Interplay between temperature-dependent strengthening mechanisms and mechanical stability in high-performance austenitic stainless steels

The effects of deformation temperature on the transformation-induced plasticity(TRIP)-aided 304L,twinning-induced plasti-city(TWIP)-assisted 316L,and highly alloyed stable 904L austenitic stainless steels were compared for the first time to tune the mechan-ical properties,strengthening mechanisms,and strength-ductility synergy.For this purpose,the scanning electron microscopy(SEM),electron backscattered diffraction(EBSD),X-ray diffraction(XRD),tensile testing,work-hardening analysis,and thermodynamics calcu-lations were used.The induced plasticity effects led to a high temperature-dependency of work-hardening behavior in the 304L and 316L stainless steels.As the deformation temperature increased,the metastable 304L stainless steel showed the sequence of TRIP,TWIP,and weakening of the induced plasticity mechanism;while the disappearance of the TWIP effect in the 316L stainless steel was also observed.However,the solid-solution strengthening in the 904L superaustenitic stainless steel maintained the tensile properties over a wide temper-ature range,surpassing the performance of 304L and 316L stainless steels.In this regard,the dependency of the total elongation on the de-formation temperature was less pronounced for the 904L alloy due to the absence of additional plasticity mechanisms.These results re-vealed the importance of solid-solution strengthening and the associated high friction stress for superior mechanical behavior over a wide temperature range.

Temperature-jump tensile tests to induce optimized TRIP/TWIP effect in a metastable austenitic stainless steel

In the present work,plastic deformation mechanisms were initially tailored by adjusting the deformation temperature in the range of 0 to 200℃ in AISI 304L austenitic stainless steel,aiming to optimize the strength-ductility synergy.It was shown that the combined twinning-induced plasticity(TWIP)/transformation-induced plasticity(TRIP)effects and a wider strain range for the TRIP effect up to higher strains by adjusting the deformation temperature are good strategies to improve the strength-ductility synergy of this metastable stainless steel.In this regard,by consideration of the observed temperature-dependency of plastic deformation,the controlled sequence of TWIP and TRIP effects for archiving superior strength-ductility trade-off was intended by the pre-designed temperature jump tensile tests.Accordingly,the optimum tensile toughness of 846 MJ/m^(3) and total elongation to 133% were obtained by this strategy via exploiting the advantages of the TWIP effect at 100℃ and the TRIP effect at 25℃ at the later stages of the straining.Consequently,a deformation-temperature-transformation(DTT)diagram was developed for this metastable alloy.Moreover,based on work-hardening analysis,it was found that the main phenomenon constraining further improvement in the ductility and strengthening was the yielding of the deformation-induced α′-martensite.

Weldable high-strength steels: Challenges and engineering applications

68 IIW Annual Assembly&International; Conference of the International Institute of Welding,2-3 July 2015,Helsinki,Finland Portevin LectureHigh-strength steels are finding ever-wider applications as awareness of the potential benefits spread and the knowledge required by designers increases.According to the different processing routes,the YS levels of high-strength steels are commercially available as follows:

Effect of cooling rate and composition on microstructure and mechanical properties of ultrahigh-strength steels

The influence of cooling rate on the microstructure and mechanical properties of two new ultrahigh-strength steels(UHSSs)with different levels of C,Cr and Ni has been evaluated for the as-cooled and untempered condition.One UHSS had higher contents of C and Cr,while the other one had a higher Ni content.On the basis of dilatation curves,microstructures,macrohardness and microhardness,continuous cooling transformation diagrams were constructed as a guide to heat treatment possibilities.Cooling rates(CRs)of 60,1 and 0.01°C/s were selected for more detailed investigations.Microstructural characterization was made by laser scanning confocal microscopy,field emission scanning electron microscopy combined with electron backscatter diffraction,electron probe microanalysis and X-ray diffraction.Mechanical properties were characterized using macrohardness,tensile and Charpy V-notch impact tests.UHSS with the higher C and Cr contents showed lower transformation temperatures and slower bainite formation kinetics than that with the higher Ni content.Higher cooling rates led to lower volume fractions and carbon contents of retained austenite together with finer prior austenite grain size,as well as effective final grain size and lath size.These changes were accompanied by higher yield and tensile strengths.The best combinations of strength and toughness were obtained with martensitic microstructures and by avoiding the formation of granular bainite accompanied by proeutectoid carbides at low CR.For the cooling rates studied,UHSS with the higher C and Cr contents showed the higher hardness and strength but at the cost of toughness.

Correlation Between Magnetic Properties and Allotropic Phase Transition of Fe–Co–V Alloy

In this study, the allotropic phase transition and its effect on the magnetic behavior of Fe Co–7 wt%V alloy were investigated. It was found that c phase is observed in the microstructure in the as-cast condition, and it diminishes after severe cold rolling（90% reduction）. After annealing at temperatures higher than 500 up to 750 ℃, the c phase is observed in the structure, again. But, this phase is disappeared by annealing at temperatures above 750 ℃ due to the formation of vanadium-rich precipitates. Thermocalc software was used in order to elucidate the influence of vanadium percent on the stability of c phase in Fe–Co alloys. Also, magnetic studies showed that the saturation induction is reduced by annealing at temperatures from 500 up to 750 ℃, which is related to the formation of residual non-magnetic γ phase.