A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR...A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR spectroscopy and X ray single crystal diffraction. X ray single crystal analysis reveals the structure consists of [La(C8H6NO2)3]n. It crystallizes in monoclinic crystal system with space group P2(1)/c. Crystallographic date: a=0. 7889(3)nm, b=2.5916(9)nm, c=1.1489(4)nm, α =90.00° , β =95.219(6)° , γ =90.00° , V=2.3393(15)nm3, Z=4, Dc=1.656g· cm- 3, μ =1.871mm- 1, F(000)=1152, R1=0.0328, wR2=0.0522. CCDC: 211700.展开更多
以N iC l2.6H2O和4-氰基吡啶为原料,在中温水热反应条件下,合成了一种新型配位聚合物[N i(C6H4NO2)2(H2O)4]n单晶体,并对其进行了元素分析、红外光谱表征和X射线单晶衍射测定。该配位聚合物属三斜晶系,P-1空间群,a=0.6298(4)nm,b=0.6907...以N iC l2.6H2O和4-氰基吡啶为原料,在中温水热反应条件下,合成了一种新型配位聚合物[N i(C6H4NO2)2(H2O)4]n单晶体,并对其进行了元素分析、红外光谱表征和X射线单晶衍射测定。该配位聚合物属三斜晶系,P-1空间群,a=0.6298(4)nm,b=0.6907(4)nm,c=0.9243(5)nm,α=96.437(8),°β=105.184(9)°,γ=113.314(9)°,V=0.3456(3)nm3,Z=2,dc=1.802 g/cm3,μ=1.452mm-1,F(000)=194,R1=0.0309,R2=0.0753。该晶体通过配位键的连接和分子间氢键相互作用形成三维的网状结构。展开更多
文摘A novel porous coordination polymer [La(C8H6NO2)3]n was synthesized by hydrothermal reaction of flexible ligands 3 (3 pyridyl)acrylate and La(NO3)3· 6H2O. The structure was characterized by elemental analysis, IR spectroscopy and X ray single crystal diffraction. X ray single crystal analysis reveals the structure consists of [La(C8H6NO2)3]n. It crystallizes in monoclinic crystal system with space group P2(1)/c. Crystallographic date: a=0. 7889(3)nm, b=2.5916(9)nm, c=1.1489(4)nm, α =90.00° , β =95.219(6)° , γ =90.00° , V=2.3393(15)nm3, Z=4, Dc=1.656g· cm- 3, μ =1.871mm- 1, F(000)=1152, R1=0.0328, wR2=0.0522. CCDC: 211700.
文摘以N iC l2.6H2O和4-氰基吡啶为原料,在中温水热反应条件下,合成了一种新型配位聚合物[N i(C6H4NO2)2(H2O)4]n单晶体,并对其进行了元素分析、红外光谱表征和X射线单晶衍射测定。该配位聚合物属三斜晶系,P-1空间群,a=0.6298(4)nm,b=0.6907(4)nm,c=0.9243(5)nm,α=96.437(8),°β=105.184(9)°,γ=113.314(9)°,V=0.3456(3)nm3,Z=2,dc=1.802 g/cm3,μ=1.452mm-1,F(000)=194,R1=0.0309,R2=0.0753。该晶体通过配位键的连接和分子间氢键相互作用形成三维的网状结构。