Effects of Nano Calcium Carbonate on Strength and Microstructure of Corundum-based Castables

The castables specimens were prepared using white fused alumina particle and powder, α-Al2O3 micropowder, hydrated alumina, nano calcium carbonate or calcium aluminate cement as starting materials. Effects of nano calcium carbonate addition on phase compositions, strength and microstructure of corundum based castables were studied. The calcium aluminate cement-containing corundum based castables with the same CaO amount was also tested for comparison. The results show that, when temperature is higher than 900 ℃ , the phase compositions of nano CaCO3-containing mixture and the calcium aluminate cement containing mixture are the same, but the forming mechanism, modality and distribution of new phases in the castables are different. With temperature rising, the hydration cement dehydrates and reacts inside cement forming calcium aluminate until the alumina in cement is not enough for the reaction （ternperature is 91 400 ℃ ） , then reacts with the surrounding alumina forming cluster CA6 in the castables. The change process of nano CaCO3 in corundum based enstables is that nano calcium carbonate decomposes to CaO after firing at 800℃ which reacts with Al2O3 forming amorphous calcium aluminate that causes an in-situ bonding. With temperature rising, the formed calcium aluminate reacts with Al2O3 in matrix and wholly forms tabular CA6 at 1 600 ℃ , which distributes uniformly in the castables. The cold and hot strength of the castables with nano calcium carbonate are obviously higher than those of the castables without nano calcium carbonate, especially at 800 -1 000 ℃ due to smaller size and higher dispersion of the nano calcium carbonate and its different reaction mechanism with Al2O3.

Effect of Nano Calcium Carbonate on Properties of Corundum-spinel Castables

Using sintered corundum as aggregate, white fused corundum powder, fused spinel powder, ultra-fine a-A12 0 3, nano calcium carbonate and hydrated alumina as matrix, effects of nano calcium carbonate additions （0. 4%, O. 8%, 1.2%, 1.6% and 2. 0% in mass, the same hereinafter） on modulus of rupture, thermal shock resi.~tanee and slag resistance of corundum -spinel castables after treating at different temperatures were studied. The results show that nano calcium carbonate decomposes at high temperatures and in-situ forms ealci- ant aluminates, which can significantly increase the CMOR and HMOR of the castables after treating at 800 -1 400 ℃ ; adding nano calcium carbonate obviously improves the thermal shock resistance of the castables, and has little influence on the high basicity slag resist- ance, however, significantly decreases the corrosion and penetration resistance to low basicity slag.

A micro-sphere catalyst complex with nano CaCO_3 precursor for hydrogen production used in ReSER process

This paper describes the preparation and evaluation of a micro-sphere catalytic complex for the hydrogen production in a Reactive Sorption Enhanced Reforming （ReSER） process. The catalytic complex made by a spray technique has a dual function containing Ni as a catalytic material and CaO as an adsorption material used in the ReSER process. The attrition characteristics of the catalytic complex are acceptable for the commercial used. The nano GaCO3 material used as a precursor of CaO showed a desirable durability with a CO2 sorption capacity of 0.6 mol CO2/kg after 10 repeating cycles under the carbonation temperature of 600 ℃, a CO2 partial pressure of 0.02 MPa, and a calcination temperature of 750 ℃ in N2 measured by a thermal gravimetric analyzer. The testing of the catalytic complex for ReSER showed a hydrogen yield of over 95 % （v/v） in the laboratory fixed fluidized bed reactor. The catalytic system has an attractive prospect in the ReSER process for hydrogen production, especially in the fluidized mode where reactor and regenerator combined in a cycling process.

Influence of Nano-Materials on Mechanical and Permeation Characteristics of High Strength Concrete

Efforts have been made to evaluate the influences of the addition of nanoparticles on the strength,durability and mineralogical changes of high strength concrete(HSC).Therefore,mixes were prepared for conventional concrete mix(CCM)of M80 grade.Further,various mixes were prepared by replacing cementitious materials initially with 1%Nano-CaCO_(3)(NC),2%NC,3%NC in the CCM,and then 1%NC and Nano-SiO_(2)(NS)NS,2%NC and NS,3%NC and NS(NC and NS were in equal proportion)in the CCM.The developed concretes were then evaluated for mechanical properties,permeation characteristics,and mineralogical studies.From the studies,it is found that the concrete at 2%NCS possesses superior mechanical and superior permeation characteristics of all the mixes.A clear variation in the mineralogical structure with the addition of nanoparticles has been observed.