Ba-Al-S-Eu sputtering target for blue emitting phosphors was prepared by powder sintering method. XRD patterns showed that the main components of the target were barium tetra aluminum sulfide （BaAl4S7）, bariutm sulf...Ba-Al-S-Eu sputtering target for blue emitting phosphors was prepared by powder sintering method. XRD patterns showed that the main components of the target were barium tetra aluminum sulfide （BaAl4S7）, bariutm sulfide （BaS）, and europium sulfide （EuS）. In the samples, part of the barium and aluminum are formed into barium aluminum oxide （BaAl2O4） with the impurity element of oxygen. The PL characteristic spectra of the target showed the 470 nm blue emission obviously, and the Ba-Al-S thin films also transmitted a purple-blue emission at the position of 440 nm.The results indicated that this method was suitable for the fabrication of the Ba-Al-S：Eu sputtering target.展开更多
Europium-doped barium thioaluminate sputtering target was synthesized by powder sintering method and thin film was deposited by radio frequency(RF) sputtering.X-ray diffractometer(XRD) pattern indicated that the main ...Europium-doped barium thioaluminate sputtering target was synthesized by powder sintering method and thin film was deposited by radio frequency(RF) sputtering.X-ray diffractometer(XRD) pattern indicated that the main compound of the target was BaAl4S7.Oxygen was the main impurity which led to the formation of BaAl2O4.It was shown that both BaAl4S7 and BaAl2S4 were contained in the as-grown thin films and a 471.7 nm emission peak in the PL spectra appeared due to a combination of BaAl4S7:Eu2+ and BaAl2S4:Eu2...展开更多
基金supported by Provincial Natural Science Foundation of Beijing (3063022)
文摘Ba-Al-S-Eu sputtering target for blue emitting phosphors was prepared by powder sintering method. XRD patterns showed that the main components of the target were barium tetra aluminum sulfide （BaAl4S7）, bariutm sulfide （BaS）, and europium sulfide （EuS）. In the samples, part of the barium and aluminum are formed into barium aluminum oxide （BaAl2O4） with the impurity element of oxygen. The PL characteristic spectra of the target showed the 470 nm blue emission obviously, and the Ba-Al-S thin films also transmitted a purple-blue emission at the position of 440 nm.The results indicated that this method was suitable for the fabrication of the Ba-Al-S：Eu sputtering target.
基金supported by the National Eleventh Five-year Pre-research Project of China (51302060203)
文摘Europium-doped barium thioaluminate sputtering target was synthesized by powder sintering method and thin film was deposited by radio frequency(RF) sputtering.X-ray diffractometer(XRD) pattern indicated that the main compound of the target was BaAl4S7.Oxygen was the main impurity which led to the formation of BaAl2O4.It was shown that both BaAl4S7 and BaAl2S4 were contained in the as-grown thin films and a 471.7 nm emission peak in the PL spectra appeared due to a combination of BaAl4S7:Eu2+ and BaAl2S4:Eu2...