Nanocrystalline oxide dispersion strengthened （ODS） ferritic steel powders with nominal composition of Fe-14Cr-3W-0.3Ti-0.4Y2O3 are synthesized using sol-gel method and hy- drogen reduction. At low reduction tempera...Nanocrystalline oxide dispersion strengthened （ODS） ferritic steel powders with nominal composition of Fe-14Cr-3W-0.3Ti-0.4Y2O3 are synthesized using sol-gel method and hy- drogen reduction. At low reduction temperature the impurity phase of CrO is detected. At higher reduction temperature the impurity phase is Cr2O3 which eventually disappears with increasing reduction time. A pure ODS ferritic steel phase is obtained after reducing the sol-gel resultant products at 1200℃ for 3 h. The HRTEM and EDS mapping indicate that the Y2O3 particles with a size of about 15 nm are homogenously dispersed in the alloy matrix. The bulk ODS ferritic steel samples prepared from such powders exhibit good mechanical performance with an ultimate tensile stress of 960 MPa.展开更多
基金supported by the Innovation Program(No.KJCX2-YW-N35)Strategic Priority Research Program(No.XDA03010303) of Chinese Academy of Sciences+1 种基金National Magnetic Confinement Fusion Program(No.2009GB106005)National Natural Science Foundation of China(Nos.11075177,91026002,11175203,51101152)
文摘Nanocrystalline oxide dispersion strengthened （ODS） ferritic steel powders with nominal composition of Fe-14Cr-3W-0.3Ti-0.4Y2O3 are synthesized using sol-gel method and hy- drogen reduction. At low reduction temperature the impurity phase of CrO is detected. At higher reduction temperature the impurity phase is Cr2O3 which eventually disappears with increasing reduction time. A pure ODS ferritic steel phase is obtained after reducing the sol-gel resultant products at 1200℃ for 3 h. The HRTEM and EDS mapping indicate that the Y2O3 particles with a size of about 15 nm are homogenously dispersed in the alloy matrix. The bulk ODS ferritic steel samples prepared from such powders exhibit good mechanical performance with an ultimate tensile stress of 960 MPa.