本文采用水热法制备了γ-Bi_2Sn_2O_7并研究了其在可见光区的光电响应。Bi_2Sn_2O_7的晶体结构和光电响应特性分别用X射线衍射和表面光电压谱进行表征。研究结果表明,合成的Bi_2Sn_2O_7呈现γ相立方结构,通过吸收光谱估算光学带隙为2.67...本文采用水热法制备了γ-Bi_2Sn_2O_7并研究了其在可见光区的光电响应。Bi_2Sn_2O_7的晶体结构和光电响应特性分别用X射线衍射和表面光电压谱进行表征。研究结果表明,合成的Bi_2Sn_2O_7呈现γ相立方结构,通过吸收光谱估算光学带隙为2.67 e V,比α-Bi_2O_3(2.85 e V)的光学带隙小。Bi_2Sn_2O_7的光电响应相对于α-Bi_2O_3在可见光区展现出一定的优势,同时对外加电压有很强的响应。展开更多
Low thermal expansion composites are difficult to obtain by using Al with larger positive thermal expansion coefficient（TEC） and the materials with smaller negative TECs. In this investigation, Y2Mo3O12 with larger ...Low thermal expansion composites are difficult to obtain by using Al with larger positive thermal expansion coefficient（TEC） and the materials with smaller negative TECs. In this investigation, Y2Mo3O12 with larger negative TEC is used to combine with Al to obtain a low thermal expansion composite with high conductivity. The TEC of Al is reduced by 19%for a ratio Al：Y2Mo3O12 of 0.3118. When the mass ratio of Al：Y2Mo3O12 increases to 2.0000, the conductivity of the composite increases so much that a transformation from capacitance to pure resistance appears. The results suggest that Y2Mo3O12 plays a dominant role in the composite for low content of Al（presenting isolate particles）, while the content of Al increases enough to contact each other, the composite presents mainly the property of Al. For the effect of high content Al, it is considered that Al is squeezed out of the cermets during the uniaxial pressure process to form a thin layer on the surface.展开更多
Ceramics usually have irregular grains, cracking, or porosity, which result in their lightproof.Y2Mo3O12 ceramics have more porosity due to the heavy hygroscopicity.Introducing ZnLi to Y2Mo3O12 could form regular grai...Ceramics usually have irregular grains, cracking, or porosity, which result in their lightproof.Y2Mo3O12 ceramics have more porosity due to the heavy hygroscopicity.Introducing ZnLi to Y2Mo3O12 could form regular grains, reduce cracking and porosity.With increasing the content of ZnLi, the grain shapes self-assembly gradually and then the laser scattering and transmittance improve.The laser scattering property and transmittance of diverging rays become the best in ceramics Y2-x(ZnLi)xMo3O12(x = 1.0 and 1.2) with regular grains and low thermal expansion.The formation mechanism of regular grains is ascribed to the substitutions of Zn^2+ and Li+for Y^3+ in Y2Mo3O12 resulting in the preferential growth.The investigation in laser scattering, transmittance and low thermal expansion behaviors of Y2-x(ZnLi)xMo3O12 could pave a way to weaken the strong-laser attack from the high-power laser weapon and the other.展开更多
Low thermal expansion materials are mostly ceramics with low conductive property, which limits their applications in electronic devices. The poor conductive property of ceramic ZrV_2 O_7 could be improved by bi-substi...Low thermal expansion materials are mostly ceramics with low conductive property, which limits their applications in electronic devices. The poor conductive property of ceramic ZrV_2 O_7 could be improved by bi-substitution of Fe and Mo for Zr and V, accompanied with low thermal expansion. Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 has electrical conductivity of 8.2× 10^(-5) S/cm and 9.41× 10^(-4) S/cm at 291 K and 623 K, respectively. From 291 K to 413 K, thermal excitation leads to the increase of carrier concentration, which causes the rapid decrease of resistance. At 413–533 K, the conductivity is unchanged due to high scattering probability and a slowing increase of carrier concentration. The conductivity rapidly increases again from533 K to 623 K due to the intrinsic thermal excitation. The thermal expansion coefficient of Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 is as low as 0.72× 10^(-6 )K^(-1) at 140–700 K from the dilatometer measurement. These properties suggest that Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 has attractive application in electronic components.展开更多
HfMgMo（3-x）WxO（12） with x = 0.5, 1.0, 1.5, 2.0, and 2.5 are developed with a simple solid state method. With increasing the content of W, solid solutions of Hf Mg Mo3-xWx O12 crystallize in an orthorhombic structu...HfMgMo（3-x）WxO（12） with x = 0.5, 1.0, 1.5, 2.0, and 2.5 are developed with a simple solid state method. With increasing the content of W, solid solutions of Hf Mg Mo3-xWx O12 crystallize in an orthorhombic structure for x≤2.0 and a monoclinic structure for x2.0. A near-zero thermal expansion（ZTE） is realized for HfMgMo（2.5）W（0.5）O（12） and negative coefficients of thermal expansion（NCTE） are achieved for other compositions with different values. The ZTE and variation of NCTE are attributed to the difference in electronegativity between W and Mo and incorporation of a different amount of W, which cause variable distortion of the octahedra and softening of the MoO4 tetrahedra, and hence an enhanced NCTE in the a- and c-axis and reduced CTE in the b-axis as revealed by Raman spectroscopy and x-ray diffraction.展开更多
Solid solutions of In2（1-x）（HfMg）xMo3O12 are synthesized by solid state reaction with the aim to reduce the phase transition temperature of In2Mo3O12 and improve its thermal expansion property.The effects of（HfMg...Solid solutions of In2（1-x）（HfMg）xMo3O12 are synthesized by solid state reaction with the aim to reduce the phase transition temperature of In2Mo3O12 and improve its thermal expansion property.The effects of（HfMg）^6＋ incorporation on the phase transition and thermal expansion are investigated.It is shown that the monoclinic-to-orthorhombic phase transition temperature obviously decreases and the coefficient of thermal expansion（CTE） of the orthorhombic becomes less negative and approaches to zero with increasing the content of（HfMg）^6＋.A near zero thermal expansion covering the case at room temperature（RT） is achieved for the solid solutions with x ≥ 0.85,implying potential applications of this material in many fields.展开更多
文摘本文采用水热法制备了γ-Bi_2Sn_2O_7并研究了其在可见光区的光电响应。Bi_2Sn_2O_7的晶体结构和光电响应特性分别用X射线衍射和表面光电压谱进行表征。研究结果表明,合成的Bi_2Sn_2O_7呈现γ相立方结构,通过吸收光谱估算光学带隙为2.67 e V,比α-Bi_2O_3(2.85 e V)的光学带隙小。Bi_2Sn_2O_7的光电响应相对于α-Bi_2O_3在可见光区展现出一定的优势,同时对外加电压有很强的响应。
基金Project supported by the National Natural Science Foundation of China(Grant Nos.10974183 and 11104252)the Doctoral Fund of the Ministry of Education of China(Grant No.20114101110003)+2 种基金the Fund for Science&Technology Innovation Team of Zhengzhou,China(Grant No.112PCXTD337)the Industrial Science and Technology Research Projects of Kaifeng,Henan Province,China(Grant No.1501049)the Key Research Projects of Henan Higher Education Institutions,China(Grant No.18A140014)
文摘Low thermal expansion composites are difficult to obtain by using Al with larger positive thermal expansion coefficient（TEC） and the materials with smaller negative TECs. In this investigation, Y2Mo3O12 with larger negative TEC is used to combine with Al to obtain a low thermal expansion composite with high conductivity. The TEC of Al is reduced by 19%for a ratio Al：Y2Mo3O12 of 0.3118. When the mass ratio of Al：Y2Mo3O12 increases to 2.0000, the conductivity of the composite increases so much that a transformation from capacitance to pure resistance appears. The results suggest that Y2Mo3O12 plays a dominant role in the composite for low content of Al（presenting isolate particles）, while the content of Al increases enough to contact each other, the composite presents mainly the property of Al. For the effect of high content Al, it is considered that Al is squeezed out of the cermets during the uniaxial pressure process to form a thin layer on the surface.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.60976016,61350012,and 11574276)the Key Scientific Research Projects of Henan Province,China(Grant No.15B140004)+2 种基金Henan Science and Technology Development Project,China(Grant No.182102210241)Key Projects of Science and Technology Research of Henan Provincial Department of Education,China(Grant No.18A140014)Industrial Science and Technology Research Projects of Kaifeng,Henan Province,China(Grant No.1501049)
文摘Ceramics usually have irregular grains, cracking, or porosity, which result in their lightproof.Y2Mo3O12 ceramics have more porosity due to the heavy hygroscopicity.Introducing ZnLi to Y2Mo3O12 could form regular grains, reduce cracking and porosity.With increasing the content of ZnLi, the grain shapes self-assembly gradually and then the laser scattering and transmittance improve.The laser scattering property and transmittance of diverging rays become the best in ceramics Y2-x(ZnLi)xMo3O12(x = 1.0 and 1.2) with regular grains and low thermal expansion.The formation mechanism of regular grains is ascribed to the substitutions of Zn^2+ and Li+for Y^3+ in Y2Mo3O12 resulting in the preferential growth.The investigation in laser scattering, transmittance and low thermal expansion behaviors of Y2-x(ZnLi)xMo3O12 could pave a way to weaken the strong-laser attack from the high-power laser weapon and the other.
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11574276,51702097,and 11574083)the Program for Innovative Research Team(in Science and Technology)in University of Henan Province,China(Grant No.16IRTSTHN017)Henan Science and Technology Development Project,China(Grant No.182102210241)
文摘Low thermal expansion materials are mostly ceramics with low conductive property, which limits their applications in electronic devices. The poor conductive property of ceramic ZrV_2 O_7 could be improved by bi-substitution of Fe and Mo for Zr and V, accompanied with low thermal expansion. Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 has electrical conductivity of 8.2× 10^(-5) S/cm and 9.41× 10^(-4) S/cm at 291 K and 623 K, respectively. From 291 K to 413 K, thermal excitation leads to the increase of carrier concentration, which causes the rapid decrease of resistance. At 413–533 K, the conductivity is unchanged due to high scattering probability and a slowing increase of carrier concentration. The conductivity rapidly increases again from533 K to 623 K due to the intrinsic thermal excitation. The thermal expansion coefficient of Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 is as low as 0.72× 10^(-6 )K^(-1) at 140–700 K from the dilatometer measurement. These properties suggest that Zr_(0.1) Fe_(0.9) V_(1.1 )Mo_(0.9 )O_7 has attractive application in electronic components.
基金supported by the National Natural Science Foundation of China(Grant Nos.10974183 and 11104252)the Key Natural Science Project of Henan Province,China(Grant No.142102210073)+1 种基金the Doctoral Fund of the Ministry of Education of China(Grant No.20114101110003)the Fund for Science & Technology Innovation Team of Zhengzhou,China(Grant No.112PCXTD337)
文摘HfMgMo（3-x）WxO（12） with x = 0.5, 1.0, 1.5, 2.0, and 2.5 are developed with a simple solid state method. With increasing the content of W, solid solutions of Hf Mg Mo3-xWx O12 crystallize in an orthorhombic structure for x≤2.0 and a monoclinic structure for x2.0. A near-zero thermal expansion（ZTE） is realized for HfMgMo（2.5）W（0.5）O（12） and negative coefficients of thermal expansion（NCTE） are achieved for other compositions with different values. The ZTE and variation of NCTE are attributed to the difference in electronegativity between W and Mo and incorporation of a different amount of W, which cause variable distortion of the octahedra and softening of the MoO4 tetrahedra, and hence an enhanced NCTE in the a- and c-axis and reduced CTE in the b-axis as revealed by Raman spectroscopy and x-ray diffraction.
基金supported by the National Natural Science Foundation of China(Grant Nos.11574276,51302249,and 51503185)the Doctoral Fund of the Ministry of Education of China(Grant No.20114101110003)
文摘Solid solutions of In2（1-x）（HfMg）xMo3O12 are synthesized by solid state reaction with the aim to reduce the phase transition temperature of In2Mo3O12 and improve its thermal expansion property.The effects of（HfMg）^6＋ incorporation on the phase transition and thermal expansion are investigated.It is shown that the monoclinic-to-orthorhombic phase transition temperature obviously decreases and the coefficient of thermal expansion（CTE） of the orthorhombic becomes less negative and approaches to zero with increasing the content of（HfMg）^6＋.A near zero thermal expansion covering the case at room temperature（RT） is achieved for the solid solutions with x ≥ 0.85,implying potential applications of this material in many fields.