A composite ceramic with nominal composition of 45.0 wt%（Ba0.5Sr0.5）TiO3–55.0 wt%MgO（acronym is BST–MgO） is sintered for fabricating a frequency reconfigurable aperture-coupled microstrip antenna. The calcined ...A composite ceramic with nominal composition of 45.0 wt%（Ba0.5Sr0.5）TiO3–55.0 wt%MgO（acronym is BST–MgO） is sintered for fabricating a frequency reconfigurable aperture-coupled microstrip antenna. The calcined BST–Mg O composite ceramic exhibits good microwave dielectric properties at X-band with appropriate dielectric constant εr around85, lower dielectric loss tan δ about 0.01, and higher permittivity tunability 14.8% at 8.33 k V/cm. An ultrahigh E-field tunability of working frequency up to 11.0%（i.e., from 9.1 GHz to 10.1 GHz with a large frequency shift of 1000 MHz）at a DC bias field from 0 to 8.33 k V/cm and a considerably large center gain over 7.5 d B are obtained in the designed frequency reconfigurable microstrip antenna. These results demonstrate that BST materials are promising for the frequency reconfigurable antenna.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.11074040)the Key Project of Shandong Provincial Department of Science and TechnologyChina(Grant No.ZR2012FZ006)
文摘A composite ceramic with nominal composition of 45.0 wt%（Ba0.5Sr0.5）TiO3–55.0 wt%MgO（acronym is BST–MgO） is sintered for fabricating a frequency reconfigurable aperture-coupled microstrip antenna. The calcined BST–Mg O composite ceramic exhibits good microwave dielectric properties at X-band with appropriate dielectric constant εr around85, lower dielectric loss tan δ about 0.01, and higher permittivity tunability 14.8% at 8.33 k V/cm. An ultrahigh E-field tunability of working frequency up to 11.0%（i.e., from 9.1 GHz to 10.1 GHz with a large frequency shift of 1000 MHz）at a DC bias field from 0 to 8.33 k V/cm and a considerably large center gain over 7.5 d B are obtained in the designed frequency reconfigurable microstrip antenna. These results demonstrate that BST materials are promising for the frequency reconfigurable antenna.