The hot deformation behavior of Ti-6Al-4V(TC4) titanium alloy was investigated in the temperature range from 650 °C to 950 °C with the strain rate ranging from 7.7×10-4 s-1 to 7.7×10-2 s-1.The hot ...The hot deformation behavior of Ti-6Al-4V(TC4) titanium alloy was investigated in the temperature range from 650 °C to 950 °C with the strain rate ranging from 7.7×10-4 s-1 to 7.7×10-2 s-1.The hot tension test results indicate that the flow stress decreases with increasing the deformation temperature and increases with increasing the strain rate.XRD analysis result reveals that only deformation temperature affects the phase constitution.The microstructure evolution under different deformation conditions was characterized by TEM observation.For the deformation of TC4 alloy,the work-hardening is dominant at low temperature,while the dynamic recovery and dynamic re-crystallization assisted softening is dominant at high temperature.展开更多
The true strain-stress curves of TC4 titanium sheet were obtained by uniaxial tensile tests under different experimental conditions,and the effects of forming temperature and strain speed on the rheological stress and...The true strain-stress curves of TC4 titanium sheet were obtained by uniaxial tensile tests under different experimental conditions,and the effects of forming temperature and strain speed on the rheological stress and hot deforming capacity were analyzed.The Forming experience for titanium alloy TC4 sheet with 1mm thickness was executed to investigate the hot forming technology of Thin-walled cylindrical cup of titanium alloy.The results showed that the softening mechanism was dynamic re-crystallization,flow curves of the TC4 alloy were characterized by a linear increase until regular single peak after which flow softening was observed.And the flow stress decreased with increasing temperature and decreasing strain rate.as the forming temperature increased,the limit drawing coefficient would decreased first and then increased,there would be a minimum 0.461 when the temperature was 770 ℃,springback would be becoming smaller,but phenomenon of lug do not Significant improvement.展开更多
文摘The hot deformation behavior of Ti-6Al-4V(TC4) titanium alloy was investigated in the temperature range from 650 °C to 950 °C with the strain rate ranging from 7.7×10-4 s-1 to 7.7×10-2 s-1.The hot tension test results indicate that the flow stress decreases with increasing the deformation temperature and increases with increasing the strain rate.XRD analysis result reveals that only deformation temperature affects the phase constitution.The microstructure evolution under different deformation conditions was characterized by TEM observation.For the deformation of TC4 alloy,the work-hardening is dominant at low temperature,while the dynamic recovery and dynamic re-crystallization assisted softening is dominant at high temperature.
文摘The true strain-stress curves of TC4 titanium sheet were obtained by uniaxial tensile tests under different experimental conditions,and the effects of forming temperature and strain speed on the rheological stress and hot deforming capacity were analyzed.The Forming experience for titanium alloy TC4 sheet with 1mm thickness was executed to investigate the hot forming technology of Thin-walled cylindrical cup of titanium alloy.The results showed that the softening mechanism was dynamic re-crystallization,flow curves of the TC4 alloy were characterized by a linear increase until regular single peak after which flow softening was observed.And the flow stress decreased with increasing temperature and decreasing strain rate.as the forming temperature increased,the limit drawing coefficient would decreased first and then increased,there would be a minimum 0.461 when the temperature was 770 ℃,springback would be becoming smaller,but phenomenon of lug do not Significant improvement.