A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block...A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block copolymer(SBS)in the assistance of coupling agent modification.Direct molding of the core-shell FCIPs without adding extra binder results in a large permeability due to the high filling ratio(55vol%)of absorbents.Importantly,the permittivity is well suppressed by the dense insulate polymer shell on the FCIPs,avoiding the severe impedance mismatch problem of the high filler content microwave absorbing materials.Investigations show that modifying the surface of FCIPs by proper amount of silane coupling agent is critical for the coating quality of the SBS shell,which is verified by resistivity and corrosion current density measurements,and can be interpreted by improved interfacial compatibility between the modified FCIPs and SBS.The obtained microwave absorbing sheet shows a minimum reflection loss of-38.74 dB at 1.57 GHz and has an effective absorption bandwidth from 1.1 to 2.3 GHz at a relatively small thickness of 2 mm.展开更多
基金Funded by the Young Top-notch Talent Cultivation Program of Hubei Provincethe National Natural Science Foundation of China(Nos.52071239,51521001)Fundamental Research Funds for the Central Universities(Nos.WUT:2021IVA116 and WUT:2021CG015)。
文摘A microwave absorbing sheet with a high complex permeability and a relatively low complex permittivity is obtained by molding of the densely coated flaky carbonyl iron particles(FCIPs)by styrenebutadiene-styrene block copolymer(SBS)in the assistance of coupling agent modification.Direct molding of the core-shell FCIPs without adding extra binder results in a large permeability due to the high filling ratio(55vol%)of absorbents.Importantly,the permittivity is well suppressed by the dense insulate polymer shell on the FCIPs,avoiding the severe impedance mismatch problem of the high filler content microwave absorbing materials.Investigations show that modifying the surface of FCIPs by proper amount of silane coupling agent is critical for the coating quality of the SBS shell,which is verified by resistivity and corrosion current density measurements,and can be interpreted by improved interfacial compatibility between the modified FCIPs and SBS.The obtained microwave absorbing sheet shows a minimum reflection loss of-38.74 dB at 1.57 GHz and has an effective absorption bandwidth from 1.1 to 2.3 GHz at a relatively small thickness of 2 mm.