High-k gate dielectric Hf Ti ON Ga As metal-oxide–semiconductor（MOS） capacitors with La ON as interfacial passivation layer（IPL） and NH3- or N2-plasma surface pretreatment are fabricated, and their interfacial an...High-k gate dielectric Hf Ti ON Ga As metal-oxide–semiconductor（MOS） capacitors with La ON as interfacial passivation layer（IPL） and NH3- or N2-plasma surface pretreatment are fabricated, and their interfacial and electrical properties are investigated and compared with their counterparts that have neither La ON IPL nor surface treatment. It is found that good interface quality and excellent electrical properties can be achieved for a NH3-plasma pretreated Ga As MOS device with a stacked gate dielectric of Hf Ti ON/La ON. These improvements should be ascribed to the fact that the NH3-plasma can provide H atoms and NH radicals that can effectively remove defective Ga/As oxides. In addition, La ON IPL can further block oxygen atoms from being in-diffused, and Ga and As atoms from being out-diffused from the substrate to the high-k dielectric. This greatly suppresses the formation of Ga/As native oxides and gives rise to an excellent high-k/Ga As interface.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.61176100 and 61274112)
文摘High-k gate dielectric Hf Ti ON Ga As metal-oxide–semiconductor（MOS） capacitors with La ON as interfacial passivation layer（IPL） and NH3- or N2-plasma surface pretreatment are fabricated, and their interfacial and electrical properties are investigated and compared with their counterparts that have neither La ON IPL nor surface treatment. It is found that good interface quality and excellent electrical properties can be achieved for a NH3-plasma pretreated Ga As MOS device with a stacked gate dielectric of Hf Ti ON/La ON. These improvements should be ascribed to the fact that the NH3-plasma can provide H atoms and NH radicals that can effectively remove defective Ga/As oxides. In addition, La ON IPL can further block oxygen atoms from being in-diffused, and Ga and As atoms from being out-diffused from the substrate to the high-k dielectric. This greatly suppresses the formation of Ga/As native oxides and gives rise to an excellent high-k/Ga As interface.