Progress of electroplating and electroless plating on magnesium alloy

The current research processes of electroplating and electroless Ni-P alloy plating on magnesium alloys were reviewed. Theoretically,the reason for difficulties in electroplating and electroless plating on magnesium alloys was given.The zinc immersion, copper immersion,direct electroless Ni-P alloy plating and electroplating and electroless plating on magnesium alloys prepared by chemical conversion coating were presented in detail.Especially,the research development of magnesium alloy AZ91 and AZ31 was discussed briefly.Based on the analysis,the existing problems and future research directions were then given.

几种超级不锈钢在模拟低温多效海水淡化环境中的点蚀行为研究

在温度分别为20,40和70℃的2倍浓缩海水模拟溶液中,利用循环伏安曲线测试和SEM观察研究,对316不锈钢和超级不锈钢904L、254sMo以及2507的极化行为和表面点蚀形貌进行了研究。结果表明,在该环境中,升高温度可降低316、904L、254sMo和2507等4种不锈钢表面钝化膜的稳定性并提高其点蚀敏感性。在不同温度中,316不锈钢表面均发生严重点蚀损伤,而254sMo和2507不锈钢表面均无明显点蚀迹象。在低温时,904L不锈钢钝化膜击穿电位较高,点蚀坑尺寸较小,点蚀倾向较低;在高温时,其点蚀电位显著降低,点蚀坑尺寸明显增大,点蚀倾向较大。

AH32长尺试样在模拟海洋潮差区腐蚀行为的电偶电流研究

利用自制的模拟实验装置模拟实海潮差,监测了在模拟潮差区内AH32长尺试样的电偶电流和电极电位变化情况。结果表明,由于供氧差异形成的宏电池作用,AH32长尺试样在潮差区和全浸区内的电极电位分布不均衡,引发了内部的电偶电流,其实质为阴、阳极反应产生的净电流。在潮差区内,AH32长尺试样不同部位的电偶电流随潮位运动发生周期性变化;当潮位最高时,所有部位的电偶电流均处于极大值状态,且中间潮位部位的电偶电流最大,由此所引起的阳极电流也最大。根据电偶电流的变化计算出的干燥、润湿和浸没状态的时间分布表明,AH32长尺试样在潮位区不同部位的腐蚀量取决于润湿和浸没时间在该部位的分配。各部位在浸没态时存在宏电池作用,产生电偶电流。而在润湿态下,由于薄液膜的溶液电阻很大,导致宏电池驱动电位几乎等于在薄液膜上的电压降,因此宏电池作用极弱,且不产生电偶电流。润湿时间和润湿电量的关系显示,潮位运动中AH32长尺试样的最大润湿时间出现在平均中潮位以上的部位,表明因润湿引起的该部位的腐蚀失重最大。结合由浸没态引起的平均中潮位腐蚀失重最大的结果可以确定,在潮水涨落过程中AH32长尺试样的最大腐蚀失重量应出现在平均中潮位偏上的部位,这与腐蚀速率的测量结果一致。