The preparation and micwave-absorbing behavior of nanosize PSZFe magnetic particles were studied.Nanosize PSZFe magnetic particles were prepared as following:nanosize Fe particles generated by themal decomposition of ...The preparation and micwave-absorbing behavior of nanosize PSZFe magnetic particles were studied.Nanosize PSZFe magnetic particles were prepared as following:nanosize Fe particles generated by themal decomposition of Fe(CO)-5 in organic solvents were encapsulated with synthesized polysilazane(PSZ) precursor and then irradiated under ultraviolet light.PSZFe particles were characterized by using transmission election microscope(TEM),X-Ray powder diffraction(XRD) and vibrating sample magntometer(VSM),and their microwave-adsorbing properties were measured by means of a vector network analyzer.The influence of the polysilazation layer on corrosion and magnetization of PSZFe particles and the relationship between polysilazation layer and micwave-absorbing behavior of PSZFe particles were investigated.Results showed that the average diameter of PSZFe particles was 30 nm,the structure of iron in PSZFe magnetic particles was α-Fe.The formation of a PSZ layer on nanosize Fe particles enchanced the corrosion resistance of PSZFe.In addition,PSZFe particles coated with 3 wt% PSZ demonstrated high corrosion resistance and fine microwave-absorbing ability as well.The reflection loss was less than -10 dB in the range of 9^8～16 GHz,and a reflection loss value of -20 dB was detected at 13 GHz.展开更多
A mesogen-jacketed liquid crystal polymer,poly{2,5 -bis［(4′-hexyloxyphenyl)oxycarbonyl］styrene}(PHPCS),with number-average d molecular weight of 1.28×１０5 and polydispersity of 1.48 was prepared vi a 2,2,6,6 ...A mesogen-jacketed liquid crystal polymer,poly{2,5 -bis［(4′-hexyloxyphenyl)oxycarbonyl］styrene}(PHPCS),with number-average d molecular weight of 1.28×１０5 and polydispersity of 1.48 was prepared vi a 2,2,6,6 -tetramethyl-piperidinyloxy mediated free radical polymerization.The thermotr opic behavior was studied by a combination of differential scanning calorimetry, thermogravimetry,polarized optical microscope and wide-angle X-ray diffracti on.PHPCS was not crystalline over the entire temperature region studied.On hea ting,PHPCS first became an isotropic melt at glass transition temperature (T g) and then a mesophase at temperatures much higher than T g.On subseq uent cooling,the formed ordered phase disappeared above T g.Contrary to t heoretical predictions and previous experimental observations,the transition fr om isotropic melt to liquid crystalline phase was an endothermic process and th e order-disorder transition took place with concurrence of heat release.展开更多
文摘The preparation and micwave-absorbing behavior of nanosize PSZFe magnetic particles were studied.Nanosize PSZFe magnetic particles were prepared as following:nanosize Fe particles generated by themal decomposition of Fe(CO)-5 in organic solvents were encapsulated with synthesized polysilazane(PSZ) precursor and then irradiated under ultraviolet light.PSZFe particles were characterized by using transmission election microscope(TEM),X-Ray powder diffraction(XRD) and vibrating sample magntometer(VSM),and their microwave-adsorbing properties were measured by means of a vector network analyzer.The influence of the polysilazation layer on corrosion and magnetization of PSZFe particles and the relationship between polysilazation layer and micwave-absorbing behavior of PSZFe particles were investigated.Results showed that the average diameter of PSZFe particles was 30 nm,the structure of iron in PSZFe magnetic particles was α-Fe.The formation of a PSZ layer on nanosize Fe particles enchanced the corrosion resistance of PSZFe.In addition,PSZFe particles coated with 3 wt% PSZ demonstrated high corrosion resistance and fine microwave-absorbing ability as well.The reflection loss was less than -10 dB in the range of 9^8～16 GHz,and a reflection loss value of -20 dB was detected at 13 GHz.
文摘A mesogen-jacketed liquid crystal polymer,poly{2,5 -bis［(4′-hexyloxyphenyl)oxycarbonyl］styrene}(PHPCS),with number-average d molecular weight of 1.28×１０5 and polydispersity of 1.48 was prepared vi a 2,2,6,6 -tetramethyl-piperidinyloxy mediated free radical polymerization.The thermotr opic behavior was studied by a combination of differential scanning calorimetry, thermogravimetry,polarized optical microscope and wide-angle X-ray diffracti on.PHPCS was not crystalline over the entire temperature region studied.On hea ting,PHPCS first became an isotropic melt at glass transition temperature (T g) and then a mesophase at temperatures much higher than T g.On subseq uent cooling,the formed ordered phase disappeared above T g.Contrary to t heoretical predictions and previous experimental observations,the transition fr om isotropic melt to liquid crystalline phase was an endothermic process and th e order-disorder transition took place with concurrence of heat release.
