苯乙烯基四配位硅改性苯丙乳液的研制

将高反应活性的五配位硅钾化合物与对苄氯苯乙烯反应，制得苯乙烯基四配位硅（简称四配位硅）单体；然后，将其与苯乙烯、丙烯酸丁酯、甲基丙烯酸共聚，制成硅改性苯丙乳液。研究了乳化剂用量、乳液的理论回含量、四配住硅单位用量对苯丙乳液性能的影响。结果表明：当乳化剂质量分数为2％，乳液固含量为40％、四配位硅单体质量分数为2％～5％时，乳液的各项性能指标较好，成膜后的膜硬度和附着力均比苯丙乳胶膜好一个等级，玻璃化温度降低了8．7℃，热失重温度提高了25℃。

含四配位硅的烯类单体改性苯丙乳液的研究

The styrene-acrylic（St-BA-MAA/SDS-DNS86/H2O）emulsion modified by the ethyl-tetra-coordinated silicon was prepared,using water as the solvent,the laurel sodium sulfate and alkyl ethyl sulfuric acid sodium（SDS-DNS86） as the emulsifiers potassium per-sulfate（KPS） for the initiator and adding the initiator minute steps for free radical polymerization.The thermal properties analyzed by TG and the glass transition temperature determined by DSC were researched to the styrene-acrylic emulsion and emulsions modified by ethyl-tetra-coordinated silicon.The results indicated that the thermal properties of the modified membrane increas and the glass transition temperature of the modified membrane decreases and adhesion force of the modified membrane enhances.

双羟基四配位硅改性苯丙乳液的合成及性能研究

通过乳液聚合方法,制备了双羟基四配位硅改性苯丙乳液;测定了乳液的粘度、粒径分布、凝胶率、稳定性等;测定了乳液成膜后的各种性能,如吸水率、热性能分析、玻璃化转变温度、附着力、硬度等.结果表明改性的苯丙乳液比纯苯丙乳液的热性能有所提高,玻璃化转变温度有所降低,附着力提高.并得出2%含量的双羟基四配位硅改性2%乳化剂、40%固含量的苯丙乳液性能最佳.

重视实验教学构建有效课堂

课堂的有效性是每个教师共同追求的目标，而化学学科有着得天独厚的优势，就是辅助教学的手段——化学实验。化学实验对构建有效课堂起着举足轻重的作用。一、在实验教学中，培养学生控制实验条件变量的意识如二氧化碳的化学性质教学片段——笔者在做完这个实验后，对学生提了以下几个问题：