To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containin...To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.展开更多
基金financial supports from the National Natural Science Foundation of China (Nos.51901068,51979099)the Key Research and Development Project of Jiangsu Province,China (No.BE2021027)+1 种基金the Opening Project of Jiangsu Key Laboratory of Advanced Structural Materials and Application Technology,China (No.ASMA202102)the Research Fund from Key Laboratory for Light-weight Materials of Jiangsu Province,China。
文摘To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.