Interfacial reaction between AZ91D magnesium alloy melt and mild steel under high temperature

The metallurgical quality control of magnesium(Mg)and Mg alloys in melting process is required to ensure a satisfied mechanical and corrosion performance,while the typical used steel crucible introduces impurities and interfacial interaction during melting process.Therefore,a systematic study about impurities diffusion and interfacial interaction between molten Mg and steel is necessary.In the present study,the interfacial reaction between molten AZ91D Mg alloy and mild steel during melting process was investigated with the melting temperatures of 700℃,750℃ and 800℃.The results show that Al(Fe,Mn)intermetallic layer is the intermetallic primarily formed at the interfaces of AZ91D melt and mild steel.Meanwhile,Al_(8)(Mn,Fe)5is indexed between Al(Fe,Mn)and AZ91D.AlFe_(3)C appears between the mild steel and Al(Fe,Mn)at 700℃ and 750℃,but absent at 800℃ due to the increased solubility of carbon in Mg matrix.It is found that the growth of the intermetallic layer is controlled by diffusion mechanism,and Al and Mn are the dominant diffusing species in the whole interfacial reaction process.By measuring the thickness of different layers,the growth constant was calculated.It increases from 1.89(±0.03)×10^(-12)m^(2)·s^(-1)at 700℃ to 3.05(±0.05)×10^(-12)m^(2)·s^(-1)at 750℃,and 5.18(±0.05)×10^(-12)m^(2)·s^(-1)at 800℃.Meanwhile,the content of Fe is linearly increased in AZ91D with the increase of holding time at 700℃ and 750℃,while it shows a significantly increment after holding for 8 h at 800℃,indicating holding temperature is more crucial to determine the Fe content of AZ91D than holding time.

Tribological behaviors of graphene oxide partly substituted with nano-SiO_(2) as lubricant additives in water for magnesium alloy/steel interfaces

Although graphene oxide(GO)has emerged as an excellent lubricant additive in water,there remain great challenges in their practical application due to high production costs.By taking into account the low cost and also its excellent tribological properties,it is likely that nano-SiO_(2)can be used as a lubricant additive to partially replace GO.Hence,this paper aims to explore the tribological properties of nano-SiO_(2)incorporated in GO nanofluids for partial GO replacement by investigating the friction coefficient and wear volume of the prepared SiO_(2)/GO hybrid nanofluids for magnesium alloy/steel sliding pairs.The experiments reveal that the SiO_(2)/GO hybrids retain low friction coefficients as compared to individual GO or SiO_(2)at all test conditions in this study.However,as for the bearing capacity test,all samples can provide a low wear volume under the loads of 1 and 3 N.With the increase of the normal load,there is considerable differences in the anti-wear behavior.Compared with that of individual GO nanofluids,the wear volume of the GO/SiO_(2)(mass ratio of 0.3:0.2)hybrid nanofluids was reduced by50.5%at 5 N and by 49.2%at 8 N.Furthermore,the wear volume of the GO/SiO_(2)(mass ratio of 0.3:0.2)hybrid nanofluids was reduced by46.3%under the rigorous conditions,as compared to individual GO nanofluids.The findings provide new insights into developing carbon nanomaterial-based hybrid nanofluids for magnesium alloy formation.