Amorphous indium-gallium-zinc oxide(a-IGZO)thin films are prepared by pulsed laser deposition and fabricated into thin-film transistor(TFT)devices.In-situ x-ray photoelectron spectroscopy(XPS)illustrates that weakly b...Amorphous indium-gallium-zinc oxide(a-IGZO)thin films are prepared by pulsed laser deposition and fabricated into thin-film transistor(TFT)devices.In-situ x-ray photoelectron spectroscopy(XPS)illustrates that weakly bonded oxygen(O)atoms exist in a-IGZO thin films deposited at high O_(2) pressures,but these can be eliminated by vacuum annealing.The threshold voltage(V_(th))of the a-IGZO TFTs is shifted under positive gate bias,and the Vth shift is positively related to the deposition pressure.A temperature variation experiment in the range of 20 K-300 K demonstrates that an activation energy of 144 meV is required for the Vth shift,which is close to the activation energy required for the migration of weakly bonded O atoms in a-IGZO thin films.Accordingly,the Vth shift is attributed to the acceptor-like states induced by the accumulation of weakly bonded O atoms at the a-IGZO/SiO_(2) interface under positive gate bias.These results provide an insight into the mechanism responsible for the Vth shift of the a-IGZO TFTs and help in the production of reliable designs.展开更多
基金Project supported by the National Natural Science Foundation of China(Grant Nos.51771144 and 62104189)the Natural Science Foundation of Shaanxi Province,China(Grant Nos.2021JC-06,2019TD-020,and 2019JLM-30)+1 种基金the China Postdoctoral Science Foundation(Grant No.2020M683483)the Fundamental scientific research business expenses of Xi'an Jiaotong University(Grant No.XZY022020017).
文摘Amorphous indium-gallium-zinc oxide(a-IGZO)thin films are prepared by pulsed laser deposition and fabricated into thin-film transistor(TFT)devices.In-situ x-ray photoelectron spectroscopy(XPS)illustrates that weakly bonded oxygen(O)atoms exist in a-IGZO thin films deposited at high O_(2) pressures,but these can be eliminated by vacuum annealing.The threshold voltage(V_(th))of the a-IGZO TFTs is shifted under positive gate bias,and the Vth shift is positively related to the deposition pressure.A temperature variation experiment in the range of 20 K-300 K demonstrates that an activation energy of 144 meV is required for the Vth shift,which is close to the activation energy required for the migration of weakly bonded O atoms in a-IGZO thin films.Accordingly,the Vth shift is attributed to the acceptor-like states induced by the accumulation of weakly bonded O atoms at the a-IGZO/SiO_(2) interface under positive gate bias.These results provide an insight into the mechanism responsible for the Vth shift of the a-IGZO TFTs and help in the production of reliable designs.