Alloying Pt with transition metals can significantly improve the catalytic properties for the oxygen reduction reaction(ORR).However,the application of Pt-transition metal alloys in fuel cells is largely limited by po...Alloying Pt with transition metals can significantly improve the catalytic properties for the oxygen reduction reaction(ORR).However,the application of Pt-transition metal alloys in fuel cells is largely limited by poor long-term durability because transition metals can easily leach.In this study,we developed a nonmetallic doping approach and prepared a P-doped Pt catalyst with excellent durability for the ORR.Carbon-supported core-shell nanoparticles with a P-doped Pt core and Pt shell(denoted as PtPx@Pt/C)were synthesized via heat-treatment phosphorization of commercial Pt/C,followed by acid etching.Compositional analysis using electron energy loss spectroscopy and X-ray photoelectron spectroscopy clearly demonstrated that Pt was enriched in the near-surface region(approximately 1 nm)of the carbon-supported core-shell nanoparticles.Owning to P doping,the ORR specific activity and mass activity of the PtP_(1.4)@Pt/C catalyst were as high as 0.62 mA cm^(–2)and 0.31 mAμgPt–^(1),respectively,at 0.90 V,and they were enhanced by 2.8 and 2.1 times,respectively,in comparison with the Pt/C catalyst.More importantly,PtP_(1.4)@Pt/C exhibited superior stability with negligible mass activity loss(6%after 30000 potential cycles and 25%after 90000 potential cycles),while Pt/C lost 46%mass activity after 30000 potential cycles.The high ORR activity and durability were mainly attributed to the core-shell nanostructure,the electronic structure effect,and the resistance of Pt nanoparticles against aggregation,which originated from the enhanced ability of the PtP_(1.4)@Pt to anchor to the carbon support.This study provides a new approach for constructing nonmetal-doped Pt-based catalysts with excellent activity and durability for the ORR.展开更多
基金financially supported by the National Natural Science Foundation of China (No. 21875221 and No. 22102156)Distinguished Young Scholars Innovation Team of Zhengzhou University (No. 32320275)+1 种基金Academic Degrees & Graduate Education Reform Project of Henan Province (2021 SJGLX 093Y)China Postdoctoral Science Foundation (2021TQ0295)。
文摘Alloying Pt with transition metals can significantly improve the catalytic properties for the oxygen reduction reaction(ORR).However,the application of Pt-transition metal alloys in fuel cells is largely limited by poor long-term durability because transition metals can easily leach.In this study,we developed a nonmetallic doping approach and prepared a P-doped Pt catalyst with excellent durability for the ORR.Carbon-supported core-shell nanoparticles with a P-doped Pt core and Pt shell(denoted as PtPx@Pt/C)were synthesized via heat-treatment phosphorization of commercial Pt/C,followed by acid etching.Compositional analysis using electron energy loss spectroscopy and X-ray photoelectron spectroscopy clearly demonstrated that Pt was enriched in the near-surface region(approximately 1 nm)of the carbon-supported core-shell nanoparticles.Owning to P doping,the ORR specific activity and mass activity of the PtP_(1.4)@Pt/C catalyst were as high as 0.62 mA cm^(–2)and 0.31 mAμgPt–^(1),respectively,at 0.90 V,and they were enhanced by 2.8 and 2.1 times,respectively,in comparison with the Pt/C catalyst.More importantly,PtP_(1.4)@Pt/C exhibited superior stability with negligible mass activity loss(6%after 30000 potential cycles and 25%after 90000 potential cycles),while Pt/C lost 46%mass activity after 30000 potential cycles.The high ORR activity and durability were mainly attributed to the core-shell nanostructure,the electronic structure effect,and the resistance of Pt nanoparticles against aggregation,which originated from the enhanced ability of the PtP_(1.4)@Pt to anchor to the carbon support.This study provides a new approach for constructing nonmetal-doped Pt-based catalysts with excellent activity and durability for the ORR.
