Fe^2+:ZnSe thin films are prepared on sapphire substrate at room temperature by electron beam evaporation and then annealed in vacuum(about 1×10^-4 Pa)at different temperatures.The influences of thermal annealing...Fe^2+:ZnSe thin films are prepared on sapphire substrate at room temperature by electron beam evaporation and then annealed in vacuum(about 1×10^-4 Pa)at different temperatures.The influences of thermal annealing on the structural and optical properties of these films such as grain size and optical transmittance are investigated.The x-ray diffraction patterns show that the Fe2+:ZnSe thin film is preferred to be oriented along the(111)plane at different annealing temperatures.After the film is annealed,the full-width-at-half-maximum(FWHM)of the x-ray diffraction peak profile(111)of the film decreases and its crystal quality is improved.Scanning electron microscope images show that the films are more dense after being annealed.Finally,the sample is used as a saturable absorber in ZBLAN fiber laser.The annealed Fe^2+:ZnSe thin films can be used to realize stable Q-switching modulation on ZBLAN fiber laser.The results demonstrate that the Fe2+:ZnSe thin film is a promising material for generating the high-power pulses of mid-infrared Q-switched fiber lasers.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.11574221)the Graduate Student’s Research and Innovation Fund of Sichuan University,China(Grant No.2018YJSY008).
文摘Fe^2+:ZnSe thin films are prepared on sapphire substrate at room temperature by electron beam evaporation and then annealed in vacuum(about 1×10^-4 Pa)at different temperatures.The influences of thermal annealing on the structural and optical properties of these films such as grain size and optical transmittance are investigated.The x-ray diffraction patterns show that the Fe2+:ZnSe thin film is preferred to be oriented along the(111)plane at different annealing temperatures.After the film is annealed,the full-width-at-half-maximum(FWHM)of the x-ray diffraction peak profile(111)of the film decreases and its crystal quality is improved.Scanning electron microscope images show that the films are more dense after being annealed.Finally,the sample is used as a saturable absorber in ZBLAN fiber laser.The annealed Fe^2+:ZnSe thin films can be used to realize stable Q-switching modulation on ZBLAN fiber laser.The results demonstrate that the Fe2+:ZnSe thin film is a promising material for generating the high-power pulses of mid-infrared Q-switched fiber lasers.