experimental research and theoretical analysis were carried out on the worn tip in terms of wear rate, wear mechanism and the effect of the tip wear on micro machining process. The wear rate was calculated as 1.7(10～10mm 3/(N·m) by using a theoretical model combined with the experimental results. Through an integration of an AFM observation on the worn tip features with the FEM simulation of the stress distribution, in addition to the unit cutting force calculation on the AFM diamond tip, the wear mechanism of the AFM diamond tip was concluded as mainly chemical wear, and the wear process was also elaborated as well.

Preparation and Mechanical Properties of Micro- and Nano-sized SiC/Fluoroelastomer Composites

Microand nano-sized SiC/fluoroelastomer （FKM） composites were prepared by a mechanical mixing method. These composites were first characterized by a rotorless rheometer. Then the effects of micro- and nano-sized SiC on hardness, static and dynamic mechanical properties of the composites were investigated. The increasing amount of the SiC filler increased the curing efficiency of the biphenyl curing system, which was evident from the rheometric properties of the resulting composites. The tensile properties of composite increased with the increasing of micro- and nano-sized SiC content. When the micro- and nano-sized SiC content was higher than 20 phr, the composites showed almost unchanged tensile properties. The increasing of the tensile property was mainly attributed to the well dispersed micro- and nano-sized SiC particles characterized by SEM images. Compared to pure FKM, the composites exhibited a higher glass transition temperature and lower tan peak value.

The Influence of Carbon Nanotubes and Nano-Silica Fume on Enhancing the Damping and Mechanical Properties of Cement-Based Materials

This paper conducted experimental studies on the damping and mechanical properties of carbon nanotube-nanosilica-cement composite materials with different carbon nanotube contents. The damping and mechanical properties enhancement mechanisms were analyzed and compared through the porosity structure test, XRD analysis, and scanning electron microscope observation. The results show that the introduction of nanosilica significantly improves the dispersion of carbon nanotubes in the cement matrix. At the same time, the addition of nanosilica not only effectively reduces the critical pore size and average pore size of the cement composite material, but also exhibits good synergistic effects with carbon nanotubes, which can significantly optimize the pore structure. Finally, a rationalization suggestion for the co-doping of nanosilica and carbon nanotubes was given to achieve a significant increase in the flexural strength, compressive strength and loss factor of cement-based materials.

Design and micro mechanical properties of nano-SiO_2 strengthened composite coatings towards remanufacturing

Nano-SiO2 particles strengthened Ni-based composite coating was designed and prepared on steel substrate. The structures and nanoparticle content of the nano-SiO2/Ni composite coating were determined by SEM, EDS and TEM; and the micro mechanical properties were tested by nano-indentation technique. The results show that 56% of particles in the solution are dispersed in size of less than 100nm, the content of nanoparticles co-deposited in the coating doubles and structure of the coating is more compact and uniform than that of Ni coating. Nano-SiO2/Ni coating exhibits excellent micro mechanical properties, and the nanohardness and elastic modulus are 7.81GPa and 198GPa, respectively, which are attributed to finer crystal strengthening, dispersion strengthening and high-density dislocation strengthening of nano-SiO2 particles to the composite coatings.

Overview of Computational Modeling in Nano/Micro Scaled Thin Films Mechanical Properties and Its Applications

This research reviews the application of computational mechanics on the properties of nano/micro scaled thin films,in which the application of different computational methods is included.The concept and fundamental theories of concerned applications,material behavior estimations,interfacial delamination behavior,strain engineering,and multilevel modeling are thoroughly discussed.Moreover,an example of an interfacial adhesion estimation is presented to systematically estimate the related mechanical reliability issue in the microelectronic industry.The presented results show that the peeled mode fracture is the dominant delamination behavior of layered material system,with high stiffness along the bonding interface.However,the shear mode fracture being dominated as the polymer cover plate with low moduli is considered.The occurrence of crack advance is also significantly influenced by the interfacial crack length and applied loading.Therefore,this paper could serve as a guideline of several engineering cases with the assistance of computational mechanics.

Lubrication Mechanism of Micro/Nano-particles on Sialon

The tribological properties of Sialon sliding against AISI52100 steel ball under the lubrication of solid particle additives, as micro-borate particle and nano-PbS particle, were evaluated by a SRV ball-on-disc test rig. The chemical composition of the worn surface was characterized by X-ray photoelectron spectroscopy (XPS). The morphologies of the worn surfaces of Sialon were analyzed by scanning electron microscopy (SEM). The results show that the particles can reduce the friction coefficient of the pairs and the wear volume of Sialon significantly. The wear resistance of micro-borate is superior to that of nano-PbS while the friction-reducing ability of PbS is better than that of borate. According to the XPS and SEM results, the wear resistance of PbS is mainly depended on the tribochemical film mainly composed of PbSO 4, which deposited on the worn surface with good bonding strength. No tribochemical reaction or deposited film was detected or observed on the worn surface of Sialon under the lubrication of borate, indicating that the possible physically deposited film generated from micro particle can also greatly reduce the wear volume of Sialon, though the friction reducing ability of which is inferior to that of nano PbS particle.

Microstructure and Mechanical Properties of Dy-α-sialon/Nano-size SiC Composites

The composite of Dy-α-sialon/10 wt pct nano-size SiC particles has been prepared from precursor powders of Si3N4, AIN, Al2O3, Dy2O3 and nano-size β-SiC. The hardness, toughness and bending strength of the composite at ambient temperature are a little higher than those of Dy-α-sialon.while the bending strength is maintained up to 1000℃ and about 2 times more than that of Dy-α-sialon at the same temperature. The fracture surfaces show that the grain size of the composite is smaller than that of Dy-α-sialon, and both Of them have predominately transgranular mode of fracture. It is believed that the decrease of the bending strength of Dy-α-sialon at elevated temperature is caused by the viscous flow of the grain boundary phase, while the addition of nanosize SiC particles effectively increases the viscosity of the grain boundary phase and therefore prevents the strength loss of Dy-α-sialon/nano-size SiC composites at elevated temperature

Impacts of Micro- and Nano-Plastics on Soil Properties and Plant Production in Agroecosystems: A Mini-Review

Micro- and nano-plastics (MNPs) are tiny plastic particles resulting from plastic product degradation. Soil MNPs have been identified as potential influential factors affecting various soil properties and crop biomass productivity. This mini-review provides a synthesis of recent findings concerning their effects on soil physicochemical properties, microorganisms, organic carbon content, soil nutrients, greenhouse gas emissions, soil fauna, and their impacts on plant ecophysiology, growth, and production. The results indicate that MNPs may markedly impede soil aggregation ability, increase porosity, decrease soil bulk density, enhance water retention capacity, influence soil pH and electrical conductivity, and escalate soil water evaporation. Exposure to MNPs may predominantly induce changes in soil microbial composition, reducing the diversity and complexity of microbial communities and microbial activity while enhancing soil organic carbon stability, influencing soil nutrient dynamics, and stimulating organic carbon decomposition and denitrification processes, leading to elevated soil respiration and methane emissions, and potentially decreasing soil nitrous oxide emission. Additionally, MNPs may adversely affect soil fauna, diminish seed germination rates, promote plant root growth, yet impair plant photosynthetic efficacy and biomass productivity. These findings contribute to a better understanding of the impacts and mechanistic foundations of MNPs. Future research avenues are suggested to further explore the impacts and economic implications.

Research on the Forming Mechanism of Micro/Nano Features during the Cast Molding Process

Cast molding process has provided a reliable, simple and cost-effective way to fabricate micro structures since decades ago. In order to obtain structures with fine, dense and deep nano-size features by cast molding, it is necessary to study the forming mechanism in the process. In this paper, based on major steps of cast molding, filling models of liquid are established and solved; and the forming mechanism of liquid is revealed. Moreover, the scale effect between the liquid and the cavity on the filling velocity of liquid is studied.It is also interesting to find out that the wettability of liquid on the cavity may be changed from wetting to dewetting depends on the pressure difference. Finally, we experimentally verify some of our modeling results on the flowing and filling state of the liquid during the cast molding process.

Microstructures and mechanical properties of nanocrystalline NiTi intermetallics formed by mechanosynthesis

The formulation of nanocrystallinc NiTi shape memory alloys has potential effects in mechanical stimulation and medical im- plantology. The present work elucidates the effect of milling time on the product＇s structural characteristics, chemical composition, and mi- crohardness for NiTi synthesized by mechanical alloying for different milling durations. Increasing the milling duration led to the formation of a nanocrystalline NiTi intermetallic at a higher level. The formation of nanocrystalline materials was directed through cold fusion, fractur- ing, and the development of a steady state, which were influenced by the accumulation of strain energy. In the morphological study, uninter- rupted cold diffusion and fracturing were visualized using transmission electron microscopy. Particle size analysis revealed that the mean particle size was reduced to -93 μm after 20 h of milling. The mechanical strength was enhanced by the formation of a nanocrystalline in- termetallic phase at longer milling time, which was confirmed by the results of Vickers hardness analyses.

Microstructure and mechanical properties analysis of β-tricalcium phosphate/carbon nanotubes scaffold based on rapid prototyping

β-TCP ceramic scaffolds were fabricated with selective laser sintering (SLS) in this work. Carbon nanotubes (CNTs) were mixed with porous β-TCP matrix to enhance the mechanical performance of the bone tissue engineering scaffolds. Scaffold reconstruction and microstructure analysis were fulfilled based on micro-computed tomography (Micro-CT) scanning data. Results show that the strength of scaffold mixed with 0.2% CNTs reaches 0.819 MPa which has been improved by 85.7% compared with that without CNTs. Micro-CT analysis shows that the scaffold has a good interconnectivity, and pore size mainly distributes in the two regions of 60-340 μm and 500-620 μm.