A novel antibacterial material （L-PET） was prepared by immobilizing ε-polylysine on polyethylene terephthalate （PET） nonwoven fabrics. Surface modifications of the fabric were performed by using a chemical modifi...A novel antibacterial material （L-PET） was prepared by immobilizing ε-polylysine on polyethylene terephthalate （PET） nonwoven fabrics. Surface modifications of the fabric were performed by using a chemical modification procedure where carboxyl groups were prepared on the PET surface, a coupling agent was grafted, and the ε-polylysine was immobilized. Scanning electron microscopy （SEM） was used to analyze the surface morphology of the fabrics, while the toluidine blue method and X-ray photoelectron spectroscopy （XPS） were used to evaluate the grafting densities. The antibacterial activities of the L-PET were investigated by using the shaking-flask method. The electron micrographs showed that the surface of the blank PET and the modified fabrics did not change. The results of XPS analysis confirmed that ε-polylysine was successfully grafted onto the surface of PET. The results of the antibacterial experiments showed that L-PET fabrics had excellent antibacterial activity against Escherichia coli and Staphylococcus aureus, and that L-PET fabrics were stable in storage for at least two years.展开更多
Polyaniline /Polyester( PANI /PET) composite conductive fabric is prepared through in-situ polymerization process using aniline as monomer and PET fabric as matrix,which is treated with alkali deweighting and low temp...Polyaniline /Polyester( PANI /PET) composite conductive fabric is prepared through in-situ polymerization process using aniline as monomer and PET fabric as matrix,which is treated with alkali deweighting and low temperature plasma. The property of PANI /PET composite conductive fabric is studied and characterized,including scanning electron microscope( SEM), infrared spectroscopy, conductivity, wash fastness and mechanical properties. The results show that the optimal polymerization conditions: the molar ratio of ammonium persulfate and aniline is1∶ 1,the concentration of sulfuric acid is 1 mol /L and reaction time is 90 min. Under optimum conditions,the surface resistivity of PANI /PET composite conductive fabric is about 170 Ω. After washed 5 times, the surface resistivity of PANI /PET composite conductive fabric is stable at 1 450 Ω. The breaking strength and breaking elongation of PANI /PET composite conductive fabric decrease compared with PET fabric.展开更多
PET crepe for making silk-like fabric can be obtained by high-twist and heat setting. Recently, new technology, that is hight-twist, heat setting and false-twist has been applied abroad. This paper selects two kinds o...PET crepe for making silk-like fabric can be obtained by high-twist and heat setting. Recently, new technology, that is hight-twist, heat setting and false-twist has been applied abroad. This paper selects two kinds of technology for making crepe, weaving and finishing, then craping effect, lustre feeling, shape feeling, and mechanical properties have been measured and compared for three kinds of crepe fabric(including silk fabric). The results show that the fabric made of PET stretch crepe possesses light soft, better craping effect and bulkness, the machincal properties are close to those of silk crepe.展开更多
基金Funded by the National Major Science & Technology Specific Projects (2009ZX10004-703)
文摘A novel antibacterial material （L-PET） was prepared by immobilizing ε-polylysine on polyethylene terephthalate （PET） nonwoven fabrics. Surface modifications of the fabric were performed by using a chemical modification procedure where carboxyl groups were prepared on the PET surface, a coupling agent was grafted, and the ε-polylysine was immobilized. Scanning electron microscopy （SEM） was used to analyze the surface morphology of the fabrics, while the toluidine blue method and X-ray photoelectron spectroscopy （XPS） were used to evaluate the grafting densities. The antibacterial activities of the L-PET were investigated by using the shaking-flask method. The electron micrographs showed that the surface of the blank PET and the modified fabrics did not change. The results of XPS analysis confirmed that ε-polylysine was successfully grafted onto the surface of PET. The results of the antibacterial experiments showed that L-PET fabrics had excellent antibacterial activity against Escherichia coli and Staphylococcus aureus, and that L-PET fabrics were stable in storage for at least two years.
基金Xi'an Polytechnic University Doctoral Initiating Project,China(No.BS1112)Shaanxi Leading Academic Discipline Project,China(No.[2008]169)+1 种基金Shaanxi Provincial Key Laboratory Scientific Research Project,China(No.12JS044)Natural Science Basic Research Plan in Shaanxi Province of China(No.2012JQ6011)
文摘Polyaniline /Polyester( PANI /PET) composite conductive fabric is prepared through in-situ polymerization process using aniline as monomer and PET fabric as matrix,which is treated with alkali deweighting and low temperature plasma. The property of PANI /PET composite conductive fabric is studied and characterized,including scanning electron microscope( SEM), infrared spectroscopy, conductivity, wash fastness and mechanical properties. The results show that the optimal polymerization conditions: the molar ratio of ammonium persulfate and aniline is1∶ 1,the concentration of sulfuric acid is 1 mol /L and reaction time is 90 min. Under optimum conditions,the surface resistivity of PANI /PET composite conductive fabric is about 170 Ω. After washed 5 times, the surface resistivity of PANI /PET composite conductive fabric is stable at 1 450 Ω. The breaking strength and breaking elongation of PANI /PET composite conductive fabric decrease compared with PET fabric.
文摘PET crepe for making silk-like fabric can be obtained by high-twist and heat setting. Recently, new technology, that is hight-twist, heat setting and false-twist has been applied abroad. This paper selects two kinds of technology for making crepe, weaving and finishing, then craping effect, lustre feeling, shape feeling, and mechanical properties have been measured and compared for three kinds of crepe fabric(including silk fabric). The results show that the fabric made of PET stretch crepe possesses light soft, better craping effect and bulkness, the machincal properties are close to those of silk crepe.