Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top ...Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top surface of the joint was characterized by scanning electron microscopy and transmission electron microscopy.The corrosion behaviors of different regions in the joint were investigated by an electrochemistry method and an alternating salt spray exposure.The corrosion was mainly dependent on the nature of precipitates in each region of the joint.The shoulder affected zone had the worst corrosion resistance as a result of the re-dissolved ofθ′(Al2Cu),T1(Al2CuLi)andδ′(Al3Li)phases,the formation of intergranular precipitates and precipitate-free zones.However,the thermomechanically affected zone had a slightly improved corrosion resistance because it had no intergranular precipitates.The heat affected zone and base metal had the best corrosion resistance.展开更多
基金Beijing Natural Science Foundation (Grant No. 3194048)China Friction Stir Welding Center and to Beijing Key Laboratory of Pipeline Critical Technology and Equipment for Deepwater Oil & Gas Development (Grant No. BIPT2018006) for the financial support
文摘Friction stir welding was used to join two AA2060-T8 plates,and then the effect of precipitate evolution on microstructure and corrosion behavior of the joint was investigated.The evolution of precipitates on the top surface of the joint was characterized by scanning electron microscopy and transmission electron microscopy.The corrosion behaviors of different regions in the joint were investigated by an electrochemistry method and an alternating salt spray exposure.The corrosion was mainly dependent on the nature of precipitates in each region of the joint.The shoulder affected zone had the worst corrosion resistance as a result of the re-dissolved ofθ′(Al2Cu),T1(Al2CuLi)andδ′(Al3Li)phases,the formation of intergranular precipitates and precipitate-free zones.However,the thermomechanically affected zone had a slightly improved corrosion resistance because it had no intergranular precipitates.The heat affected zone and base metal had the best corrosion resistance.