Plasma electrolytic oxidation(PEO) coatings were fabricated on 6063 aluminum alloy in a cheap and convenient electrolyte. The effect of different current densities, i e, 5, 10, 15, and 20 A/dm2on the microstructure an...Plasma electrolytic oxidation(PEO) coatings were fabricated on 6063 aluminum alloy in a cheap and convenient electrolyte. The effect of different current densities, i e, 5, 10, 15, and 20 A/dm2on the microstructure and corrosion behavior of coatings was comprehensively studied by scanning electron microscopy(SEM), stereoscopic microscopy, potentiodynamic polarization and electrochemical impedance spectroscopy(EIS), respectively. It is found that the pore density decreases and the pore size increases with increasing current density. The XRD results show that the coatings are only composed of α-Al2O3and γ-Al2O3. Potentiodynamic polarization test proves that the coating formed under 10 A/dm2possesses the best anticorrosion property. The long time EIS test shows that the coating under 10 A/dm2is able to protect the aluminum alloy substrate after long time of immersion in 0.59 M NaCl solution, which confirms the salt solution immersion test results in 2 M NaCl solution.展开更多
Plasma electrolytic oxidation（PEO） coatings were prepared on AZ31 magnesium alloy using alkaline phosphate as base electrolyte system, and with the addition of sodium silicate（Na2SiO3）, sodium aluminate（NaAlO2） ...Plasma electrolytic oxidation（PEO） coatings were prepared on AZ31 magnesium alloy using alkaline phosphate as base electrolyte system, and with the addition of sodium silicate（Na2SiO3）, sodium aluminate（NaAlO2） and potassium fluorozirconate（K2ZrF6） as additives. The microstructure, phase composition and element composition as well as surface profile of the PEO coatings were analyzed by means of scanning electron microscopy（SEM）, X-ray diffraction（XRD）, energy dispersive X-ray spectroscopy（EDS）, and threedimensional（3 D） optical profilometry. The corrosion and wear properties were evaluated by electrochemical potentiodynamic polarization in 3.5 wt% Na Cl solution and ball-on-disc wear tests, respectively. The results showed that the anions of the additives effectively participated in the coating formation influencing its microstructural features, chemical composition, corrosion resistance and tribological behaviour. It was observed that the sample treated by PEO in the electrolyte solution containing K2ZrF6 as an additive showed better corrosion and abrasive resistance.展开更多
基金Funded by the National Natural Science Foundation of China(Nos.51371039 and 51871031)
文摘Plasma electrolytic oxidation(PEO) coatings were fabricated on 6063 aluminum alloy in a cheap and convenient electrolyte. The effect of different current densities, i e, 5, 10, 15, and 20 A/dm2on the microstructure and corrosion behavior of coatings was comprehensively studied by scanning electron microscopy(SEM), stereoscopic microscopy, potentiodynamic polarization and electrochemical impedance spectroscopy(EIS), respectively. It is found that the pore density decreases and the pore size increases with increasing current density. The XRD results show that the coatings are only composed of α-Al2O3and γ-Al2O3. Potentiodynamic polarization test proves that the coating formed under 10 A/dm2possesses the best anticorrosion property. The long time EIS test shows that the coating under 10 A/dm2is able to protect the aluminum alloy substrate after long time of immersion in 0.59 M NaCl solution, which confirms the salt solution immersion test results in 2 M NaCl solution.
基金Funded by National Natural Science Foundation of China(No.51371039)Zhejiang Provincial Natural Science Foundation of China(No.LGG18E020004)+1 种基金Open Foundation of Zhejiang Provincial Top Key Discipline of Mechanical EngineeringScience and Technology Project of Zhejiang Province(No.2015C37037)
文摘Plasma electrolytic oxidation（PEO） coatings were prepared on AZ31 magnesium alloy using alkaline phosphate as base electrolyte system, and with the addition of sodium silicate（Na2SiO3）, sodium aluminate（NaAlO2） and potassium fluorozirconate（K2ZrF6） as additives. The microstructure, phase composition and element composition as well as surface profile of the PEO coatings were analyzed by means of scanning electron microscopy（SEM）, X-ray diffraction（XRD）, energy dispersive X-ray spectroscopy（EDS）, and threedimensional（3 D） optical profilometry. The corrosion and wear properties were evaluated by electrochemical potentiodynamic polarization in 3.5 wt% Na Cl solution and ball-on-disc wear tests, respectively. The results showed that the anions of the additives effectively participated in the coating formation influencing its microstructural features, chemical composition, corrosion resistance and tribological behaviour. It was observed that the sample treated by PEO in the electrolyte solution containing K2ZrF6 as an additive showed better corrosion and abrasive resistance.