合成CSH凝胶在混凝土中的增强作用

利用硅质材料和石灰制得的合成CSH凝胶具有如下特征:合成产物结晶度很差,呈凝胶态,在扫描电镜下可观察到其棉花朵状的纤维网络结构,颗粒细度较高,比表面积大于25m^2/g。本文研究了这种合成凝胶在混凝土中的使用及对混凝土的增强作用,并且探讨了增强作用的机理。

THE IMPERMEABILITY OF CEMENT MORTAR BY DRYTHERMAL CURING

The relationship of unstable osmosis coefficient to time and osmosis deep is derived from the osmosis equation in this paper. Mercury porosimeter is used to study the pore structure of cement mortar. The method of volume density is used to determine the changes of specific pore volume, and therelation between pore structure and impermeability is analyzed. Although the drythermal curing method has many advantages over other curing method, the directional pore along the direction of evaporization of water is formed inside concrete. The harmful pore above 2000(?) is increased and the average diameter of pore rises. As a result, the mortar impermeability loses seriously.

C-S-H及C-S-H脱水相对水泥石结构改性的研究

以C-S-H及C-S-H脱水相作水泥水化物沉淀中心的品种。从理论上阐明了它们是具有较大介电常数、较小物理化学不均匀系数、高分散度的晶种物质,故具有优先吸附的界面效应及优先沉淀的结晶中心作用,可缓和原始矿物表面的高浓度的屏蔽效应及界面的近程析晶,使水化物分布均匀、结构致密,从而提高水泥石强度。C-S-H及C-S-H脱水相两者中,尤以后者作用更显著。

晶种对蒸压粉煤灰净浆制品性能的影响

本文研究了晶种掺量及蒸压时间对粉煤灰、石灰、石膏反应率和粉煤灰硅酸盐制品的孔结构及产物形态、分布的影响。提出了有效托勃奠来石及有效托勃奠来石系数表达式。结果表明:适量晶种消除了水化产物局部化现象,减少了无效托勃奠来石量。

干热脱模养护对硅酸盐制品强度的影响

煤渣、粉煤灰和煤矸石等硅酸盐制品的凝固及硬化过程绥慢,初始强度较低,在蒸汽养护之前必须有较长的静停时间,延长养护周期,阻碍了生产的发朕。尤其是当前采用成型机制作空心砌块,产量较高,如不相应地缩短养护周期,将影响到成型机的推广使用。

经干热养护水泥砂浆的抗渗性

本文从渗透方程导出砂浆非稳态渗透系数与时间和渗透深度的关系,采用水银压入法研究水泥浆体的孔结构,采用容重法测试砂浆比孔容的变化,分析孔结构与抗渗性的关系。干热养护虽然具有很多优点,但混凝土内部沿水分蒸发方向形成定向串通毛细孔道,大于2000A的多害孔增加,最大可几孔径增大,因而严重地降低砂浆的抗渗性。

合成C-S-H凝胶对水泥石-集料界面区的影响

研究了利用硅质材料和钙质材料经常温常压下水热反应制得的合成C-S-H疑胶对水泥石-集料界面区结构和性能的影响,发现这种合成凝胶对界面区的结构和性能有独特的改善作用。本文还探讨了合成C-S-H凝胶对界面区的作用机理。