The effects of cold-rolling reduction,annealing temperature,and time on recrystallization behavior and kinetics of cold-rolled Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were investigated using the Vickers hardness test,scanning ...The effects of cold-rolling reduction,annealing temperature,and time on recrystallization behavior and kinetics of cold-rolled Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were investigated using the Vickers hardness test,scanning electronic microscopy(SEM),transmission electron microscopy(TEM)and electron backscatter diffractometry(EBSD).The results show that the rate of the recrystallization increased with increasing annealing temperature and rolling reduction.Recrystallized grains nucleated preferentially at sites with high density dislocation and deformation stored energy and then grew into integral grains.Recrystallization texture changed from-1010-//RD to-1120-//RD.The grain orientation changed from random orientation to the orientation with the maximum misorientation around 30°.Recrystallization kinetics and maps were constructed based on the Johnson-Mehl-Avrami-Kolmogorov(JMAK)equation to derive parameters sensitive to the microstructure.The activation energies for recrystallization of 30%,50%and 70%cold-rolling reductions were determined to be 240,249 and 180 kJ/mol,respectively.展开更多
基金Project(STRFML-2013)supported by the Science and Technology on Reactor Fuel and Materials Laboratory,ChinaProject(2014BAC03B05)supported by the Key Projects of the National Science and Technology of China
文摘The effects of cold-rolling reduction,annealing temperature,and time on recrystallization behavior and kinetics of cold-rolled Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy were investigated using the Vickers hardness test,scanning electronic microscopy(SEM),transmission electron microscopy(TEM)and electron backscatter diffractometry(EBSD).The results show that the rate of the recrystallization increased with increasing annealing temperature and rolling reduction.Recrystallized grains nucleated preferentially at sites with high density dislocation and deformation stored energy and then grew into integral grains.Recrystallization texture changed from-1010-//RD to-1120-//RD.The grain orientation changed from random orientation to the orientation with the maximum misorientation around 30°.Recrystallization kinetics and maps were constructed based on the Johnson-Mehl-Avrami-Kolmogorov(JMAK)equation to derive parameters sensitive to the microstructure.The activation energies for recrystallization of 30%,50%and 70%cold-rolling reductions were determined to be 240,249 and 180 kJ/mol,respectively.