The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire...The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire retardant paint from excessive heat during welding,it is necessary to get accurately reserved area near the welding joints prior to welding. For the foregoing reasons,the 80 ℃ temperature field distribution of thick plate multi-pass welding was analyzed with SYSWELD.The influence of welding groove form and time interval on welding temperature field was also analyzed. Results showed that the range of 80 ℃ welding temperature field increased with the increasing of weld layers at first and then it inclined to stable value. Interpass time setting was crucial to control the range of 80 ℃ welding temperature field. It was also found that double V groove had better thermal diffusivity than double-bevel groove.And double-bevel groove was better than single V groove.展开更多
基金Project(No.2016ZDJS05B03)supported by Shandong Key ResearchDevelopment Plan,Project(No.17CX06005&No.18CX06054A)supported by Department of Science&Technology of Shandong Province the Fundamental Research Funds for the Central Universities
文摘The PPG PITT-CHAR XP flame retardant system has been used by COOEC to preventing the thermal softening of steel in the high temperature,whose degradation temperature is 80 ℃.To prevent damage to PPG PITT-CHAR XP fire retardant paint from excessive heat during welding,it is necessary to get accurately reserved area near the welding joints prior to welding. For the foregoing reasons,the 80 ℃ temperature field distribution of thick plate multi-pass welding was analyzed with SYSWELD.The influence of welding groove form and time interval on welding temperature field was also analyzed. Results showed that the range of 80 ℃ welding temperature field increased with the increasing of weld layers at first and then it inclined to stable value. Interpass time setting was crucial to control the range of 80 ℃ welding temperature field. It was also found that double V groove had better thermal diffusivity than double-bevel groove.And double-bevel groove was better than single V groove.