Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system. In this work, HfO_2/SiO_2 multilayer films are prepared by e-beam evaporation and then β-r...Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system. In this work, HfO_2/SiO_2 multilayer films are prepared by e-beam evaporation and then β-ray irradiation is employed as the post-processing method. The particle irradiation affects the laser induced damage threshold(LIDT),which includes defects, surface roughness, packing density and residual stress. The residual stress that is relaxed during irradiation changes from compressive stress into tensile stress. Our results indicate that appropriate tensile stress can improve LIDT remarkably. In view of the fact that LIDT rises from 8 J/cm^2 to 12 J/cm^2, i.e., 50% increase, after the film has been irradiated by 2.2×10^(13)/cm^2 β-ray, the particle irradiation can be used as a controllable and desirable postprocessing method to improve the resistance to laser induced damage.展开更多
Ta5+doped β-Ga2O3 single crystals were grown by using the optical floating zone method, and then annealed in the air and nitrogen gas at 1400℃ for 20 hours.The transmittance spectra, photoluminescence(PL), x-ray irr...Ta5+doped β-Ga2O3 single crystals were grown by using the optical floating zone method, and then annealed in the air and nitrogen gas at 1400℃ for 20 hours.The transmittance spectra, photoluminescence(PL), x-ray irradiation spectra, and PL decay profiles of the samples were measured at room temperature.The relevant results show that the optical transmittance of the samples annealed in the air or nitrogen gas was improved.By drawing the(ahv)2–hv graph,it can be seen that the band gap decreased after being annealed in the air, but increased in nitrogen gas.The PL spectra and x-ray irradiation spectra show that the luminescent intensity of the sample annealed in the air increased substantially,while decreased for the sample annealed in nitrogen.The PL decay time of the Ta:β-Ga2O3 annealed in the air increased significantly compared with that of the Ta:β-Ga2O3 sample without annealing, but the tendency after annealing in nitrogen gas was opposite.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant No.11405085)the Jiangsu Provincial Natural Science Fund,China(Grant No.BK20130789)
文摘Post-processing can effectively improve the resistance to laser damage in multilayer films used in a high power laser system. In this work, HfO_2/SiO_2 multilayer films are prepared by e-beam evaporation and then β-ray irradiation is employed as the post-processing method. The particle irradiation affects the laser induced damage threshold(LIDT),which includes defects, surface roughness, packing density and residual stress. The residual stress that is relaxed during irradiation changes from compressive stress into tensile stress. Our results indicate that appropriate tensile stress can improve LIDT remarkably. In view of the fact that LIDT rises from 8 J/cm^2 to 12 J/cm^2, i.e., 50% increase, after the film has been irradiated by 2.2×10^(13)/cm^2 β-ray, the particle irradiation can be used as a controllable and desirable postprocessing method to improve the resistance to laser induced damage.
基金Project supported by the National Natural Science Foundation of China(Grant No.51802327)the Science and Technology Commission of Shanghai Municipality,China(Grant No.18511110500)
文摘Ta5+doped β-Ga2O3 single crystals were grown by using the optical floating zone method, and then annealed in the air and nitrogen gas at 1400℃ for 20 hours.The transmittance spectra, photoluminescence(PL), x-ray irradiation spectra, and PL decay profiles of the samples were measured at room temperature.The relevant results show that the optical transmittance of the samples annealed in the air or nitrogen gas was improved.By drawing the(ahv)2–hv graph,it can be seen that the band gap decreased after being annealed in the air, but increased in nitrogen gas.The PL spectra and x-ray irradiation spectra show that the luminescent intensity of the sample annealed in the air increased substantially,while decreased for the sample annealed in nitrogen.The PL decay time of the Ta:β-Ga2O3 annealed in the air increased significantly compared with that of the Ta:β-Ga2O3 sample without annealing, but the tendency after annealing in nitrogen gas was opposite.