High performance aluminosilicate based cementitious materials were produced using calcined gangue as one of the major raw materials. The gangue was calcined at 500℃. The main constituent was calcined gangue, fly ash ...High performance aluminosilicate based cementitious materials were produced using calcined gangue as one of the major raw materials. The gangue was calcined at 500℃. The main constituent was calcined gangue, fly ash and slag, while alkali-silicate solutions were used as the diagenetic agent. The structure of gangue-containing aluminosilicate based cementitious materials was studied by the methods of IR, NMR and SEM. The results show that the mechanical properties are affected by the mass ratio between the gangue, slag and fly ash, the kind of activator and additional salt. For 28-day curing time, the compressive strength of the sample with a mass proportion of 2：1：1 （gangue： slag： fly ash） is 58.9 MPa, while the compressive strength of the sample containing 80wt% gangue can still be up to 52.3 MPa. The larger K^＋ favors the formation of large silicate oligomers with which AI（OH）4- prefers to bind. Therefore, in Na-K compounding activator solutions more oligomers exist which result in a stronger compressive strength of aluminosilicate-based cementitious materials than in the case of Na-containing activator. The reasons for this were found through IR and NMR analysis. Glauber＇s salt reduces the 3-day compressive strength of the paste, but increases its 7-day and 28-day compressive strengths.展开更多
To study the dissolution mechanism of gangue, dissolution characteristics of the gangue samples calcined at different temperatures in alkaline solutions and alkali metal silicate solutions with respect to Si and Al io...To study the dissolution mechanism of gangue, dissolution characteristics of the gangue samples calcined at different temperatures in alkaline solutions and alkali metal silicate solutions with respect to Si and Al ions were analyzed by identical coupled plasma optical emission spectroscopy （ICP）. The results show that the extent of dissolution of Al and Si varies with calcination temperature. It shows that the samples have a higher degree of dissolution in NaOH than in KOH medium. Si and Al appear to have synchro-dissolution behavior in alkaline solution, which means that Si and Al could dissolve from the mineral surface in certain linked forms. The result that a higher degree of dissolution exists in sodium silicate solution and a lower degree of dissolution exists in sodium-potassium silicate solution of Al is proved by the 29Si NMR spectra and the mean connectivity degree of these alkali metal silicate solutions.展开更多
基金This work was supported by the National High-Tech Research and Development Program of China (No.2003AA332020), the Nation-al Natural Science Foundation of China (No.50474002) and the Key Project of the Ministry of Education of China (No.104231).
文摘High performance aluminosilicate based cementitious materials were produced using calcined gangue as one of the major raw materials. The gangue was calcined at 500℃. The main constituent was calcined gangue, fly ash and slag, while alkali-silicate solutions were used as the diagenetic agent. The structure of gangue-containing aluminosilicate based cementitious materials was studied by the methods of IR, NMR and SEM. The results show that the mechanical properties are affected by the mass ratio between the gangue, slag and fly ash, the kind of activator and additional salt. For 28-day curing time, the compressive strength of the sample with a mass proportion of 2：1：1 （gangue： slag： fly ash） is 58.9 MPa, while the compressive strength of the sample containing 80wt% gangue can still be up to 52.3 MPa. The larger K^＋ favors the formation of large silicate oligomers with which AI（OH）4- prefers to bind. Therefore, in Na-K compounding activator solutions more oligomers exist which result in a stronger compressive strength of aluminosilicate-based cementitious materials than in the case of Na-containing activator. The reasons for this were found through IR and NMR analysis. Glauber＇s salt reduces the 3-day compressive strength of the paste, but increases its 7-day and 28-day compressive strengths.
基金This work was financially supported by the National Natural Science Foundation of China (No.50474002) and the Key Project of theMinistry of Education of China (No.104231)
文摘To study the dissolution mechanism of gangue, dissolution characteristics of the gangue samples calcined at different temperatures in alkaline solutions and alkali metal silicate solutions with respect to Si and Al ions were analyzed by identical coupled plasma optical emission spectroscopy （ICP）. The results show that the extent of dissolution of Al and Si varies with calcination temperature. It shows that the samples have a higher degree of dissolution in NaOH than in KOH medium. Si and Al appear to have synchro-dissolution behavior in alkaline solution, which means that Si and Al could dissolve from the mineral surface in certain linked forms. The result that a higher degree of dissolution exists in sodium silicate solution and a lower degree of dissolution exists in sodium-potassium silicate solution of Al is proved by the 29Si NMR spectra and the mean connectivity degree of these alkali metal silicate solutions.