The effect of surface morphology of 6H-SiC substrate on the ohmic contact properties of Ti/6H-SiC structure is studied. The H-terminated surface on Si-face 6H-SiC is obtained by both dipping SiC into HF acid solution ...The effect of surface morphology of 6H-SiC substrate on the ohmic contact properties of Ti/6H-SiC structure is studied. The H-terminated surface on Si-face 6H-SiC is obtained by both dipping SiC into HF acid solution for 15 s and thermal heating SiC in hydrogen atmosphere at 1100 ℃ for 10 min, while the H-terminated surface on C-face 6H-SiC could be obtained only by the latter method. Ti is deposited on Si-face and C-face SiC substrates with H-terminated surfaces and ohmic contact is obtained without high-temperature annealing.展开更多
A high-quality Ga2O3 thin film is deposited on an SiC substrate to form a heterojunction structure. The band alignment of the Ga2O3/6H-SiC heterojunction is studied by using synchrotron radiation photoelectron spectro...A high-quality Ga2O3 thin film is deposited on an SiC substrate to form a heterojunction structure. The band alignment of the Ga2O3/6H-SiC heterojunction is studied by using synchrotron radiation photoelectron spectroscopy, The energy band diagram of the Ga2O3/6H-SiC heterojunction is obtained by analysing the binding energies of Ga 3d and Si 2p at the surface and the interface of the heterojunction. The valence band offset is experimentally determined to be 2.8 eV and the conduction band offset is calculated to be 0.89 eV, which indicate a type-II band alignment. This provides useful guidance for the application of Ga2O3/6H-SiC electronic devices.展开更多
基金Project supported by the Innovation Program of the Chinese Academy of Sciences (Grant No. KJCX2-EW-W10)the Shanghai Municipal Science and Technology Commission, China (Grant Nos. 09DZ1141400 and 09520714900)the Young Scientists Fund of the National Natural Science Foundation of China (Grant No. 51002176)
文摘The effect of surface morphology of 6H-SiC substrate on the ohmic contact properties of Ti/6H-SiC structure is studied. The H-terminated surface on Si-face 6H-SiC is obtained by both dipping SiC into HF acid solution for 15 s and thermal heating SiC in hydrogen atmosphere at 1100 ℃ for 10 min, while the H-terminated surface on C-face 6H-SiC could be obtained only by the latter method. Ti is deposited on Si-face and C-face SiC substrates with H-terminated surfaces and ohmic contact is obtained without high-temperature annealing.
基金supported by the National Natural Science Foundation of China(Grant Nos.50702071 and 50772122)the Young Scientists Fund of the National Natural Science Foundation of China(Grant No.51002176)
文摘A high-quality Ga2O3 thin film is deposited on an SiC substrate to form a heterojunction structure. The band alignment of the Ga2O3/6H-SiC heterojunction is studied by using synchrotron radiation photoelectron spectroscopy, The energy band diagram of the Ga2O3/6H-SiC heterojunction is obtained by analysing the binding energies of Ga 3d and Si 2p at the surface and the interface of the heterojunction. The valence band offset is experimentally determined to be 2.8 eV and the conduction band offset is calculated to be 0.89 eV, which indicate a type-II band alignment. This provides useful guidance for the application of Ga2O3/6H-SiC electronic devices.