Leaching of low grade zinc oxide ores in Ida^(2-)-H_2O system

Ida2--H2O system（iminodiacetate aqueous solution） was used to leach a low grade zinc oxide ore for Zn extraction.The effects of leaching time,liquid-solid ratio（L/S）,total concentration of Ida2-（[Ida2-]T）,leaching temperature and pH on Zn leaching recovery and the dissolution of impurities such as Ca,Mg,Cu,Ni,Fe,Pb and Cd were investigated.Results show that Ca,Mg and Fe in ores were hardly dissolved in alkalescent iminodiacetate aqueous solution,while valuable metals such as Cu,Ni,Pb and Cd were partly dissolved into leaching liquor with Zn.The recovery of Zn reaches 76.6% when the ores were leached for 4 h at 70 ℃ by 0.9 mol/L iminodiacetate aqueous solution with pH of 8 and L/S of 5：1.

Leaching kinetics of low grade zinc oxide ore in NH_3-NH_4Cl-H_2O system

The leaching kinetics of low grade zinc oxide ore in NH3-NH4Cl-H2O system was studied. The effects of ore particle size, reaction temperature and the sum concentration of ammonium ion and ammonia on the leaching efficiency of zinc were examined. The leaching kinetics of low-grade zinc oxide ore in NH3-NH4Cl-H2O system follows the kinetic law of shrinking-core model. The results show that diffusion through the inert particle pores is the leaching kinetics rate controlling step. The calculated apparent activation energy of the process is about 7.057 kJ/mol. The leaching efficiency of zinc is 92.1% under the conditions of ore particle size of 69 μm, holding at 80 ℃ for 60 min, sum ammonia concentration of 7.5 mol/L, the molar ratio of ammonium to ammonia being 2-1, and the ratio (g/mL) of solid to liquid being 1-10.

Laboratory Study on the Removal of Fluorine from High Fluorine Bearing Zinc Oxide Ore

An ever increasing demand for zinc has resulted in worldwide efforts to exploit complex and lean grade reserves of zinc oxide ore. In this study experiments were done on zinc recovery from high-fluorine bearing zinc oxide ore. First the effect of different variables on fluorine removal was investigated. Optimum experimental conditions occurred when the temperature was 1173 K, roasting time was 90 min and air flow was at a velocity of 5 m/min, the fluorine removal from the samples reached over 93%. The results obtained indicate that fluorine removal is not enhanced by adding diluted sulfuric acid or water as a binder. Second the roasted materials were leached with a diluted sulfuric acid, neutralized, flocculated and filtrated. The which satisfies the requirement of fluorine residual fluorine content in the leached content in the leached solutions for the solutions was less than 38 mg/L production of electrolytic zinc.

Study on the pre-treatment of oxidized zinc ore prior to flotation

The pre-treatment of zinc oxide bearing ores with high slime content is important to ensure that resources are utilized optimally. This paper reports an improved process using hydrocyclone de-sliming, dispersion reagents, and magnetic removal of iron minerals for the pre-treatment of zinc oxide ore with a high slime and iron content, and the benefits compared to traditional technologies are shown. In addition, this paper investigates the damage related to fine slime and iron during zinc oxide flotation, the necessity of using hydrocyclone de-sliming together with dispersion reagents to alleviate the influence of slime, and interactions among hydrocyclone de-sliming, reagent dispersion, and magnetic iron removal. Results show that under optimized operating conditions the entire beneficiation technology results in a flotation concentrate with a Zn grade of 34.66% and a recovery of 73.41%.

Zinc extraction from zinc oxidized ore using(NH4)2SO4 roasting−leaching process

An improved method of(NH4)2SO4 roasting followed by water leaching to utilize zinc oxidized ores was studied.The operating parameters were obtained by investigating the effects of the molar ratio of(NH4)2SO4 to zinc,roasting temperature,and holding time on zinc extraction.The roasting process followed the chemical reaction control mechanism with the apparent activation energy value of 41.74 kJ·mol^−1.The transformation of mineral phases in roasting was identified by X-ray diffraction analysis combined with thermogravimetry–differential thermal analysis curves.The water leaching conditions,including the leaching temperature,leaching time,stirring velocity,and liquid-to-solid ratio,were discussed,and the leaching kinetics was studied.The reaction rate was obtained under outer diffusion without product layer control;the values of the apparent activation energy for two stages were 4.12 and 8.19 kJ·mol^−1.The maximum zinc extraction ratio reached 96%while the efficiency of iron extraction was approximately 32%under appropriate conditions.This work offers an effective method for the comprehensive use of zinc oxidized ores.