Silicon-substituted hydroxyapatite (Ca10(PO4)6-x(SiO4)x(OH)2-x, Si-HA) composite coatings on a bioactive titanium substrate were prepared by electrophoretic deposition technique with the addition of triethanolamine (T...Silicon-substituted hydroxyapatite (Ca10(PO4)6-x(SiO4)x(OH)2-x, Si-HA) composite coatings on a bioactive titanium substrate were prepared by electrophoretic deposition technique with the addition of triethanolamine (TEA) to enhance the ionization degree of Si-HA suspension. The surface structure was characterized by XRD, SEM, XRF, EDS and FTIR. The bond strength of the coating was investigated. The results show that the depositing thickness and the images of Si-HA coating can be changed with the variation of deposition time. The XRD spectra of Ti/Si-HA coatings show the characteristic diffraction peaks of HA, and the incorporation of silicon changes the lattice parameter of the crystal. The FTIR spectra shows that the most notable effect of silicon substitution is the decrease of intensities of —OH and PO43- groups with the silicon contents increasing. XRD and EDS element analyses present that the content of silicon in the coating increases with increasing silicon concentration in the suspension. The bioactive TiO2 coating formed may improve the bond strength of the coatings. The interaction of Ti/Si-HA coating with BSA is much greater than that of Ti/HA coating, suggesting that the incorporation of silicon in HA is significant to improve the bioactive performance of HA.展开更多
基金Project(39931702) supported by the National Natural Science Foundation of ChinaProject(041223) supported by the Natural Science Foundation of Hebei Province, China
文摘Silicon-substituted hydroxyapatite (Ca10(PO4)6-x(SiO4)x(OH)2-x, Si-HA) composite coatings on a bioactive titanium substrate were prepared by electrophoretic deposition technique with the addition of triethanolamine (TEA) to enhance the ionization degree of Si-HA suspension. The surface structure was characterized by XRD, SEM, XRF, EDS and FTIR. The bond strength of the coating was investigated. The results show that the depositing thickness and the images of Si-HA coating can be changed with the variation of deposition time. The XRD spectra of Ti/Si-HA coatings show the characteristic diffraction peaks of HA, and the incorporation of silicon changes the lattice parameter of the crystal. The FTIR spectra shows that the most notable effect of silicon substitution is the decrease of intensities of —OH and PO43- groups with the silicon contents increasing. XRD and EDS element analyses present that the content of silicon in the coating increases with increasing silicon concentration in the suspension. The bioactive TiO2 coating formed may improve the bond strength of the coatings. The interaction of Ti/Si-HA coating with BSA is much greater than that of Ti/HA coating, suggesting that the incorporation of silicon in HA is significant to improve the bioactive performance of HA.