We report helium ion irradiation experiments for a new type of dispersion-strengthened NiMo-Y_(2)O_(3)alloy with three different irradiation doses and varying irradiation dose rates at 750℃to evaluate its helium-indu...We report helium ion irradiation experiments for a new type of dispersion-strengthened NiMo-Y_(2)O_(3)alloy with three different irradiation doses and varying irradiation dose rates at 750℃to evaluate its helium-induced damage behavior.Transmission electron microscopy was used to reveal the evolution of helium bubbles after irradiation.The experimental results show that with increasing ion dose,the number density of helium bubbles increases continuously.However,the mean size of helium bubbles first increases and then decreases,mainly due to the varied ion dose rates.The volume fractions of helium bubbles in the three investigated samples after irradiation are 0.15%,0.32%,and 0.27%,which are lower than that of the Hastelloy N alloy(0.58%)after similar irradiation conditions.This indicates that the NiMo-Y_(2)O_(3)alloy exhibits better helium-induced-swelling resistance than the Hastelloy N alloy,highlighting its potential applicability to MSRs,from the perspective of irradiation performance.展开更多
利用纳米压痕仪的连续刚度测量模式测试了常温氙离子辐照后Hastelloy N合金的纳米硬度。结果表明,辐照样品的纳米硬度均大于未辐照样品的纳米硬度,且辐照剂量在0.5~3.0 dpa这一范围内时,辐照样品的纳米硬度处于饱和状态。在Nix-Gao模型...利用纳米压痕仪的连续刚度测量模式测试了常温氙离子辐照后Hastelloy N合金的纳米硬度。结果表明,辐照样品的纳米硬度均大于未辐照样品的纳米硬度,且辐照剂量在0.5~3.0 dpa这一范围内时,辐照样品的纳米硬度处于饱和状态。在Nix-Gao模型的基础上,分离出未辐照样品和辐照样品的压痕尺寸效应,并通过VLM(volume law of mixture)模型来模拟实验测得的纳米硬度。由于随着压头压入深度的增加,塑性影响区中将同时包含辐照损伤层与基体,在VLM模型中引入“界面参数”(χ)以修正基体的形变量,改进后的模型能够更好地模拟纳米压痕的实验结果。展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.12022515,11975304,and 91126012)the Youth Innovation Promotion Association,CAS(Grant No.202063)。
文摘We report helium ion irradiation experiments for a new type of dispersion-strengthened NiMo-Y_(2)O_(3)alloy with three different irradiation doses and varying irradiation dose rates at 750℃to evaluate its helium-induced damage behavior.Transmission electron microscopy was used to reveal the evolution of helium bubbles after irradiation.The experimental results show that with increasing ion dose,the number density of helium bubbles increases continuously.However,the mean size of helium bubbles first increases and then decreases,mainly due to the varied ion dose rates.The volume fractions of helium bubbles in the three investigated samples after irradiation are 0.15%,0.32%,and 0.27%,which are lower than that of the Hastelloy N alloy(0.58%)after similar irradiation conditions.This indicates that the NiMo-Y_(2)O_(3)alloy exhibits better helium-induced-swelling resistance than the Hastelloy N alloy,highlighting its potential applicability to MSRs,from the perspective of irradiation performance.
文摘利用纳米压痕仪的连续刚度测量模式测试了常温氙离子辐照后Hastelloy N合金的纳米硬度。结果表明,辐照样品的纳米硬度均大于未辐照样品的纳米硬度,且辐照剂量在0.5~3.0 dpa这一范围内时,辐照样品的纳米硬度处于饱和状态。在Nix-Gao模型的基础上,分离出未辐照样品和辐照样品的压痕尺寸效应,并通过VLM(volume law of mixture)模型来模拟实验测得的纳米硬度。由于随着压头压入深度的增加,塑性影响区中将同时包含辐照损伤层与基体,在VLM模型中引入“界面参数”(χ)以修正基体的形变量,改进后的模型能够更好地模拟纳米压痕的实验结果。