Two-dimensional(2D)mesoporous metal-oxide(hydroxide)nanomaterials with defects are promising towards the realization of efficient electrocatalysis.Herein,we report a facile and effective one-pot solvothermal route to ...Two-dimensional(2D)mesoporous metal-oxide(hydroxide)nanomaterials with defects are promising towards the realization of efficient electrocatalysis.Herein,we report a facile and effective one-pot solvothermal route to synthesize mesoporous Mo_(x)-Co-O hybrid nanosheets(NSs)which is composed of crystalline Mo_(4)O_(11) and amorphous cobalt hydroxide.Due to the corrosion of 1-octylamine at high temperatures,abundant mesoporous holes are created in situ over the Mo_(x)-Co-O hybrid NSs during the solvothermal process,which is beneficial to increasing the electrochemical surface area.The dimension of the Mox-Co-O NSs,size of mesoporous and the concentration of defects can be easily modulated by controlling the molar ratio of Mo/Co.Electrochemical measurements reveal that the 2D mesoporous Mo_(x)-Co-O NSs show an excellent activity for the oxygen evolution reaction with the highest catalytic activity of η_(10)=276 mV at 10 mA cm^(−2)in 1 mol L^(−1)KOH.Enhanced adsorption of intermediates and abundant oxygen vacancies achieved by appropriate Mo doping are the two main factors that contribute to the excellent catalytic activity of Mo_(0.2)-Co-O NSs.This work,with the construction of 2D metal-oxide(hydroxide)crystallineamorphous nanomaterials possessing abundant holes,oxygen vacancies and enhanced adsorption of intermediates,provides important insight on the design of more efficient catalysts.展开更多
基金the National Key R&D Program of China(2020YFB1505802)the Ministry of Science and Technology(2017YFA0208200)+1 种基金the National Natural Science Foundation of China(22025108,U21A20327,and 22121001)the Start-up Funds from Xiamen University.
文摘Two-dimensional(2D)mesoporous metal-oxide(hydroxide)nanomaterials with defects are promising towards the realization of efficient electrocatalysis.Herein,we report a facile and effective one-pot solvothermal route to synthesize mesoporous Mo_(x)-Co-O hybrid nanosheets(NSs)which is composed of crystalline Mo_(4)O_(11) and amorphous cobalt hydroxide.Due to the corrosion of 1-octylamine at high temperatures,abundant mesoporous holes are created in situ over the Mo_(x)-Co-O hybrid NSs during the solvothermal process,which is beneficial to increasing the electrochemical surface area.The dimension of the Mox-Co-O NSs,size of mesoporous and the concentration of defects can be easily modulated by controlling the molar ratio of Mo/Co.Electrochemical measurements reveal that the 2D mesoporous Mo_(x)-Co-O NSs show an excellent activity for the oxygen evolution reaction with the highest catalytic activity of η_(10)=276 mV at 10 mA cm^(−2)in 1 mol L^(−1)KOH.Enhanced adsorption of intermediates and abundant oxygen vacancies achieved by appropriate Mo doping are the two main factors that contribute to the excellent catalytic activity of Mo_(0.2)-Co-O NSs.This work,with the construction of 2D metal-oxide(hydroxide)crystallineamorphous nanomaterials possessing abundant holes,oxygen vacancies and enhanced adsorption of intermediates,provides important insight on the design of more efficient catalysts.