Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monola...Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.展开更多
Block copolymers with different backbone compositions have been prepared by the condensation of dimethylamino terminated poly（dimethylsiloxane） （PDMS） and hydroquinone terminated poly（phthalazinone ether nitrile...Block copolymers with different backbone compositions have been prepared by the condensation of dimethylamino terminated poly（dimethylsiloxane） （PDMS） and hydroquinone terminated poly（phthalazinone ether nitrile） （PPEN） in the presence of chlorobenzcne/N-methyl pyrrolidone （NMP） as solvents. The products were characterized by FTIR, ^1H NMR and gel permeation chromatography. Differential scanning calorimetry analysis indicated that the block copolymers showed separated microphase.展开更多
High molecular weight copoly(ether ketone)s (PEK) based on 4-(4-hydroxyphenyl)-1- phthalazinone (DHPZ)/4,4-thiobisphenol (TBP)/4,4-diflourodiphenylketone (DFK) were prepared by nucleophilic substitution polycondensati...High molecular weight copoly(ether ketone)s (PEK) based on 4-(4-hydroxyphenyl)-1- phthalazinone (DHPZ)/4,4-thiobisphenol (TBP)/4,4-diflourodiphenylketone (DFK) were prepared by nucleophilic substitution polycondensation. The copolymers were characterized by FT-IR and 1H-NMR. Thermal properties and solubility of copolymers were studied.展开更多
基金This project was financially supported by National High Technology and Development Program of China(863 Program)(No.2003AA33G030)
文摘Trimethoxysilyl-functionalized PPEK（PKGS） films had been designed to serve as wear resistant coatings for silicon surfaces. These surface films were formed by a dip-coating technique applied to self-assembled monolayers（SAMs）.The formation and wetting behavior of PKGS films were characterized by means of contact angle measurement.The friction coefficient of the film prepared is very low（about 0.1）,and the anti-wear behavior is good,with a lack of failure after sliding over 1800 s.
文摘Block copolymers with different backbone compositions have been prepared by the condensation of dimethylamino terminated poly（dimethylsiloxane） （PDMS） and hydroquinone terminated poly（phthalazinone ether nitrile） （PPEN） in the presence of chlorobenzcne/N-methyl pyrrolidone （NMP） as solvents. The products were characterized by FTIR, ^1H NMR and gel permeation chromatography. Differential scanning calorimetry analysis indicated that the block copolymers showed separated microphase.
基金This work was supported by the National Natural Science Foundation of China (59473901).
文摘High molecular weight copoly(ether ketone)s (PEK) based on 4-(4-hydroxyphenyl)-1- phthalazinone (DHPZ)/4,4-thiobisphenol (TBP)/4,4-diflourodiphenylketone (DFK) were prepared by nucleophilic substitution polycondensation. The copolymers were characterized by FT-IR and 1H-NMR. Thermal properties and solubility of copolymers were studied.