[ZnO(0.5 nm)/Co(0.6 nm)]60 multilayers were fabricated by magnetron sputtering. The magnetic, transport and optical properties were studied. The ferromagnetic state at low temperature was demonstrated. Most of the gra...[ZnO(0.5 nm)/Co(0.6 nm)]60 multilayers were fabricated by magnetron sputtering. The magnetic, transport and optical properties were studied. The ferromagnetic state at low temperature was demonstrated. Most of the grains in the samples will be unblocked when temperature is below 50K. The measured magneto-resistance at 4.8K is higher than 30%. This value is larger than any other reported data. The transport mechanism may come down to a combination of tunnelling conduction with the second-order hopping. Some small peaks on transmittance curves were found, the matter is still open.展开更多
We investigate the variations from as-deposited Zn1-x： Cox O magnetic semiconductors to the post-annealed Co- ZnCoO granular composite. The as-deposited Zn1-x Cox 0 magnetic semiconductor deposited under thermal none...We investigate the variations from as-deposited Zn1-x： Cox O magnetic semiconductors to the post-annealed Co- ZnCoO granular composite. The as-deposited Zn1-x Cox 0 magnetic semiconductor deposited under thermal nonequilibrium conditions is composed of Zn1-x. Cox O nanograins of high Co concentration. The room-temperature ferromagnetism with high magnetization and large negative magnetoresistance are found in the as-deposited samples. By annealing, the samples become of granular composite consisting of the Co metal grains and the remanent Zn1-x CoxO matrix. Although the magnetization is enhanced after annealing, the spin-dependent negative magnetoresistance disappears at room temperature. The magnetoresistance observed in the annealed samples in the high field region has no relation with the ferromagnetism, which in turn indicates that the roomtemperature ferromagnetism and large negative magnetoresistance observed in the as-deposited are the intrinsic properties of the Zn1-x Cox O magnetic semiconductor.展开更多
The search for two-dimensional(2D)nodal ring semimetallic materials is a current research hotspot in spintronics,and designing a 2D nodal ring(NR)material with high Curie temperature(TC)and strong robustness to spin-o...The search for two-dimensional(2D)nodal ring semimetallic materials is a current research hotspot in spintronics,and designing a 2D nodal ring(NR)material with high Curie temperature(TC)and strong robustness to spin-orbit coupling(SOC)is an even greater challenge.Here,based on the first-principles calculations and symmetry analysis,we predict that 2D Mn_(2)N_(3)is a nodal ring semimetal(NRSM)with three energy bands near the Fermi energy level consisting of electrons in the same spin channel.An electron-like energy band and two hole-like energy bands near the Fermi plane cross to form two NRs centered at the pointΓ.Symmetry analysis shows that the spin-polarized NR semimetal is robust to SOC due to the conservation of horizontal mirror symmetry.Monte-Carlo simulations further demonstrate that the TCof the 2D Mn_(2)N_(3)reaches 530 K,well above the room temperature.Notably,the 2D Mn_(2)N_(3)remains an NRSM on h-BN substrate.Our results not only reveal a general framework for designing 2D NR materials,but also promote further research in the direction of multifunctional quantum devices for spintronics.展开更多
文摘[ZnO(0.5 nm)/Co(0.6 nm)]60 multilayers were fabricated by magnetron sputtering. The magnetic, transport and optical properties were studied. The ferromagnetic state at low temperature was demonstrated. Most of the grains in the samples will be unblocked when temperature is below 50K. The measured magneto-resistance at 4.8K is higher than 30%. This value is larger than any other reported data. The transport mechanism may come down to a combination of tunnelling conduction with the second-order hopping. Some small peaks on transmittance curves were found, the matter is still open.
基金Supported by the National Basic Research Programme of China under Grant No 2001CB610603, the National Natural Science Foundation of China under Grant Nos 50402019 10234010 and 50572053, NCET040634 and the Doctoral Fund of Jinan University （B0404）.
文摘We investigate the variations from as-deposited Zn1-x： Cox O magnetic semiconductors to the post-annealed Co- ZnCoO granular composite. The as-deposited Zn1-x Cox 0 magnetic semiconductor deposited under thermal nonequilibrium conditions is composed of Zn1-x. Cox O nanograins of high Co concentration. The room-temperature ferromagnetism with high magnetization and large negative magnetoresistance are found in the as-deposited samples. By annealing, the samples become of granular composite consisting of the Co metal grains and the remanent Zn1-x CoxO matrix. Although the magnetization is enhanced after annealing, the spin-dependent negative magnetoresistance disappears at room temperature. The magnetoresistance observed in the annealed samples in the high field region has no relation with the ferromagnetism, which in turn indicates that the roomtemperature ferromagnetism and large negative magnetoresistance observed in the as-deposited are the intrinsic properties of the Zn1-x Cox O magnetic semiconductor.
基金Project supported by Taishan Scholar Program of Shandong Province,China(Grant No.ts20190939)Independent Cultivation Program of Innovation Team of Jinan City(Grant No.2021GXRC043)National Natural Science Foundation of China(Grant Nos.52173283 and 62071200)
文摘The search for two-dimensional(2D)nodal ring semimetallic materials is a current research hotspot in spintronics,and designing a 2D nodal ring(NR)material with high Curie temperature(TC)and strong robustness to spin-orbit coupling(SOC)is an even greater challenge.Here,based on the first-principles calculations and symmetry analysis,we predict that 2D Mn_(2)N_(3)is a nodal ring semimetal(NRSM)with three energy bands near the Fermi energy level consisting of electrons in the same spin channel.An electron-like energy band and two hole-like energy bands near the Fermi plane cross to form two NRs centered at the pointΓ.Symmetry analysis shows that the spin-polarized NR semimetal is robust to SOC due to the conservation of horizontal mirror symmetry.Monte-Carlo simulations further demonstrate that the TCof the 2D Mn_(2)N_(3)reaches 530 K,well above the room temperature.Notably,the 2D Mn_(2)N_(3)remains an NRSM on h-BN substrate.Our results not only reveal a general framework for designing 2D NR materials,but also promote further research in the direction of multifunctional quantum devices for spintronics.