In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and h...In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and hydrogen evolution experiment were performed to study the corrosion resistance of AZ80,AZ80 with CPCC and coated AZ80 with scratch.The results show that the coating improves the corrosion resistance of the AZ80 from a current density of(85±4)to(4±1)μA/cm^(2).When the coating was damaged,its protection on substrate would be reduced.The scratch with a length of around 12 mm on the coating reduced the corrosion resistance to a current density of(39±1)μA/cm^(2).In addition,the corrosion occurred initially in the scratch area and the corrosion site first occurred at the junction of the scratch and the coating.Besides,the micro corrosion mechanism of the specimen containing scratch was clarified.展开更多
The influence of heat treatment on the corrosion behavior of rolled Mg5 Gd alloys in 3.5 wt.% Na Cl solution saturated with Mg(OH)2 was characterized by immersion test, electrochemical test, scanning electrochemical m...The influence of heat treatment on the corrosion behavior of rolled Mg5 Gd alloys in 3.5 wt.% Na Cl solution saturated with Mg(OH)2 was characterized by immersion test, electrochemical test, scanning electrochemical microscopy(SECM) and corrosion morphology analysis in order to improve the corrosion resistance of Mg alloys. The results showed that solution treatment reduced the corrosion rate of the Mg5 Gd significantly, resulting in relatively uniform corrosion and shallow corrosion cavities due to the dissolution of Cd-containing particles. The following aging process could further decrease the corrosion rate. Precipitation of nano-sized Cd-containing particles did not cause apparent micro-galvanic corrosion, which could be attributed to the formation of a protective corrosion product film fully covering the particles.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.52071036,51701027)the Fundamental Research Funds for the Central Universities,China(Nos.2020CDJQY-A002,2021CDJCGJ009)the National Key Research and Development Program of China(Nos.2016YFB0301100,2016YFB0101700)。
文摘In order to analyze the effect of scratch on the corrosion behaviour of a calcium phosphate conversion coating(CPCC)on AZ80,the electrochemical testing,scanning vibrating electrode technique(SVET),immersion test and hydrogen evolution experiment were performed to study the corrosion resistance of AZ80,AZ80 with CPCC and coated AZ80 with scratch.The results show that the coating improves the corrosion resistance of the AZ80 from a current density of(85±4)to(4±1)μA/cm^(2).When the coating was damaged,its protection on substrate would be reduced.The scratch with a length of around 12 mm on the coating reduced the corrosion resistance to a current density of(39±1)μA/cm^(2).In addition,the corrosion occurred initially in the scratch area and the corrosion site first occurred at the junction of the scratch and the coating.Besides,the micro corrosion mechanism of the specimen containing scratch was clarified.
基金financial supports from the National Natural Science Foundation of China (51801168,51731008)Natural Science Foundation of Fujian Province (2018J05093),ChinaNational Environmental Corrosion Platform of China。
文摘The influence of heat treatment on the corrosion behavior of rolled Mg5 Gd alloys in 3.5 wt.% Na Cl solution saturated with Mg(OH)2 was characterized by immersion test, electrochemical test, scanning electrochemical microscopy(SECM) and corrosion morphology analysis in order to improve the corrosion resistance of Mg alloys. The results showed that solution treatment reduced the corrosion rate of the Mg5 Gd significantly, resulting in relatively uniform corrosion and shallow corrosion cavities due to the dissolution of Cd-containing particles. The following aging process could further decrease the corrosion rate. Precipitation of nano-sized Cd-containing particles did not cause apparent micro-galvanic corrosion, which could be attributed to the formation of a protective corrosion product film fully covering the particles.