The magnetic properties and magnetization reversible processes of Llo FePt （3 nm）/Pb（Mg1/3Nb2/3）O3-PbTiO3 （PMN-PT） heterostructure were investigated by using the phase field model. The simulation results show th...The magnetic properties and magnetization reversible processes of Llo FePt （3 nm）/Pb（Mg1/3Nb2/3）O3-PbTiO3 （PMN-PT） heterostructure were investigated by using the phase field model. The simulation results show that the magnetic coercivities and magnetic domains evolution in the Llo FePt thin film are significantly influenced by the compressive strains stemming from the polarization of single crystal PMN-PT substrate under an applied electric field. It is found that the magnetic coercivities increase with increasing of the compressive strain. A large compressive strain is beneficial to aligning the magnetic moments along the out-of-plane direction and to the enhancement of perpendicular magnetic anisotropy. The variations of magnetic energy densities show that when compressive strains are different at the magnetization reversible processes, the magnetic anisotropy energies and the magnetic exchange energies firstly increase and then decrease, the negative demagnetization energy peaks appear at coercivities fields, and the magnetoelastic energies are invariable at large external magnetic field with the energy maximum appearing at coercivities fields. The variations of the magnetoelastic energies bring about the perpendicular magnetic anisotropy so that the magnetoelastic energy is lower at the large external magnetic fields, whereas the appearance of magnetoelastic energy peaks is due to the magnetization-altered direction from the normal direction of the plane of the Llo FePt thin film at coercivities fields.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.11474167,51701091,and 11504020)the Start-up Funds of NUIST,China(Grant Nos.2243141601035 and 2243141601018)
文摘The magnetic properties and magnetization reversible processes of Llo FePt （3 nm）/Pb（Mg1/3Nb2/3）O3-PbTiO3 （PMN-PT） heterostructure were investigated by using the phase field model. The simulation results show that the magnetic coercivities and magnetic domains evolution in the Llo FePt thin film are significantly influenced by the compressive strains stemming from the polarization of single crystal PMN-PT substrate under an applied electric field. It is found that the magnetic coercivities increase with increasing of the compressive strain. A large compressive strain is beneficial to aligning the magnetic moments along the out-of-plane direction and to the enhancement of perpendicular magnetic anisotropy. The variations of magnetic energy densities show that when compressive strains are different at the magnetization reversible processes, the magnetic anisotropy energies and the magnetic exchange energies firstly increase and then decrease, the negative demagnetization energy peaks appear at coercivities fields, and the magnetoelastic energies are invariable at large external magnetic field with the energy maximum appearing at coercivities fields. The variations of the magnetoelastic energies bring about the perpendicular magnetic anisotropy so that the magnetoelastic energy is lower at the large external magnetic fields, whereas the appearance of magnetoelastic energy peaks is due to the magnetization-altered direction from the normal direction of the plane of the Llo FePt thin film at coercivities fields.
