The insertion layer of TiO2 between polymer-fullerene blend and LiF/AI electrode is used to enhance the shortcircuit current Isc and fill factor （FF）. The solar cell based on the blend of poly[2-methoxy-5-（2＇-ethy...The insertion layer of TiO2 between polymer-fullerene blend and LiF/AI electrode is used to enhance the shortcircuit current Isc and fill factor （FF）. The solar cell based on the blend of poly[2-methoxy-5-（2＇-ethylhexyloxy）- 1,4-phenylenevinylene] （MEH-PPV） and C60 with the modifying layer of TiO2 （about 20nm） shows the open- circuit Voc of about 0.62 V, short circuit current Isc of about 2.35 mA/cm^2, filling factor FF of about 0.284, and the power conversion efficiency （PCE） of about 2.4% under monochromatic light （50Onto） photoexcitation of about 17mW/cm^2. Compared to ceils without the TiO2 layer, the power conversion efficiency increases by about 17.5%. Similar effect is also obtained in cells with the undoped MEH-PPV structure of ITO/PEDOT：PASS/MEH- PPV/（TiO2）LiF/AI. The improved solar cell performance can be attributed to enhanced carrier extraction efficiency at the active layer/electrode interfaces when TiO2 is inserted.展开更多
基金Supported by the Trans-Century Training Programme for the Talents of Natural Science by the State Education Commission, Key Project of the Ministry of Education of China under Grant No 105041, the National Natural Science Foundation of China under Grant Nos 90401006, 10434030 and 90301004, and the National Basic Research Program of China under Grant No 2003CB314707.
文摘The insertion layer of TiO2 between polymer-fullerene blend and LiF/AI electrode is used to enhance the shortcircuit current Isc and fill factor （FF）. The solar cell based on the blend of poly[2-methoxy-5-（2＇-ethylhexyloxy）- 1,4-phenylenevinylene] （MEH-PPV） and C60 with the modifying layer of TiO2 （about 20nm） shows the open- circuit Voc of about 0.62 V, short circuit current Isc of about 2.35 mA/cm^2, filling factor FF of about 0.284, and the power conversion efficiency （PCE） of about 2.4% under monochromatic light （50Onto） photoexcitation of about 17mW/cm^2. Compared to ceils without the TiO2 layer, the power conversion efficiency increases by about 17.5%. Similar effect is also obtained in cells with the undoped MEH-PPV structure of ITO/PEDOT：PASS/MEH- PPV/（TiO2）LiF/AI. The improved solar cell performance can be attributed to enhanced carrier extraction efficiency at the active layer/electrode interfaces when TiO2 is inserted.