Fiber-shaped energy storage devices are indispensable parts of wearable and portable electronics.Aqueous rechargeable Ni/Fe battery is a very appropriate energy storage device due to their good safety without organic ...Fiber-shaped energy storage devices are indispensable parts of wearable and portable electronics.Aqueous rechargeable Ni/Fe battery is a very appropriate energy storage device due to their good safety without organic electrolytes, high ionic conductivity, and low cost. Unfortunately, the low energy density,poor power density and cycling performance hinder its further practical applications. In this study, in order to obtain high performance negative iron-based material, we first synthesized a-iron oxide(α-Fe2O3) nanorods(NRs) with superstructures on the surface of highly conductive carbon nanotube fibers(CNTFs), then electrically conductive polypyrrole(PPy) was coated to enhance the electron, ion diffusion and cycle stability. The as-prepared α-Fe2O3@PPy NRs/CNTF electrode shows a high specific capacity of 0.62 Ah cm-3 at the current density of 1 A cm-3. Furthermore, the Ni/Fe battery that was assembled by the above negative electrode shows a maximum volumetric energy density of 15.47 mWh cm-3 with228.2 mW cm-3 at a current density of 1 A cm-3. The cycling durability and mechanical flexibility of the Ni/Fe battery were tested, which show good prospect for practical application. In summary, these merits make it possible for our Ni/Fe battery to have practical applications in next generation flexible energy storage devices.展开更多
基金This work was supported by the National Natural Science Foundation of China (51972162 and 51703241)the Postdoctoral Foundation of Jiangsu Province (2019Z203 and 2019K001)the Science and Technology Project of Nanchang (2017-SJSYS008)
文摘Fiber-shaped energy storage devices are indispensable parts of wearable and portable electronics.Aqueous rechargeable Ni/Fe battery is a very appropriate energy storage device due to their good safety without organic electrolytes, high ionic conductivity, and low cost. Unfortunately, the low energy density,poor power density and cycling performance hinder its further practical applications. In this study, in order to obtain high performance negative iron-based material, we first synthesized a-iron oxide(α-Fe2O3) nanorods(NRs) with superstructures on the surface of highly conductive carbon nanotube fibers(CNTFs), then electrically conductive polypyrrole(PPy) was coated to enhance the electron, ion diffusion and cycle stability. The as-prepared α-Fe2O3@PPy NRs/CNTF electrode shows a high specific capacity of 0.62 Ah cm-3 at the current density of 1 A cm-3. Furthermore, the Ni/Fe battery that was assembled by the above negative electrode shows a maximum volumetric energy density of 15.47 mWh cm-3 with228.2 mW cm-3 at a current density of 1 A cm-3. The cycling durability and mechanical flexibility of the Ni/Fe battery were tested, which show good prospect for practical application. In summary, these merits make it possible for our Ni/Fe battery to have practical applications in next generation flexible energy storage devices.