高速钢表面类金刚石(diamond-like carbon,DLC)薄膜的沉积效率和膜-基结合力影响其在切削刀具领域的应用。基于空心阴极原理,利用等离子体增强化学气相沉积(plasma-enhanced chemical vapor deposition,PECVD)的方法,在体积比为1∶3的CH...高速钢表面类金刚石(diamond-like carbon,DLC)薄膜的沉积效率和膜-基结合力影响其在切削刀具领域的应用。基于空心阴极原理,利用等离子体增强化学气相沉积(plasma-enhanced chemical vapor deposition,PECVD)的方法,在体积比为1∶3的CH_(4)和C_(2)H_(2)的混合气体中加入N_(2)在高速钢表面制备类金刚石薄膜,研究了N_(2)体积分数对DLC薄膜结合力和耐磨性的影响。结果表明:掺氮可提高DLC薄膜的沉积效率,改善膜结构。随着N_(2)体积分数的增加,DLC薄膜中sp^(3)键含量和摩擦因数均先增大后减小。掺10%体积分数N_(2)的DLC薄膜厚度达1543 nm,膜-基结合力等级从HF4提高到HF2,摩擦因数降至0.139,耐磨性提高。展开更多
The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters ...The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.展开更多
基金supported by the National Key R&D Program of China(No.2019YFE0123900)the National Natural Sci-ence Foundation of China(Grant No.51974069)the Special Fund for Basic Scientific Research of Central Colleges(N2125035).
文摘The mechanical and frictional properties of ta-C coatings deposited on the substrate surface affect applications in the field of cutting tools and wear-resistant components.In this paper,the effect of bias parameters on the performance of ta-C coatings was investigated based on high power impulse magnetron sputtering(HiPIMS)technology.The results show that bias voltage has a significant effect on the deposition rate,structure,and wear resistance of the coating.In the range of bias voltage−50 V to−200 V,the ta-C coating performance was the best under bias voltage−150 V.The thickness reached 530.4 nm,the hardness value reached 35.996 GPa,and the bonding force in-creased to 14.2 N.The maximum sp3 bond content was 59.53% at this condition.